Polyethylene foamed packaging film and processing method thereof

A technology of polyethylene foaming and processing methods, applied in chemical instruments and methods, lamination devices, lamination, etc., can solve the problems of stretchability, mechanical strength, surface strength and surface flatness, etc., and achieve enhanced stretchability , Improve the effect of quality performance

Inactive Publication Date: 2015-07-29
ANHUI YUANZHOU PACKAGING MATERIAL CO LTD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a polyethylene foam packaging film with stable process, good quality and high strength, aiming at defects...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyethylene foamed packaging film and processing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A polyethylene foam packaging film and its processing method, characterized in that: the polyethylene foam packaging film is sequentially composed of high polymer layer one, foam layer, high polymer layer two, metal composite layer, barrier layer Composition, the high polymer layer one is PET 12 The high polymer layer of the material, its thickness accounts for 5% of the total thickness of the polyethylene foam packaging film, and the foam layer is EPE 147 The foam layer of the material, its thickness accounts for 65% of the total thickness of the polyethylene foam packaging film, and the second high polymer layer is PET 12 The high polymer layer of the material, its thickness accounts for 5% of the total thickness of the polyethylene foam packaging film, and the metal composite layer is AL 12 Aluminum foil layer made of aluminum foil, its thickness accounts for 5% of the total thickness of polyethylene foam packaging film, and the barrier layer is PEY 45 The barrie...

Embodiment 2

[0025] A polyethylene foam packaging film and its processing method, characterized in that: the polyethylene foam packaging film is sequentially composed of high polymer layer one, foam layer, high polymer layer two, metal composite layer, barrier layer Composition, the high polymer layer one is PET 12 The high polymer layer of the material, its thickness accounts for 10% of the total thickness of the polyethylene foam packaging film, and the foam layer is EPE 147 The foaming layer of material, its thickness accounts for 55%% of the total thickness of polyethylene foaming packaging film, and described high polymer layer two is PET 12 The high polymer layer of the material, its thickness accounts for 10% of the total thickness of the polyethylene foam packaging film, and the metal composite layer is AL 12 Aluminum foil layer made of aluminum foil, its thickness accounts for 10% of the total thickness of polyethylene foam packaging film, and the barrier layer is PEY 45 The b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polyethylene foamed packaging film and a processing method thereof. The polyethylene foamed packaging film is characterized by comprising a high polymer layer I, a foaming layer, a high polymer layer II, a metal composite layer and a partition layer in sequence, wherein the high polymer layer is made of a PET12 material; the foamed layer is made of an EPE147 material; the high polymer layer is made of the PET12 material; the metal composite layer is an aluminum foil layer made of an AL12 material; the partition layer is made of a PEY45 material. The polyethylene foamed packaging film is of a five-layer structure, the quality performance of the polyethylene foamed film is greatly improved, the high polymer layer I is combined with the partition layer after being combined with the foamed layer, the high polymer layer II and the metal composite layer in a processing process, and finally total compounding is peformed, so that the quality performance of the polyethylene foamed film is improved, and the flexibility, the mechanical strength, the surface strength and the surface evenness of the polyethylene foamed film are improved.

Description

[0001] technical field [0002] The invention relates to the processing field of packaging films, in particular to a polyethylene foam packaging film and a processing method thereof. Background technique [0003] With the improvement of consumers' awareness of health and environmental protection, they pay more and more attention to the packaging materials of products. Foam packaging film is one of many packaging film products. During the processing of the existing foam packaging film, the compounding of the multi-layer structure is difficult to control, resulting in unsatisfactory stretchability, mechanical strength, surface strength and surface smoothness, and the product quality needs to be improved. Contents of the invention [0004] The purpose of the present invention is to provide a polyethylene foam packaging film with stable process, good quality and high strength, aiming at defects such as unsatisfactory flexibility, mechanical strength, surface strength an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B15/085B32B15/04B32B27/08B32B27/36B32B7/12B32B37/15B32B37/12B32B38/16
Inventor 范道钱
Owner ANHUI YUANZHOU PACKAGING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap