Water antistatic synthetic leather and preparation method thereof

An anti-static and synthetic leather technology, applied in the field of synthetic leather manufacturing, can solve the problems of static electricity, safety and hidden dangers, etc., and achieve the effects of improving processing rheology, improving stretching and good mechanical properties

Inactive Publication Date: 2015-04-29
JIANGSU GUOXIN SYNTHETIC LEATHER
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its products are also prone to static electricity due to friction during use, which brings various safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Ingredients: 100 parts of water-based polyurethane resin with a modulus greater than 1000, 1 part of antistatic agent SN, 2 parts of PEG400, 1 part of EFKA2560 defoamer, 1 part of EFKA3772 leveling agent, 0.5 part of MOLYKOTE 557 silicone dry slip agent, PE- 0.5 parts of g-MAH compatibilizer.

[0020] The physical and chemical properties of this synthetic leather are as follows: surface resistance 3.5*10 6 Ω,, tensile load in warp direction is 205 N, tensile load in weft direction is 152 N, elongation at break in warp direction is 7%, elongation at break in weft direction is 13%, tear load in warp direction is 12N, tear load in weft direction is 11N , The peeling load is 20N, and the aging test does not crack.

Embodiment 2

[0022] Ingredients: 100 parts of water-based polyurethane resin with a modulus greater than 1000, 1 part of antistatic agent SN, 3 parts of Span 20, 1 part of EFKA2560 defoamer, 1 part of EFKA3772 leveling agent, 0.5 part of Dow Corning 557, PP-g-MAH 0.5 parts of compatibilizer.

[0023] The physical and chemical properties of this synthetic leather are as follows: surface resistance 3.4*10 6 Ω,, tensile load in warp direction is 203 N, tensile load in weft direction is 151 N, elongation at break in warp direction is 7%, elongation at break in weft direction is 13%, tear load in warp direction is 14N, tear load in weft direction is 12N , Peel load 21N, no cracking in aging test.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
modulusaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses water antistatic synthetic leather and a preparation method thereof. The synthetic leather is prepared from an antistatic sizing agent by adopting a rolling process, wherein the antistatic sizing agent is prepared by following components in parts by weight: 100 parts of water polyurethane resin, 5 to 10 parts of antistatic agent, 0.5 to 1 part of antifoaming agent, 0.5 to 1 part of flatting agent, 0.5 part of organic silicon dry sliding agent and 0.3 to 0.5 part of compatilizer, and the antistatic agent is a complex consisting of a quaternary ammonium cationic surfactant and a nonionic surfactant. The synthetic leather is not only relatively good in mechanical property and capable of improving tensile strength and impact strength of the product, realizing high filling and improving the processing rheological property, but also relatively excellent in antistatic characteristic.

Description

technical field [0001] The invention belongs to the field of synthetic leather manufacture, and in particular relates to a water-based antistatic synthetic leather and a preparation method of the water-based antistatic synthetic leather. Background technique [0002] Artificial leather and synthetic leather are the earliest substitutes invented for leather fabrics. It is made of PVC, plasticizer and other additives and calendered on cloth. At present, in the production process of domestic PVC decorative synthetic leather, plasticizers, PVC resin powder, heavy calcium, stabilizers, foaming agents, and other main raw materials are usually used. This kind of synthetic leather is prone to static electricity during the production process, especially the surface treatment process and organic solvents, causing fires. Its products are also prone to static electricity due to friction during use, which brings various safety hazards. The water-based anti-static synthetic leather prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/14B32B27/06B32B33/00
CPCD06N3/14D06N3/0059D06N3/0077D06N3/0088D06N2209/046D06N2209/103D06N2211/28
Inventor 毛国兵
Owner JIANGSU GUOXIN SYNTHETIC LEATHER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com