Bamboo cane softener and preparation method thereof

A kind of softener and bamboo strip technology, which is applied in the direction of manufacturing tools, wood treatment, wood processing utensils, etc., can solve the problems of affecting the toughness and strength of bamboo, the softening method is too simple, and the bamboo is easy to be baked, so as to achieve better results and facilitate Promote and use, soften the effect of good effect

Inactive Publication Date: 2015-05-06
赵俊辉
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing bamboo sticks are generally softened in the traditional way of roasting. After the bamboo is roasted, it can be bent and woven into various products. This softening method is too simple, and it is easy to break the bamboo, which affects the toughness and strength of the bamboo.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Embodiment 1: bamboo stick softening agent comprises 6 parts of strong glycerol, 6 parts of alcohol ether glycosides, 6 parts of polyoxyethylene ethers, 20 parts of surfactants, 15 parts of stearic acid, 6 parts of urethanes, paraffin 2 parts, 160 parts of deionized water,

[0012] The surfactant mainly includes: octylphenol polyoxyethylene ether, polyoxyethylene sulfosuccinate nonylphenol sodium salt, alkylphenol polyoxyethylene rice phosphate, alkylphenol polyoxyethylene rice phosphate ammonium , each accounting for 25%.

[0013] The preparation method of the surfactant is to take octylphenol polyoxyethylene ether, sulfosuccinic acid polyoxyethylene ether nonylphenol sodium salt, alkylphenol polyoxyethylene rice phosphoric acid ester, alkylphenol polyoxyethylene rice phosphoric acid Ammonium is placed in a stirring tank, the stirring speed is 2500r / mim, the stirring temperature is 80-90°C, and the stirring time is 5 minutes.

[0014] Bamboo softener preparation meth...

Embodiment 2

[0017] Embodiment 2: bamboo stick softening agent comprises 9 parts of strong glycerol, 9 parts of alcohol ether glycosides, 9 parts of polyoxyethylene ethers, 30 parts of surfactants, 20 parts of stearic acid, 9 parts of urethanes, paraffin 3 parts, 170 parts of deionized water,

[0018] The surfactant mainly includes: octylphenol polyoxyethylene ether, polyoxyethylene sulfosuccinate nonylphenol sodium salt, alkylphenol polyoxyethylene rice phosphate, alkylphenol polyoxyethylene rice phosphate ammonium , each accounting for 25%.

[0019] The preparation method of the surfactant is to take octylphenol polyoxyethylene ether, sulfosuccinic acid polyoxyethylene ether nonylphenol sodium salt, alkylphenol polyoxyethylene rice phosphoric acid ester, alkylphenol polyoxyethylene rice phosphoric acid Ammonium is placed in a stirring tank, the stirring speed is 2500r / mim, the stirring temperature is 80-90°C, and the stirring time is 5 minutes.

[0020] Bamboo softener preparation meth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a bamboo cane softener and a preparation method thereof. The preparation method comprises the following steps: placing glycerol, alcohol ether glucoside, polyoxyethylene ether and 100-110 parts of deionized water in a stirring tank A to stir to obtain a liquid A, wherein the stirring speed is 3000r / mim; the stirring temperature is 60-65 DEG C; and the time is 5 minutes; meanwhile, placing stearic acid, ethyl carbamate and surplus deionized water in a stirring tank B and stirring for 5 minutes to obtain a liquid B; adding the liquid A and the liquid B to a stirring tank C according to a proportion of 1:(0.6-0.8), stirring for 2 minutes, adding paraffin, continuously stirring for 3 minutes, finally adding a surfactant, wherein the stirring speed is 2500r / mim; the stirring temperature is 80-90 DEG C; and the time is 10 minutes; and cooling after completing stirring. The bamboo cane softener prepared by the preparation method is good in softening effect, does not have corrosion and is good in effect and is convenient to popularize and use. By utilizing the bamboo cane softener, the strength and the tenacity of a softened part are increased.

Description

Technical field: [0001] The invention relates to the technical field of bamboo softening, in particular to a bamboo strip softener and a preparation process thereof. Background technique: [0002] The existing bamboo sticks are generally softened in the traditional way of roasting. After the bamboo is roasted, it can be bent and woven into various products. This softening method is too simple, and it is easy to break the bamboo, which affects the toughness and strength of the bamboo. . Invention content: [0003] The technical problem to be solved by the present invention is to overcome the defects of the prior art and provide a softener for bamboo sticks and a preparation process thereof. [0004] The technical problem to be solved by the present invention is realized by the following technical solutions. [0005] The softening agent for bamboo strips is characterized in that it includes 6-9 parts of strong glycerol, 6-9 parts of alcohol ether glycosides, 6-9 parts of p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K3/50B27K5/06
CPCB27K3/50B27K5/06
Inventor 赵俊辉
Owner 赵俊辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com