Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Production method for blended fabric of viscose and bamboo fiber

A viscose fiber and blended fabric technology, applied in the textile field, can solve the problems of poor fiber cohesion, poor perspiration effect, poor weaving, etc., achieve uniform heating, supplement process energy loss, and improve yarn quality.

Inactive Publication Date: 2015-05-13
SUZHOU CHENHENG WEAVING
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Viscose fiber, one of the main varieties of man-made fibers; alkali cellulose is formed from natural cellulose, and then reacted with carbon disulfide to form cellulose xanthate, and the viscous solution obtained by dissolving in dilute lye is called viscose Viscose fiber is made into viscose fiber after wet spinning and a series of treatment processes; viscose fiber is also called rayon and ice silk. High-grade new variety; but due to the inherent properties of viscose fiber itself: the fiber is relatively fluffy, the single fiber is relatively brittle, and the weavability is poor. Poor resultant force
[0003] When traditional cotton and polyester raw materials are used in spring and summer clothing fabrics, they have the disadvantage of poor perspiration effect and poor antibacterial effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] In the preparation method of a kind of viscose fiber and bamboo fiber blended fabric provided in this embodiment, the selected warp and weft thread materials are counted in parts by mass: 50 parts of viscose fiber, 9 parts of bamboo fiber, 75 parts of cotton fiber, superfine denier 10 parts of polyester, the preparation process of the fiber fabric is cleaning, carding, drawing, roving, spun yarn and weaving operations, wherein: the weaving process includes warping, boiling and setting, sizing and air-jet operations;

[0026] The specific steps of boiling type setting are as follows: Inject water into the shaping box, the amount of water injected is 68% of the volume of the box; When heating the inside of the box so that the water temperature rises to 88°C, keep it warm for 2 hours; Put the fabric into the box from the top of the box, and submerge it in the water, use the water in the box to quickly shape the fabric, and the setting time is 16 minutes; Remove the f...

Embodiment 2

[0036] In the preparation method of a viscose fiber and bamboo fiber blended fabric provided in this embodiment, the selected warp and latitude thread materials are counted in parts by mass: 60 parts of viscose fiber, 12 parts of bamboo fiber, 80 parts of cotton fiber, superfine denier 12 parts of polyester, the preparation process of the fiber fabric is cleaning, carding, drawing, roving, spun yarn and weaving operations, in which: the weaving process includes warping, boiling and setting, sizing and air-jet operations;

[0037] The specific steps of boiling type setting are as follows: Inject water into the shaping box, the amount of water injected is 70% of the volume of the box; When heating the inside of the tank so that the water temperature rises to 88°C, keep it warm for 2.5 hours; Put the fabric into the box from the top of the box and submerge it in the water. Use the water in the box to quickly shape the fabric, and the setting time is 17 minutes; Remove the f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Winding densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method for blended fabric of viscose and bamboo fiber. Materials of warp yarns and weft yarns selected by the production method for the blended fabric of the viscose and the bamboo fiber comprises, by weight, 40-90 parts of viscose, 8-15 parts of bamboo fiber, 60-95 parts of cotton fiber and 8-18 parts of super fine denier polyester, wherein a cotton cloth weaving procedure comprises the operations of beaming, sizing through boiling, slashing and air blasting; specific procedures of the beaming comprises the steps that the blended fabric is dipped into finishing liquid for 25-40min at normal temperature, the finishing agent content in the finishing liquid is 1.0-3.0%, then microwave treatment is conducted, vacuumization is firstly conducted to reach a vacuum degree ranging from -0.04MPa to 0.03MPa, then microwave steaming and boiling wood-pulp treatment is conducted, the microwave frequency is 120MHz-240MHz, and the microwave processing time is 3-5min. The production method for the blended fabric of the viscose and the bamboo fiber can combine the advantages of the bamboo fiber and the viscose, strengthen the cohesive force between fiber of the blended fabric of the viscose and the bamboo fiber, meanwhile, bacteria growth is restrained, peculiar smells and wet are absorbed, and air permeability can be achieved.

Description

technical field [0001] The invention belongs to the technical field of textiles, in particular to a method for making a viscose fiber and bamboo fiber blended fabric. Background technique [0002] Viscose fiber, one of the main varieties of man-made fibers; alkali cellulose is formed from natural cellulose, and then reacted with carbon disulfide to form cellulose xanthate, and the viscous solution obtained by dissolving in dilute lye is called viscose Viscose fiber is made into viscose fiber after wet spinning and a series of treatment processes; viscose fiber is also called rayon and ice silk. High-grade new variety; but due to the inherent properties of viscose fiber itself: the fiber is relatively fluffy, the single fiber is relatively brittle, and the weavability is poor. Combined force is poor. [0003] When traditional cotton and polyester raw materials are used in spring and summer clothing fabrics, they all have the disadvantages of poor perspiration effect and poo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/00D06B3/10D06M15/693D06M13/165D06M13/192D06M13/148D06M11/44D06M13/232D06M15/03D06M11/80D06M11/74D06M15/09D06M10/00D06M101/06D03D15/217D03D15/225D03D15/283D03D15/33D03D15/47D03D15/50
Inventor 陈菊珍陈菊媛
Owner SUZHOU CHENHENG WEAVING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com