Method for preparing refractory material binder by oxidizing waste water sludge from aluminum alloy profile factory

A technology for oxidizing wastewater and refractory materials, applied in adhesives, inorganic adhesives, etc., can solve environmental pollution and other problems, achieve the effects of reducing environmental pollution, easy mixing and molding, and simple and easy preparation methods

Inactive Publication Date: 2016-08-17
TANGSHAN COLLEGE
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, manufacturers of aluminum alloy profiles generally produce hundreds of tons of the above-mentioned sludge that cannot be treated and can only be landfilled, causing great environmental pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The present invention is described in detail below in conjunction with the examples, the purpose is only to better understand the contents of the present invention, and the examples given are not intended to limit the contents of the present invention.

[0016] A method for preparing a refractory material binder by oxidizing waste water sludge from an aluminum alloy profile factory is carried out according to the following steps:

[0017] (1) Take the sludge recovered from the oxidation wastewater treatment of the aluminum material factory, the chemical composition of the sludge is calculated by weight percentage: Al 2 o 3 60.50, SiO 2 2.15, Na 2 O 1.67, CaO 0.22, SO 3 2.15, P 2 o 5 1.30, loss on ignition 32.01; after washing and suction filtration, according to the dry weight of sludge, add sludge accounting for 20% of the total weight of raw materials into the reaction vessel;

[0018] (2) Add water accounting for 30% of the total weight of raw materials int...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing a refractory material adhesive from oxidized wastewater sludge in aluminum alloy section plants, which comprises the following steps: taking sludge, washing with water, carrying out vacuum filtration, adding 10-30% of sludge into a reaction vessel on dry basis of sludge, adding 10-30% of sludge into the reaction vessel, adding 20-40% of water, and regulating the sludge into paste; slowly adding 40-60% of phosphoric acid, heating until the mixture temperature reaches 80-120 DEG C, promoting chemical reaction while continuously stirring, and finishing the reaction when the solution becomes clear and transparent; and cooling to room temperature, and standing for 24 hours to obtain the refractory material adhesive. The main component is aluminum dihydrogen phosphate, the pH value is 1.46, and the density is 1.45-1.47 g / cm<3>. The method is simple and easy to implement and low in cost, can recycle the oxidized wastewater sludge in aluminum alloy section plants, achieves the goal of waste comprehensive utilization, and reduces the environmental pollution caused by direct discharge of waste.

Description

technical field [0001] The invention relates to a treatment method for oxidized wastewater sludge from an aluminum alloy profile factory, in particular to a method for preparing refractory material binders from the oxidized wastewater sludge from an aluminum alloy profile factory. Background technique [0002] A large amount of waste water and sludge will be generated during the production and processing of aluminum alloy profiles. The sources are as follows: ①The alkaline solution after the mold is boiled and washed is all discharged into the waste water, which wastes a lot of alkali and generates a large amount of sludge every day; ②With the During the production, the aluminum in the alkali etching tank will continue to accumulate, and when it reaches a certain level, it will be discarded and discharged, and a large amount of alkali will be wasted and a large amount of sludge will be generated; carry out, the aluminum ions continue to rise, and when it reaches a certain le...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J1/00
Inventor 刘大成宋长友刘艳娟孙秀君李悦吴爱兵王仲军葛伟青魏利滨项新成
Owner TANGSHAN COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap