Environment-friendly cold-resistant polyvinyl chloride elastomer composition and preparation method thereof

A technology of polyvinyl chloride and polyvinyl chloride resin, applied in the field of materials, can solve the problem of high cost of raw materials for diethylene glycol dibenzoate plasticizers, the influence of elastomers on normal temperature toughness and low temperature toughness, and unsatisfactory low temperature resistance and other problems, to achieve excellent plasticizing effect, good heat aging resistance, and improve the effect of normal temperature toughness

Active Publication Date: 2015-09-09
JIANGSU XINGHUA RUBBER BELT
View PDF17 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the toughening agent used in the patent application number CN201310473887.1 is silicone rubber, which has poor compatibility with the polyvinyl chloride matrix, which affects the normal temperature toughness and low temperature toughness of the elastomer, and the low temperature resistance is not ideal.
The application number is CN201210161975.3, which discloses a cold-resistant and environment-friendly polyvinyl chloride-based special cable material. The diethylene glycol dibenzoate plasticizer used is high in raw material cost, which limits its application in the civil range.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly cold-resistant polyvinyl chloride elastomer composition and preparation method thereof
  • Environment-friendly cold-resistant polyvinyl chloride elastomer composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] The present invention also provides a preparation method of the above-mentioned environment-friendly and cold-resistant polyvinyl chloride elastomer composition, comprising the following steps:

[0030] Step 1: Stir and mix each component in a kneader evenly, and use the friction heat generated by stirring to raise the temperature of the mixture;

[0031] Step 2: After the temperature of the mixture of the components in the kneader rises to 90-100°C, the material is discharged, and then sent to the cooling agitator to cool to below 45°C;

[0032] Step 3: Put the cooled mixture on a two-stage screw extruder to extrude the material. The two-stage screw extruder includes a twin-screw extruder and a single-screw extruder. The twin-screw extruder four The temperatures of each heating zone and the extrusion die are respectively: T1=85~100°C, T2=100~120°C, T3=120~140°C, T4=130~150°C, T die=130~150°C; The temperatures of the heating zone and the extrusion die of the single-scr...

Embodiment 1

[0034]With the polyvinyl chloride resin of 100 weight parts, the dioctyl terephthalate of 75 weight parts, the epoxy soybean oil of 25 weight parts, the polyurethane rubber of 10 weight parts, the nano active calcium carbonate of 15 weight parts, 5 weight parts Calcium-zinc composite stabilizer, 1.5 parts by weight of zinc stearate, 0.6 parts by weight of four [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester and 1 part by weight of The high-pigment carbon black is stirred and mixed at high speed in the kneader. The frictional heat generated by the stirring makes the temperature of the mixed material rise to 90-100°C, and then the material is discharged. The material is extruded and granulated on a twin-screw extruder, wherein the temperatures of the four heating zones of the twin-screw extruder and the extrusion die are respectively: T 1 =85~100℃, T 2 =100~120℃, T 3 =120~140℃, T 4 =130~150℃, T 模 =130-150°C; the temperatures of the heating zone and e...

Embodiment 2

[0036] With the polyvinyl chloride resin of 100 weight parts, the diheptyl terephthalate of 90 weight parts, the epoxy group esterified linseed oil of 10 weight parts, the ethylene-vinyl acetate copolymer of 20 weight parts (vinyl acetate weight percent 40%), 5 parts by weight of nano-active calcium carbonate, 8 parts by weight of calcium-zinc composite stabilizer, 1 part by weight of polyethylene wax, 0.2 parts by weight of tetrakis [β-(3,5-di-tert-butyl- 4-hydroxyphenyl) propionic acid] pentaerythritol ester and 3 parts by weight of rutile titanium dioxide are stirred and mixed at high speed in a kneader. The cooling mixer is cooled to below 45°C, and then the cooled mixture is extruded on a twin-screw extruder for granulation, where the temperatures of the four heating zones of the twin-screw extruder and the extrusion die are: T 1 =85~100℃, T 2 =100~120℃, T 3 =120~140℃, T4 =130~150℃, T 模 =130-150°C; the temperatures of the heating zone and extrusion die of the single-s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Shore hardnessaaaaaaaaaa
Shore hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environment-friendly cold-resistant polyvinyl chloride elastomer composition and a preparation method thereof. The preparation method comprises the following steps: mixing a polyvinyl chloride resin, dialkyl terephthalate, synthetic vegetable oil, polar rubber, nano activated calcium carbonate, a calcium zinc composite stabilizer, a lubricant, an antioxidant and a pigment in a kneader; after the temperature of the mixture reaches 90-100 DEG C, discharging, cooling, and carrying out extrusion granulation on the cooled mixture in a double screw extruder, wherein the Shore hardness of the elastomer composition at -5 DEG C is lower than 80. The elastomer composition has the advantages of excellent low-temperature toughness, high mechanical strength, high thermal aging resistance, environment friendliness, no toxicity, excellent comprehensive properties and the like, and is especially suitable for preparing escalator balance compensation chain sheaths, door / window and vehicle window seals, insulation sheaths of wires and cables and the like.

Description

【Technical field】 [0001] The invention relates to the field of materials, in particular to an environment-friendly cold-resistant polyvinyl chloride elastomer composition and a preparation method thereof. 【Background technique】 [0002] Polyvinyl chloride elastomer has the characteristics of low price, adjustable mechanical properties and good flame retardancy. It is suitable for many occasions such as preparing elevator balance compensation chain sheaths, insulating sheaths for wires and cables, and door and window seals. However, polyvinyl chloride elastomers have certain defects in terms of environmental protection and low-temperature toughness. [0003] So far, many patents have reported the composition and preparation methods of low-temperature-resistant or cold-resistant polyvinyl chloride elastomer materials. For example, the application numbers are CN201210569416.6, CN201410284632.5, CN200810023863.5 and other Chinese patents. Although the polyvinyl chloride elasto...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L75/04C08L23/08C08L33/04C08K13/02C08K5/12C08K5/1515C08K3/26C08K5/098C08K5/134C08K3/04B29C47/92B29C48/92
CPCC08K3/26C08K5/098C08K13/02C08L27/06C08L31/04C08L33/08C08L75/04B29C48/92B29C2948/92704C08K2201/003C08K2201/011C08K2201/014C08L2201/08C08L2205/025C08L2205/03C08L2205/035C08L2205/06C08L91/00C08K5/12C08K2003/265C08K5/1345C08K3/04C08L23/0853C08L23/06C08K2003/2241C08L33/04C08K5/526
Inventor 王庚超魏伟黄近都毛亮
Owner JIANGSU XINGHUA RUBBER BELT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap