Optimization for synthetic process of triethylenediamine novel cation asphalt emulsifier

A technology of asphalt and emulsified asphalt, which is applied in the field of organic synthesis and effective utilization of polyalkylamine quaternary ammonium salts, can solve problems such as thin covering films, and achieve reduced interfacial tension, high interfacial activity and oil phase compatibility, ultra-low The effect of oil-water interfacial tension

Inactive Publication Date: 2015-06-10
QINGDAO HUICHENG PETROCHEM TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the emulsifying ability of quaternary ammonium salts is equivalent to that of diamines, the covering film formed after combining with stone and other substrates and demulsifying is relatively thin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Optimization for synthetic process of triethylenediamine novel cation asphalt emulsifier
  • Optimization for synthetic process of triethylenediamine novel cation asphalt emulsifier

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Example 1: Weigh a certain amount of the emulsifier in a beaker, add 200ml of water, heat to 50-60°C, stir with a glass rod to dissolve it, and adjust the pH to 2-3 with industrial hydrochloric acid. Then weigh 300g of road petroleum asphalt No. 100, and heat it to 110°C to melt it. Start the colloid mill (preheat it with 60°C hot water before starting), inject the emulsifier aqueous solution into the colloid mill, then slowly pour the asphalt into the colloid mill for emulsification, and put the emulsion into the colloid mill for about one minute. Mineral water bottle, close the colloid mill.

[0029] Weigh 100g of stone, take a certain amount of water and additives, add it to the iron bowl, mix evenly, then weigh a certain amount of emulsified asphalt, pour it into the iron bowl, stir quickly and fully, and start timing, and the record can be mixed time and molding time.

[0030] Emulsification conditions: No. 100 road petroleum asphalt, pH=2~3, emulsification measu...

Embodiment 2

[0035] Example 2: Weigh a certain amount of emulsifier in a beaker, add 200ml of water, heat to 50-60°C, stir with a glass rod to dissolve it, and adjust the pH to 2-3 with industrial hydrochloric acid. Then weigh 300AH-90 asphalt and heat it to 120°C to melt it. Start the colloid mill (preheat it with 60°C hot water before starting), inject the emulsifier aqueous solution into the colloid mill, then slowly pour the asphalt into the colloid mill for emulsification, and put the emulsion into the colloid mill for about one minute. Mineral water bottle, close the colloid mill.

[0036] Weigh 100g of stone, take a certain amount of water and additives, add it to the iron bowl, mix evenly, then weigh a certain amount of emulsified asphalt, pour it into the iron bowl, stir quickly and fully, and start timing, and the record can be mixed time and molding time.

[0037] Emulsification conditions: AH-90 asphalt, pH=2, emulsification measurement is 1%.

[0038] Emulsification effect:...

Embodiment 3

[0042] Example 3: Take a certain amount of emulsifier in a beaker, add 200ml of water, heat to 50-60°C, stir with a glass rod to dissolve it, and adjust the pH to 2-3 with industrial hydrochloric acid. Then weigh 300g of Road Petroleum Asphalt No. 180, and heat it to 100°C to melt it. Start the colloid mill (preheat it with 60°C hot water before starting), inject the emulsifier aqueous solution into the colloid mill, then slowly pour the asphalt into the colloid mill for emulsification, and put the emulsion into the colloid mill for about one minute. Mineral water bottle, close the colloid mill.

[0043] Weigh 100g of stone, take a certain amount of water and additives, add it to the iron bowl, mix evenly, then weigh a certain amount of emulsified asphalt, pour it into the iron bowl, stir quickly and fully, and start timing, and the record can be mixed time and molding time.

[0044] Emulsification conditions: No. 180 road petroleum asphalt, pH=2~3, emulsification measuremen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface tensionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a novel asphalt emulsifier by using rosin, chloropropylene oxide and diethylenetriamine through a two-step reaction, and an optimum reaction technology condition for synthesizing the asphalt emulsifier is obtained. According to the invention, CMC value of a target product is 4.89*10<-4>mol / L, the value is little; and the surface tension under critical micelle concentration is 25.28mN / m. The synthesized emulsifier is the median-cracking type asphalt emulsifier, can be widely used for a bonding layer, a fog sealing layer and solvent-free cold mixing, and can be used for recovery and utilization of asphalt and stabilization of an asphalt pavement base layer.

Description

technical field [0001] The invention relates to the organic synthesis and effective utilization of polyalkylamine quaternary ammonium salts, and belongs to the field of chemical organic synthesis. Background technique [0002] In recent years, with the development of the economy, countries all over the world have higher and higher requirements for traffic roads and roads. It is hoped that the built roads can drive various types of vehicles and reduce unnecessary maintenance costs. Especially on fast-moving expressways, the requirements for the driving surface are higher. Experience shows that the pavement made of emulsifier is an ideal pavement material. [0003] For the development of emulsified asphalt, it mainly focuses on how to control the demulsification time of asphalt emulsion and prepare a uniform and stable fine emulsion. Generally, the bitumen content in the emulsion is below 65%, but countries such as France have developed O / W emulsions with a bitumen concentra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07C219/12C07C213/02C08J3/03C08L95/00
Inventor 朱洪学周卫星
Owner QINGDAO HUICHENG PETROCHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com