Electronic damping paint and preparation method thereof

A damping paint and electronic technology, applied in the field of paint, can solve the problems of unsatisfactory compressive performance and lack of mechanical properties, and achieve the effect of good enclosing, protecting electronic components, and good film-forming effect.

Inactive Publication Date: 2015-10-14
苏州洋杰电子有限公司
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The performance of damping coatings generally includes sound insulation and shock absorption, heat insulation and sealing. It can be directly sprayed on the surface of the substrate, which has certain advantages. The disadvantage is that it does not have sufficient mechanical properties and the compression resistance is not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] An electronic damping paint, comprising the following components in parts by mass:

[0026] 25 parts of epoxy resin, 15 parts of polyurethane, 3 parts of white carbon black, 5 parts of glass fiber, 3 parts of nano-calcium carbonate, 4 parts of polyalkylacrylate, 5 parts of polyamide, 5 parts of alcohol ester twelve and 15 parts of water .

[0027] A preparation method of electronic damping paint, the preparation steps are as follows:

[0028] (1) Accurately weigh each raw material;

[0029] (2) Put the solid phase components into a ball mill and grind them evenly to obtain mixed powder;

[0030] (3) Mix the mixed powder and liquid components together, place them in a static mixer, and mix them uniformly to obtain a premix;

[0031] (4) Put the premixed material indoors for 48 hours to obtain the electronic damping coating.

[0032] The performance of the electronic damping coating was tested, and the results showed that:

[0033] Composite loss factor (η≥0.03, dete...

Embodiment 2

[0036] An electronic damping paint, comprising the following components in parts by mass:

[0037] 40 parts of epoxy resin, 25 parts of polyurethane, 7 parts of white carbon black, 10 parts of glass fiber, 10 parts of nano-calcium carbonate, 9 parts of polyalkylacrylate, 10 parts of polyamide, 12 parts of alcohol ester twelve and 32 parts of water .

[0038] A preparation method of electronic damping paint, the preparation steps are as follows:

[0039] (1) Accurately weigh each raw material;

[0040] (2) Put the solid phase components into a ball mill and grind them evenly to obtain mixed powder;

[0041] (3) Mix the mixed powder and liquid components together, place them in a static mixer, and mix them uniformly to obtain a premix;

[0042] (4) Put the premixed material indoors for 48 hours to obtain the electronic damping coating.

[0043] The performance of the electronic damping coating was tested, and the results showed that:

[0044] Composite loss factor (η≥0.03, ...

Embodiment 3

[0047] An electronic damping paint, comprising the following components in parts by mass:

[0048] 38 parts of epoxy resin, 24 parts of polyurethane, 6 parts of white carbon black, 9 parts of glass fiber, 8 parts of nano-calcium carbonate, 8 parts of polyalkylacrylate, 9 parts of polyamide, 10 parts of alcohol ester twelve and 27 parts of water .

[0049] A preparation method of electronic damping paint, the preparation steps are as follows:

[0050] (1) Accurately weigh each raw material;

[0051] (2) Put the solid phase components into a ball mill and grind them evenly to obtain mixed powder;

[0052] (3) Mix the mixed powder and liquid components together, place them in a static mixer, and mix them uniformly to obtain a premix;

[0053] (4) Place the premixed material in a vacuum for 16 hours to obtain the electronic damping coating.

[0054] The performance of the electronic damping coating was tested, and the results showed that:

[0055] Composite loss factor (η≥0.0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an electronic damping paint and a preparation method thereof, and belongs to the technical field of paints. The paint comprises the following components in parts by weight: 25 to 40 parts of epoxy resin, 15 to 25 parts of polyurethane, 3 to 7 parts of white carbon black, 5 to 10 parts of glass fiber, 3 to 10 parts of nano calcium carbonate, 4 to 9 parts of polyalkyl acrylate, 5 to 10 parts of polyamide, 5 to 12 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, and 15 to 32 parts of water. The preparation method comprises the following steps: (1) weighing; (2) grinding; (3) mixing in a static mixer; (4) indoor standing for 24 to 48 hours to obtain the electronic damping paint. Dual resins are adopted as the damping resin, nano calcium carbonate is taken as the nano filling material to enhance the damping effect of coating, at the same time the coating film-forming effect is good, the electronic elements can be well enclosed by the paint, thus the electronic elements can be better protected, and moreover, the paint has a damping and noise-reducing effect.

Description

technical field [0001] The invention belongs to the technical field of coatings, in particular to an electronic damping coating and a preparation method thereof. Background technique [0002] Electronic coatings are coating compositions for electronic components or equipment. With the advancement of technology, the types and quantities of electronic components and equipment are increasing, and the volume is getting smaller and smaller, and the design is getting more sophisticated. This refined development trend, on the one hand, greatly meets people's use needs, and on the other hand, drives the refined development trend in many fields. [0003] Electronic coatings are a refined field developed to meet the needs of the electronics industry. Different from general coatings, coatings in the electronic field have stricter performance requirements for coating compositions. [0004] First of all, electronic coatings are generally sprayed, so the preparation process needs to be ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D175/04C09D133/08C09D177/00C09D7/12
Inventor 刘杰
Owner 苏州洋杰电子有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com