Rubber for buffering supporting piece in automobile

A support and rubber technology, applied in the field of rubber, to achieve strong oil resistance, improve processing performance, high hardness and rigidity

Inactive Publication Date: 2015-09-02
柳州日高汽车减振技术有限责任公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Considering the conditions of use and processing performance, a rubber with high hardness, oil resistance and good processability is needed, but the rubber currently on the market cannot meet the demand, or it can meet one requirement and the other two requirements cannot be met. Either it meets two of the requirements and cannot meet the other requirement, so the existing rubber cannot satisfy the characteristics of high hardness, oil resistance and good processability at the same time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber for buffering supporting piece in automobile
  • Rubber for buffering supporting piece in automobile

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0025] Example 1 Recipe: Materials

[0026] Material

parts by weight

NBR

80

high styrene

20

Zinc oxide

5

stearic acid

1

Dihydroquinoline antioxidants

2

P-aniline antioxidant

1.5

Paraffin

1

N220 carbon black

46

N550 carbon black

30

sulfur

2.2

N-cyclohexyl-2-benzothiazole sulfenamide accelerator

1.5

2,2`-dithiodibenzothiazole accelerator

0.5

[0027] The preparation of above-mentioned composition can adopt banbury mixer and open mill mixing, and its steps are as follows:

[0028] Internal mixer mixing: put high styrene HS-60 into the open mixer, open the roller distance to 0.2-0.5mm thin pass for 6 minutes, then put it into the internal mixer together with NBR 3305 and mix for 90 seconds , and then put in zinc oxide, stearic acid, anti-aging agent and paraffin for mixing. At this time, the temperature of the internal mixer is a...

example 2

[0029] Example 2 Recipe: Materials

[0030] Material

parts by weight

NBR

100

high styrene

/

Zinc oxide

5

stearic acid

1

Dihydroquinoline antioxidants

2

P-aniline antioxidant

1.5

Paraffin

1

N220 carbon black

46

N550 carbon black

30

sulfur

2.2

N-cyclohexyl-2-benzothiazole sulfenamide accelerator

1.5

2,2`-dithiodibenzothiazole accelerator

0.5

[0031] The preparation of above-mentioned composition can adopt banbury mixer and open mill mixing, and its steps are as follows:

[0032] Internal mixer mixing: Put nitrile rubber 3305 into the internal mixer and mix for 90 seconds, add zinc oxide, stearic acid, anti-aging agent and paraffin and mix, add half of the reinforcing agent after 120 seconds, and put in half of the reinforcing agent after 90 seconds For the other half of the reinforcing agent, add sulfur and accelerator after 9...

example 3

[0033] Example 3 Recipe: Materials

[0034] Material

parts by weight

natural rubber

80

high styrene

20

Zinc oxide

5

stearic acid

1

Dihydroquinoline antioxidants

2

[0035] P-aniline antioxidant

1.5

Paraffin

1

N220 carbon black

46

N550 carbon black

30

sulfur

2.2

N-cyclohexyl-2-benzothiazole sulfenamide accelerator

1.5

2,2`-dithiodibenzothiazole accelerator

0.5

[0036] The preparation of above-mentioned composition can adopt banbury mixer and open mill mixing, and its steps are as follows:

[0037] Internal mixer mixing: put high styrene HS-60 and natural rubber (standard one) into the open mixer respectively, open the roller distance to 0.2-0.5mm, masticate separately for 6 minutes, and then put the two together into the Mix in the internal mixer for 120 seconds, put in zinc oxide, stearic acid, anti-aging agent an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
rate of changeaaaaaaaaaa
Login to View More

Abstract

The invention is suitable for the technical field of rubber and provides rubber for buffering supporting piece in an automobile. The rubber comprises or includes the following components in parts by weight: 70-90 parts of nitrile rubber buna, 10-30 parts of high styrene, 1-3 parts of a dihydroquinoline antiaging agent, 1-3 parts of a p-phenylenediamine antiaging agent, 1-4 parts of paraffin, 4-8 parts of an activator, 1-3 parts of stearic acid, 60-100 parts of a reinforcing agent, 0.5-2.5 parts of a vulcanizing agent and 2-5 parts of an accelerant. By using the nitrile rubber buna, the oil resistance of the rubber obtained is greatly improved, so that the product is maintained in a good performance and shape in a working environment filled with oil. By using the high styrene, the hardness of the rubber can be remarkably improved, and the rubber has high hardness on the premise that the filling amount of the rubber product is not high.

Description

technical field [0001] The invention belongs to the technical field of rubber, and in particular relates to a rubber with high hardness, good oil resistance and good processability, which is used for the buffer support parts in automobiles. Background technique [0002] The main function of the automobile shock absorber is buffering and vibration isolation. It can be said that the comfort of the car when driving directly depends on the shock absorber in the car, and the rubber parts are installed on the limiter of the shock absorber connecting rod to play a limiting role. Position, cushioning, vibration isolation, and the connecting rod limiter is filled with hydraulic oil, which requires that the rubber of the inner buffer support must have oil resistance and high hardness, so as to ensure that it is not easy to produce performance during use. changes and play an excellent role in vibration isolation and buffering. Considering the conditions of use and processing performan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L25/06C08L91/06C08K13/02C08K5/09C08K3/06C08K5/18C08K3/04C08K5/47
CPCC08L9/02C08K2201/014C08L2205/03C08L25/06C08L91/06C08K13/02C08K5/09C08K3/06C08K5/18C08K3/04C08K5/47
Inventor 郑羽健林杰
Owner 柳州日高汽车减振技术有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products