Compound modified asphalt and preparation method thereof

A technology of compound modified asphalt and asphalt, which is applied in building components, building insulation materials, buildings, etc., to achieve the effect of shortening the preparation period, long service life and good high temperature stability

Inactive Publication Date: 2015-11-04
丁德凤
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the rapid development of my country's smelting industry and iron and steel industry, the smelting industry has higher and higher requirem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] Example 1:

[0016] A composite modified asphalt, which is made of the following raw materials in parts by weight: 100 parts of asphalt, 10 parts of SBS, 4 parts of rubber powder, 4 parts of furfural extraction oil, 3 parts of activator, 3 parts of stabilizer Copies.

[0017] A preparation method of composite modified asphalt includes the following steps:

[0018] (1) Heat a part of the asphalt to 130°C, and then add 2% of SBS and a predetermined amount of furfural extraction oil to the hot asphalt for shear dispersion;

[0019] (2) Add 15% rubber powder and a predetermined amount of activator to another part of asphalt, and swell at a temperature of 180°C for 100 minutes;

[0020] (3) Disperse the pre-dispersed SBS and swollen rubber powder at high speed at 180℃ for 65min;

[0021] (4) Add stabilizer and develop at low speed for 35 min.

[0022] Based on the above, the present invention is prepared with materials such as asphalt, SBS, rubber powder, furfural extract oil, etc., by...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of compound modified asphalt and relates to the technical field of chemical engineering. The compound modified asphalt is prepared from, by weight, 90-110 parts of asphalt, 10 parts of SBS, 4-5 parts of rubber powder, 4-5 parts of furfural extract oil, 3-4 parts of activator and 3-4 parts of stabilizer. The compound modified asphalt is prepared from asphalt, SBS, rubber powder and furfural extract oil, and the ratio of all the components is optimized, so that the prepared compound modified asphalt is good in high-temperature stability, high in low-temperature anti-cracking performance, excellent in ageing resistance and long in service life. All technological parameters are optimized in the preparation process, production efficiency is improved, and the preparation period is shortened.

Description

technical field [0001] The invention relates to the technical field of chemical engineering, in particular to a composite modified asphalt and a preparation method thereof. Background technique [0002] In civil engineering, asphalt is a widely used waterproof material and anti-corrosion material. It is mainly used in the waterproofing of roofs, grounds and underground structures, and the anti-corrosion of wood and steel. Asphalt is also widely used as cementing material for pavement structure in road engineering. It can be used in proportion to build asphalt pavement with different structures after it is mixed with mineral materials of different compositions. It is widely used in expressways. With the rapid development of my country's smelting industry and iron and steel industry, the smelting industry has higher and higher requirements for carbon products, and ordinary medium-temperature pitch can no longer meet its needs due to the difference in its index performance. Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L95/00C08L53/02C08L21/00C08L91/00
Inventor 丁德凤
Owner 丁德凤
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap