Abrasion resistant steel and low-carbon steel dissimilar metal submerged-arc welding technology

A welding process and dissimilar metal technology, applied in the field of dissimilar metal welding process, to achieve the effect of reducing production cost, ensuring normal production and high weld strength

Active Publication Date: 2015-05-20
云南昆钢新型复合材料开发有限公司
View PDF10 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the technical problem of welding high-carbon, high-manganese wear-resistant steel and low-carbon steel dissimilar metals when welding wear-resistant composite material blanks, the invention provides a high-carbon, high-manganese wear-resistant steel and low-carbon steel dissimilar metals Submerged arc welding welding process, through the adjustment and control of welding position, we

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Abrasion resistant steel and low-carbon steel dissimilar metal submerged-arc welding technology
  • Abrasion resistant steel and low-carbon steel dissimilar metal submerged-arc welding technology
  • Abrasion resistant steel and low-carbon steel dissimilar metal submerged-arc welding technology

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0045] Example 1

[0046] The welding process of wear-resistant steel and low carbon steel dissimilar metal submerged arc welding, the welding diagram is as follows figure 2 As shown, including the following steps:

[0047] Step (1), select dry, oil-free, and rust-free carbon steel welding wire 5, and keep the welding wire dry, oil-free and rust-free in the welding area; select alkaline flux as the flux, and the flux must be at 300℃ before welding Bake for 2 hours;

[0048] Step (2), when the welding voltage is 25V, the welding current is 250A, the welding speed is 0.2m / min, the groove depth is 10mm, the groove angle is 120°, and the interlayer temperature is 40°C, the resistance to wear-resistant steel Fully welded with low carbon steel groove, and the connection method is DC positive connection during welding;

[0049] Step (3): During the first welding, first weld 6 is performed on the side of low carbon steel 1 first, and after the welding is completed, the second welding 10 is ...

Example Embodiment

[0055] Example 2

[0056] The welding process of wear-resistant steel and low carbon steel dissimilar metal submerged arc welding, the welding diagram is as follows figure 2 As shown, including the following steps:

[0057] Step (1), select dry, oil-free, and rust-free carbon steel welding wire, and keep the welding wire dry, oil-free and rust-free in the welding area; choose alkaline flux as the flux, and the flux must be baked at 400 ℃ before welding 1 hour;

[0058] Step (2), when the welding voltage is 45V, the welding current is 550A, the welding speed is 1.0m / min, the groove depth is 15mm, the groove angle is 100°, and the interlayer temperature is 120°C, for wear-resistant steel Fully welded with low carbon steel groove, and the connection method is DC positive connection during welding;

[0059] Step (3): During the first welding, first weld 6 is performed on the side of low carbon steel 1 first, and after the welding is completed, the second welding 10 is directly performed...

Example Embodiment

[0065] Example 3

[0066] The welding process of wear-resistant steel and low carbon steel dissimilar metal submerged arc welding, the welding diagram is as follows figure 2 As shown, including the following steps:

[0067] Step (1), select dry, oil-free, and rust-free carbon steel welding wire, and keep the welding wire dry, oil-free and rust-free in the welding area; choose alkaline flux as the flux, and the flux must be baked at 350℃ for 1.5 hour;

[0068] Step (2), when the welding voltage is 35V, the welding current is 400A, the welding speed is 0.5m / min, the groove depth is 20mm, the groove angle is 90°, and the interlayer temperature is 80°C. Fully welded with low carbon steel groove, and the connection method is DC positive connection during welding;

[0069] Step (3): During the first welding, first weld 6 is performed on the side of low carbon steel 1 first, and after the welding is completed, the second welding 10 is directly performed on the side 2 of wear-resistant stee...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an abrasion resistant steel and low-carbon steel dissimilar metal submerged-arc welding technology and belongs to the technical field of dissimilar metal welding technologies. According to the technology, by the adjustment and controlling to welding positions, welding parameters, interlayer-temperature and the like, when the high-carbon and high-manganese abrasion resistant steel is welded with the low-carbon steel dissimilar metal, the purposes of preheating before welding and slow cooling after welding are achieved, so that no cracks occur in welding seams after welding is completed, the welding seams do not crack after being heated again through a heating furnace, and it is guaranteed that rolling goes on smoothly. Compared with a traditional abrasion resistant steel and low-carbon steel dissimilar metal welding technology, the abrasion resistant steel and the low-carbon steel dissimilar metal submerged-arc welding technology has no special requirements for raw materials and equipment, so that the manufacturing cost is lowered.

Description

technical field [0001] The invention belongs to the technical field of dissimilar metal welding technology, and in particular relates to a dissimilar metal welding technology related to wear-resistant steel and low carbon steel. Background technique [0002] Wear-resistant steel is generally high carbon (C), high manganese (Mn) alloy steel. Wear-resistant steel is usually used to process and manufacture wear-resistant lining plates and sieve plates, and to produce and transport cement slurry, ore slurry and other transportation pipes. Wear-resistant composite materials produced by low-carbon steel and wear-resistant steel not only have the performance of wear-resistant steel, but also reduce the consumption of wear-resistant steel, thereby reducing the consumption of alloy elements such as manganese (Mn), so wear-resistant composite materials It is gradually replacing the application of wear-resistant steel in various fields. [0003] The production process of wear-resista...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K9/18B23K9/235B23K9/02
CPCB23K9/02B23K9/18B23K9/235
Inventor 张竹明杜顺林尹正培张跃李俊兴王云春武绍权
Owner 云南昆钢新型复合材料开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap