Polystyrene foam grain light-weight aggregate and preparation method thereof

A technology of polystyrene foam and lightweight aggregate is applied in the field of building materials, which can solve the problems of reducing the durability of composite materials, poor adhesion between particles and cementitious materials, and increasing the water absorption rate of polystyrene foam particles. To achieve the effect of reducing floating, good overall effect and low water absorption

Inactive Publication Date: 2015-10-21
SHIHEZI UNIVERSITY
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, when polystyrene foam particles are used as the filler aggregate of the cementitious material, the cohesive force between the particles and the cementitious material is poor; at the same time, the surface modification changes the advantage that the polystyrene foam particles do not absorb water, which will increase Water absorption by large polystyrene foam particles, reducing composite durability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A lightweight aggregate of polystyrene foam particles, prepared from the following raw materials: polystyrene foam particles, epoxy resin, curing agent, plasticizer and diluent; the polystyrene foam particles are waste polystyrene The foam is broken and formed, and the diameter is 3-5mm; the epoxy resin adopts E44 epoxy resin, the curing agent adopts T31, the plasticizer adopts dibutyl ester, the diluent adopts acetone, and the polystyrene The mass ratio of ethylene foam particles, E44 epoxy resin, T31, acetone and dibutyl ester is 1:2.5~3:2~3:0.25~0.3:0.25~0.3.

[0013] A method for preparing lightweight aggregate of polystyrene foam particles, comprising the steps of: mixing polystyrene foam particles, E44 epoxy resin, T31, acetone, and dibutyl ester in a mass ratio of 1:3:3:0.3:0.3 Weigh it for later use; add T31, acetone, and dibutyl ester in turn to E44 epoxy resin, stir for 1 min to prepare epoxy resin glue, then pour the prepared epoxy resin glue into polystyrene...

Embodiment 2

[0015] A lightweight aggregate of polystyrene foam particles, prepared from the following raw materials: polystyrene foam particles, epoxy resin, curing agent, plasticizer and diluent; the polystyrene foam particles are waste polystyrene The foam is broken and formed, and the diameter is 3-5mm; the epoxy resin adopts E44 epoxy resin, the curing agent adopts T31, the plasticizer adopts dibutyl ester, the diluent adopts acetone, and the polystyrene The mass ratio of ethylene foam particles, E44 epoxy resin, T31, acetone and dibutyl ester is 1:2.5~3:2~3:0.25~0.3:0.25~0.3.

[0016] A method for preparing lightweight aggregate of polystyrene foam particles, comprising the steps of: mixing polystyrene foam particles, E44 epoxy resin, T31, acetone, and dibutyl ester in a mass ratio of 1:2.5:2.5:0.25:0.25 Take by weighing for later use; add T31, acetone, and dibutyl ester in sequence to E44 epoxy resin, stir for 2 minutes to prepare epoxy resin glue, then pour the prepared epoxy resin...

Embodiment 3

[0018] A lightweight aggregate of polystyrene foam particles, prepared from the following raw materials: polystyrene foam particles, epoxy resin, curing agent, plasticizer and diluent; the polystyrene foam particles are waste polystyrene The foam is broken and formed, and the diameter is 3-5mm; the epoxy resin adopts E44 epoxy resin, the curing agent adopts T31, the plasticizer adopts dibutyl ester, the diluent adopts acetone, and the polystyrene The mass ratio of ethylene foam particles, E44 epoxy resin, T31, acetone and dibutyl ester is 1:2.5~3:2~3:0.25~0.3:0.25~0.3.

[0019] A method for preparing lightweight aggregate of polystyrene foam particles, comprising the steps of: mixing polystyrene foam particles, E44 epoxy resin, T31, acetone, and dibutyl ester in a mass ratio of 1:3:2:0.25:0.25 Weigh it for later use; add T31, acetone, and dibutyl ester successively to E44 epoxy resin for 2 minutes to prepare epoxy resin glue, then pour the prepared epoxy resin glue into polyst...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a polystyrene foam grain light-weight aggregate and a preparation method thereof. The polystyrene foam grain light-weight aggregate is prepared from the following raw materials: polystyrene foam grains, E44 epoxy resin, T31, dibutyl ester and acetone. The preparation method comprises the following steps: weighing polystyrene foam grains, E44 epoxy resin, T31, acetone and dibutyl ester according to the mass ratio of 1: (2.5-3): (2-3): (0.25-0.3): (0.25-0.3) for later use; sequentially adding T31, acetone and dibutyl ester into E44 epoxy resin to prepare an epoxy resin adhesive; then pouring the prepared epoxy resin adhesive into the polystyrene foam grains, and uniformly stirring to obtain the polystyrene foam grain light-weight aggregate. The prepared polystyrene foam grain light-weight aggregate has the characteristic of light weight, overcomes the shortcoming that the surface cohesive force between the polystyrene foam grains and a binding material is relatively poor, is extremely low in water absorption and relatively good in service durability, and facilitates reclamation and utilization of waste polystyrene foam.

Description

technical field [0001] The invention belongs to the field of building materials, in particular to a lightweight aggregate of polystyrene foam particles and a preparation method thereof. Background technique [0002] In recent years, polystyrene foam has developed rapidly, and the annual output has exceeded 50 tons. The disadvantage of polystyrene foam is that it cannot be reused, and it cannot be degraded by itself, so that nearly ten million cubic meters of waste polystyrene become white pollutants every year because they cannot be treated and degraded. In the prior art, artificial degradation is mainly used to process waste polystyrene foam, which costs a lot. If these discarded polyphenylene foams are fully utilized, not only can the problem of white pollution be solved, the development of polystyrene foams can be promoted, but also a large amount of capital expenditures caused by waste disposal can be reduced. In order to solve the problem of recovery and utilization o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B16/08C04B26/10
Inventor 马玉薇李刚张付奇李洁汤骅张建鹏刘乐杨方方
Owner SHIHEZI UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products