Preparation method of ultra-high molecular weight polyethylene cotton type cut-resistant gloves

An ultra-high molecular weight, polyethylene technology, applied in protective clothing, clothing, clothing, etc., can solve the problems of high cost, airtight and sweat absorption, and achieve the effect of good elasticity, comfortable and convenient wearing, and not easy to hook silk.

Active Publication Date: 2016-08-17
JIANGSU HANVO SAFETY PROD CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the existing cut-resistant gloves use the method of adding steel wire or carbon fiber inside the glove, which is expensive, airtight and sweat-absorbing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0023] A method for preparing ultra-high molecular weight polyethylene cotton type cut-resistant gloves, the glove is passed through yarn: ultra-high molecular weight polyethylene / polyester staple fiber blended yarn, polyester-coated spandex-coated yarn, PVC-coated glass fiber spandex long Silk yarn and elastic thread are mixed and woven; the cuffs of the woven gloves are closed with knitted rib cuffs, and at a temperature of 120°C, they are formed by a hot-melt machine for one-time hot-melt hemming, and the surface is chemically treated with a waterproof finishing agent , to get the finished product.

[0024] Use the full computer U3 high-speed glove knitting machine for knitting, select the 13-needle knitting program for the stitch length, and select 40 parts of the above-mentioned ultra-high molecular weight polyethylene / polyester blended yarn, cotton-wrapped spandex core when knitting the palm and fingers 10 parts of yarn, 30 parts of PVC-coated glass fiber spandex filamen...

specific Embodiment 2

[0026] A method for preparing ultra-high molecular weight polyethylene cotton type cut-resistant gloves, the glove is passed through yarn: ultra-high molecular weight polyethylene / polyester staple fiber blended yarn, polyester-coated spandex-coated yarn, PVC-coated glass fiber spandex long Silk yarn and elastic thread are mixed and woven; the cuffs of the woven gloves are closed with knitted rib cuffs. At a temperature of 180°C, they are formed by a hot-melt machine for one-time hot-melt hemming and treated with a waterproof finishing agent. , to get the finished product.

[0027] Use the full computer U3 high-speed glove knitting machine for knitting, and select the knitting program of 15 stitches. When knitting the palm and fingers, choose 50 parts of the above-mentioned ultra-high molecular weight polyethylene / polyester blended yarn, cotton-wrapped spandex core 30 parts of yarn, 40 parts of PVC coated glass fiber spandex filament yarn.

[0028] When the ultra-high molecula...

specific Embodiment 3

[0029] A method for preparing ultra-high molecular weight polyethylene cotton type cut-resistant gloves, the glove is passed through yarn: ultra-high molecular weight polyethylene / polyester staple fiber blended yarn, polyester-coated spandex-coated yarn, PVC-coated glass fiber spandex long Silk yarn and elastic thread are mixed and woven; the cuffs of the woven gloves are closed with knitted rib cuffs. At a temperature of 130°C, they are formed at one time by a hot-melt machine for hot-melt hemming, and are chemically treated on the surface with a waterproof finishing agent. , to get the finished product.

[0030] Use the full computer U3 high-speed glove knitting machine for knitting, select the knitting program of 15 stitches, and when knitting the palm and fingers, use the above-mentioned yarn ultra-high molecular weight polyethylene / polyester blended yarn 42 parts, cotton-wrapped spandex core 16 parts of yarn, 33 parts of PVC-coated glass fiber spandex filament yarn.

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for producing ultra-high molecular weight polyethylene cotton-type anti-cutting gloves. The gloves are formed by mixing and weaving of yarns such as ultra-high molecular weight polyethylene / polyester staple fiber blended yarns, polyester spandex wrap yarns, polyvinyl chloride (PVC) coated glass fiber spandex filament yarns and elastic yarns, cuffs of woven gloves are closed up by knitted rib cuffs, hot melting edge wrapping and one-time forming are achieved through a hot melting machine at the temperature from 120 DEG C to 180 DEG C, and surface chemical processing is performed through water-proof finishing agents so that finished products can be obtained. According to the method for producing the ultra-high molecular weight polyethylene cotton-type anti-cutting gloves, the process is simple, large-scale automatic production can be achieved, the anti-cutting performance of the gloves is high, the elasticity is good, a user can conveniently and comfortably wear the gloves, and the operation is flexible. Besides, the dust-proof effect is good, and harm to products due to falling of fibers of the gloves can be avoided. The gloves can be widely applied to people in special industries such as automobile assembly industry, glass industry, metal rolling sheet industry, cutting industry, recovery processing industry, police and the like.

Description

technical field [0001] The invention relates to labor protection gloves, in particular to a preparation method of ultra-high molecular weight polyethylene blended staple fiber cut-resistant protective gloves. Background technique [0002] Most of the existing cut-resistant gloves adopt the method of adding steel wire or carbon fiber inside the glove, which is expensive, airtight and sweat-absorbent. UltraHigh Molecular Weight Polyethylene Fiber PE (UltraHigh Molecular Weight Polyethylene Fiber PE), also known as high-strength modulus polyethylene fiber, high-performance polyethylene fiber, high-degree orientation polyethylene fiber, has high modulus, high performance, corrosion resistance, density Low-level characteristics, together with aramid fiber and carbon fiber, are called the three high-performance fibers. At present, PE fiber cut-resistant gloves and other industrial application products are basically filament products. Compared with PE staple fiber and yarn product...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A41D19/015A41D31/00
Inventor 张炜栋黄旭张娟
Owner JIANGSU HANVO SAFETY PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap