Sintering prevention vanadium-containing stone coal microwave roasting method

A microwave roasting and anti-sintering technology is applied in the field of vanadium extraction from stone coal, which can solve the problems of reducing material sintering, affecting the forward progress of vanadium-containing stone coal and its roasting effect, etc., so as to improve air permeability, reduce sintering phenomenon, and achieve good effect. Effect

Inactive Publication Date: 2015-06-24
WUHAN UNIV OF SCI & TECH
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] To sum up, microwave roasting of vanadium-containing stone coal can obtain a higher vanadium leaching rate in the leaching operation of vanadium-containing stone coal, but the sintering of materials will seriously affect the forward progress of the vanadium-containing stone coal microwave roasting process and its roasting. Effect
At present, there is no treatment method that can effectively reduce material sintering and give full play to the beneficial effect of microwave roasting.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An anti-sintering microwave roasting method for vanadium-containing stone coal. The concrete steps of described method are:

[0024] Step 1. First crush the vanadium-containing stone coal until the particle size is less than 6mm, and then divide it into coarse-grained vanadium-containing stone coal and fine-grained vanadium-containing stone coal. The particle size of the coarse-grained vanadium-containing stone coal is less than 6mm and greater than or equal to 1mm, the particle size of fine-grained vanadium-containing stone coal is less than 1mm.

[0025] Step 2. According to the mass ratio of fine-grained vanadium-containing stone coal to water: 1:0.06~0.07, add water to the fine-grained vanadium-containing stone coal, granulate, and obtain pellets with a particle size of 3-8 mm, and dry , to obtain dried pellets.

[0026] Step 3: Place the dried pellets in an industrial microwave roasting equipment as a base material and spread them on the bottom layer,...

Embodiment 2

[0030] An anti-sintering microwave roasting method for vanadium-containing stone coal. The concrete steps of described method are:

[0031] Step 1. First crush the vanadium-containing stone coal until the particle size is less than 6mm, and then divide it into coarse-grained vanadium-containing stone coal and fine-grained vanadium-containing stone coal. The particle size of the coarse-grained vanadium-containing stone coal is less than 6mm and greater than or equal to 1mm, the particle size of fine-grained vanadium-containing stone coal is less than 1mm.

[0032] Step 2. According to the mass ratio of fine-grained vanadium-containing stone coal to water: 1:0.07~0.08, add water to the fine-grained vanadium-containing stone coal, granulate, and obtain pellets with a particle size of 3-5mm, and dry , to obtain dried pellets.

[0033] Step 3: Place the dried pellets in an industrial microwave roasting equipment as a base material and spread them on the bottom lay...

Embodiment 3

[0037] An anti-sintering microwave roasting method for vanadium-containing stone coal. The concrete steps of described method are:

[0038] Step 1. First crush the vanadium-containing stone coal until the particle size is less than 6mm, and then divide it into coarse-grained vanadium-containing stone coal and fine-grained vanadium-containing stone coal. The particle size of the coarse-grained vanadium-containing stone coal is less than 6mm and greater than or equal to 1mm, the particle size of fine-grained vanadium-containing stone coal is less than 1mm.

[0039] Step 2. According to the mass ratio of fine-grained vanadium-containing stone coal to water: 1:0.08~0.09, add water to the fine-grained vanadium-containing stone coal, granulate, and obtain pellets with a particle size of 5-8mm, and dry , to obtain dried pellets.

[0040] Step 3: Place the dried pellets in an industrial microwave roasting equipment as a base material and spread them on the bottom lay...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a sintering prevention vanadium-containing stone coal microwave roasting method. According to the technical scheme, the method includes: crushing vanadium-containing stone coal into coarse-grained vanadium-containing stone coal with the grain size less than 6mm and greater than 1mm and fine-grained vanadium-containing stone coal with the grain size less than 1mm; adding water to the fine-grained vanadium-containing stone coal to be mixed according to the mass ratio of the fine-grained vanadium-containing stone coal to the water of 1:0.06-0.09 to produce small balls 3-8mm in grain size and drying the small balls; placing the dried small balls in an industrial microwave roasting device as bedding materials, placing the coarse-grained vanadium-containing stone coal on the bedding materials prior to microwave roasting, and cooling to indoor temperature to obtain vanadium-containing stone coal roasting materials, wherein the microwave roasting is characterized in that the temperature rate ranging from 25 DEG C / min to 55 DEG C / min is increased rapidly to the temperature rate ranging from 750 DEG C to 850 DEG C, 25-40 min constant-temperature microwave roasting is performed, and the industrial microwave roasting device is 2400 to 2500 MHz (megahertz) in frequency. With the method, sintering during microwave roasting of the vanadium-containing stone coal is obviously reduced, and the effect of microwave roasting is good.

Description

technical field [0001] The invention belongs to the technical field of vanadium extraction from stone coal. In particular, it relates to a sintering-proof microwave roasting method for vanadium-containing stone coal. Background technique [0002] Vanadium-containing stone coal is an important vanadium-containing resource unique to my country. Through the continuous efforts of scientific and technological workers and the growing scale of the vanadium extraction industry from stone coal, vanadium extraction from stone coal has become an extremely important part of the field of vanadium extraction. Most of the vanadium in stone coal is trivalent vanadium, and it often occurs in aluminosilicate minerals such as mica and illite in the form of isomorphism, which is relatively stable. The traditional sodium roasting-water leaching vanadium extraction process has been gradually replaced by the blank roasting-acid leaching and direct acid leaching processes that are currently becomi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B1/02C22B1/24C22B34/22
Inventor 张一敏袁益忠刘涛黄晶包申旭陈铁军
Owner WUHAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products