Part treatment process

A processing technology and parts technology, applied in the field of parts processing technology, can solve problems such as poor performance and incomplete processing of parts, and achieve the effects of high wear resistance, high hardness, and elimination of tissue defects

Inactive Publication Date: 2015-08-05
ZHEJIANG WANXI PRECISION CASTING
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problems of incomplete processing and poor performance of the above-mentioned parts, the purpose of the present invention is to provide a part with good processing performance, high hardness, high plasticity and toughness, high wear resistance, and eliminate structural defects, so that the parts can be used in Handling of parts working under large dynamic loads

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] A part treatment process, characterized in that the specific process is as follows: (1) normalizing; (2) annealing: including recrystallization annealing, stress relief annealing, spheroidizing annealing and complete annealing; (3) tempering : Including low temperature tempering, medium temperature tempering, high temperature tempering and multiple tempering; (4) Quenching: including salt bath quenching, martensite graded quenching, bainite isothermal quenching, surface quenching and partial quenching; Quality: Composite heat treatment process of quenching and tempering. The step (1) normalizing of the present invention is to improve the mechanical properties of the low carbon steel, improve the machinability, refine the crystal grains, and eliminate structural defects, and the step (2) annealing can reduce the hardness of the part material, improve the plasticity, and benefit Cutting or pressure processing can reduce residual stress and improve the homogenization of st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a part treatment process, which is characterized by specifically comprising: (1) normalizing; (2) annealing, wherein the annealing comprises re-crystallization annealing, destressing annealing, spheroidization annealing, and complete annealing; (3) tempering, wherein the tempering comprises low temperature tempering, medium temperature tempering, high temperature tempering, and multiple tempering; (4) quenching, wherein the quenching comprises salt bath quenching, martensite grading quenching, bainite isothermal quenching, surface quenching, and local quenching; and (5) quenching and high temperature tempering, wherein a quenching and tempering composite heat treatment process is performed. The part treatment process of the present invention has the following beneficial conditions that: the performance of the treated part is good, high hardness, high plasticity, high toughness and high wear resistance are provided, the structure defects are eliminated, and the part can work in a larger dynamic load.

Description

technical field [0001] The invention relates to a part processing technology. Background technique [0002] After the metal is cast, smelted and solidified into parts, the material of the parts needs to be further processed to make the parts have high hardness and relatively strong wear resistance. Many manufacturers will use normalizing, annealing, tempering or quenching heat treatment processes Parts are processed. However, the current processing of parts is only to change a single performance such as hardness or wear resistance. The overall performance of the part is not comprehensive. During use, the service life is short and easy to be damaged due to the lack of performance. Contents of the invention [0003] In order to solve the problems of incomplete processing and poor performance of the above-mentioned parts, the purpose of the present invention is to provide a part with good processing performance, high hardness, high plasticity and toughness, high wear resistan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D1/00
Inventor 林芳梅
Owner ZHEJIANG WANXI PRECISION CASTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products