Titanium nickel alloy workpiece chemical polishing working solution and production method thereof

A chemical polishing and titanium-nickel alloy technology, which is applied in the field of chemical polishing working fluid for titanium-nickel alloy workpieces, can solve problems such as polishing surface damage, achieve high removal rate, convenient cleaning, and save energy consumption

Inactive Publication Date: 2015-06-17
DALIAN SANDAAOKE CHEM
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the chemical polishing working fluids applied to titanium-nickel alloy workpieces are basically composed of oxidizing agents, passivating agents, corrosive agents and activating agents. Disadvantages of big damage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] A kind of chemical polishing working liquid of titanium-nickel alloy workpiece, it is characterized in that each raw material and consumption are as follows: every 1000 L liquid contains sodium thiosulfate 8g, the raw material of every 1000 L liquid is hydrofluoric acid 200L, fluosilicic acid 30L, nitric acid 380L, hydrogen peroxide 150L, ​​phosphoric acid 200L and water 40L.

[0008] The production method is carried out according to the following steps: add the calculated and weighed deionized water into the reaction kettle, heat it to 45°C, start the agitator and control the speed at 60 rpm, and then add the calculated and weighed sodium thiosulfate, hydrofluoric acid , Fluosilicic acid, nitric acid, hydrogen peroxide and phosphoric acid were added to the reaction kettle in turn, and stirred while adding until the mixture was uniform. When the temperature of the solution dropped to room temperature, the material was discharged and packaged.

[0009] The chemical polis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a titanium nickel alloy workpiece chemical polishing working solution. 1000L of the titanium nickel alloy workpiece chemical polishing working solution comprises following raw materials, 8g of sodium thiosulfate, 200L of hydrofluoric acid, 30L of fluosilicic acid, 380L of nitric acid, 150L of hydrogen peroxide, 200L of phosphoric acid, and 40L of water. A production method comprises following steps: weighed deionized water is delivered into a reaction vessel, and is heated to 45 DEG C; a stirrer is turned on, and rotating speed is controlled to be 60r / min; weighed sodium thiosulfate, hydrofluoric acid, fluosilicic acid, nitric acid, hydrogen peroxide, and phosphoric acid are delivered into the reaction vessel successively with stirring until uniform mixing is realized; and an obtained solution is cooled to room temperature, and is collected and packaged.

Description

technical field [0001] The invention relates to a chemical polishing fluid for metal workpieces and a production method, in particular to a chemical polishing fluid and a production method for titanium-nickel alloy workpieces with convenient cleaning after polishing, high removal rate and low damage. Background technique [0002] Chemical polishing is a method that uses chemical reagents (polishing fluid) to selectively dissolve the uneven areas of the sample surface to eliminate wear marks and etch leveling. At present, the chemical polishing working fluids applied to titanium-nickel alloy workpieces are basically composed of oxidizing agents, passivating agents, corrosive agents and activating agents. The disadvantage of large damage. Contents of the invention [0003] The present invention aims to solve the above-mentioned technical problems existing in the prior art, and provides a chemical polishing working liquid and a production method for a titanium-nickel alloy w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23F3/06
Inventor 潘德顺吕栓锁卢建明
Owner DALIAN SANDAAOKE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com