A technology of composite water blocking and reinforcement materials, applied in the direction of chemical instruments and methods, drilling compositions, etc., can solve the problems of water pollution, water solubility, high cost, etc., and achieve good environmental protection, good durability, and low cost low effect

Inactive Publication Date: 2015-07-29
SHANDONG YOUGU NEW MATERIAL TECH CO LTD
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing polyurethane reinforcement materials are not only extremely expensive, but also easily soluble in water, so they cannot block a large amount of gushing water, and in particular, they will cause serious pollution to water bodies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] In the embodiment of the present invention, an organic-inorganic composite water plugging reinforcement material is composed of component A and component B: the raw materials of component A according to mass percentage include 99% water glass, 0.5% chain extender crosslinking agent, and organic metal Catalyst 0.2% and amine catalyst 0.3%; The raw materials of component B according to mass percentage include crude MDI 75%, polypropylene glycol PPG-2000 8%, polyether triol 330N 2%, diluent 14% and foam stabilizer 1% ; The mass ratio of component A and component B is 1:0.7. Water glass is potassium water glass with a water glass modulus of 2. The chain extension crosslinking agent is glycerin. The organometallic catalyst is potassium acetate. The amine catalyst is an aliphatic amine catalyst. The crude MDI is polymethylene polyphenyl isocyanate PM-200.

[0020] The preparation method of the organic-inorganic composite water plugging reinforcement material includes the fol...

Embodiment 2

[0022] In the embodiment of the present invention, an organic-inorganic composite water plugging reinforcement material is composed of component A and component B: the raw materials of component A according to mass percentage include 97.9% water glass, 1% chain extension crosslinking agent, and organic metal Catalyst 0.4% and amine catalyst 0.7%; the raw materials of component B according to mass percentage include crude MDI 70%, polypropylene glycol PPG-2000 4%, polyether triol 330N 7%, diluent 17.5% and foam stabilizer 1.5% ; The mass ratio of component A and component B is 1:0.9. The water glass is sodium water glass with a water glass modulus of 3. The chain extension crosslinking agent is 1,4-butanediol. The organometallic catalyst is zinc isooctanoate. The amine catalyst is one or a mixture of two or more of alicyclic amine catalysts, aromatic amine catalysts, and amine compound catalysts. The crude MDI is polymethylene polyphenyl isocyanate PM-200.

[0023] The prepara...

Embodiment 3

[0025] In the embodiment of the present invention, an organic-inorganic composite water plugging reinforcement material is composed of component A and component B: the raw materials of component A according to mass percentage include 97% water glass, 1.5% chain extender crosslinking agent, and organic metal Catalyst 0.6% and amine catalyst 0.9%; B component in terms of mass percentage of raw materials including crude MDI 65%, polyether triol 330N 10%, diluent 23% and foam stabilizer 2%; A component and B component The mass ratio is 1:1.2. Water glass is a mixture of sodium water glass and potassium water glass with a water glass modulus of 2. The chain extension crosslinking agent is triethylene glycol. The organometallic catalyst is dibutyltin dilaurate. The amine catalyst is an aromatic amine catalyst. The crude MDI is polymethylene polyphenyl isocyanate PM-200.

[0026] The preparation method of the organic-inorganic composite water plugging reinforcement material includes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an organic-inorganic composite water plugging reinforcement material and a preparation method thereof. The material consists of a component A and a component B, wherein the component A comprises the following ingredients by weight percent: 97-99% of water glass, 0.5-1.5% of a chain extension cross-linking agent, 0.2-0.6% of an organo-metallic catalyst, and 0.3-0.9% of an amine catalyst; the component B comprises the following ingredients by weight percent: 65-75% of crude MDI, 0-8% of PPG (polypropylene glycol)-2000, 2-10% of polyether triol 330N, 14-23% of a diluent and 1-2% of a foam stabilizer; the mass ratio of the component A to the component B is 1:(0.7-1.2). The preparation method comprises the following steps: mixing the ingredients of the component B according to the weight percent, leaving the mixture to stand for 12 hours, adding the component A, and uniformly stirring, so as to obtain the water plugging reinforcement material which is high in strength, good in environment friendliness and durability, non-flammable, and low in cost. According to the invention, the limitation problem that a polyurethane water plugging material can be used for reinforcement or plugging of a small amount of leakage water only.

Description

Technical field [0001] The invention relates to the field of water blocking materials, in particular to an organic-inorganic composite water blocking reinforcement material and a preparation method thereof. Background technique [0002] Organic reinforcing materials are generally composed of polyisocyanate (crude MDI, commonly known as black material) and combined polyether (multifunctional polyether, small alcohol, flame retardant and other additives, gel catalyst, strong blowing catalyst or trimerization catalyst) It is a polymer material formed after mixing one or two or more of them, commonly known as white material. The existing polyurethane reinforcement materials are not only extremely expensive, but also easy to dissolve in water, cannot block a large amount of water gushing, and especially cause great pollution to the water body. Summary of the invention [0003] The purpose of the present invention is to provide a low-cost, environmentally friendly organic-inorganic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G18/76C08G18/66C08G18/48C08G18/32C09K8/467
CPCC08G18/3206C08G18/4812C08G18/4825C08G18/4829C08G18/6674C08G18/6677C08G18/7664C09K8/426C09K8/467
Inventor 刘鹏苗本雨何国林李露露
Owner SHANDONG YOUGU NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap