A kind of oil-based modified water-based epoxy antirust primer and preparation method thereof

An anti-rust primer and water-based epoxy resin technology, applied in epoxy resin coatings, anti-corrosion coatings, coatings, etc., can solve the problems of difficult promotion and application, low hardness of paint film, slow drying time, etc., and achieve good adhesion. Focus, broad application prospects, tough paint film effect

Active Publication Date: 2018-02-02
镇江德昇新材料科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to its short development history, people do not have a correct understanding of it. So far, my country has not issued a national standard for water-based industrial anti-corrosion coatings. In addition, some of its own characteristics (slow drying time, paint film hardness low) and people's long-term habit of using solvent-based coatings, making its promotion and application encounter many difficulties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of oil-based modified water-based epoxy antirust primer and preparation method thereof
  • A kind of oil-based modified water-based epoxy antirust primer and preparation method thereof
  • A kind of oil-based modified water-based epoxy antirust primer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An oil-based water-based epoxy antirust primer, consisting of component A and component B, the mass ratio of component A to component B is 5:1; by mass fraction, wherein: Components include: 30% water-based epoxy resin curing agent, 5% additives, 45% anti-rust pigment and 20% deionized water; component B includes: 92% solvent-based epoxy resin and 8% epoxy reactive diluent.

[0024] The composition of the auxiliary agent is a dispersant, a wetting agent, a defoamer, an anti-flash corrosion agent, a leveling agent, a stabilizer and a thickener, and the mass ratios of various components in the auxiliary agent to the first component are respectively 0.5 %, 0.2%, 0.3%, 1.0%, 0.2%, 2%, 0.8%.

[0025] The water-based epoxy resin curing agent is a water-dilutable amine curing agent without surfactant, and the amine value of the water-based epoxy resin curing agent is 160.

[0026] The anti-rust pigment is a combination of mica iron oxide, zinc phosphate, zinc oxide, composit...

Embodiment 2

[0038] An oil-based water-based epoxy antirust primer, consisting of component A and component B, the mass ratio of component A to component B is 7:1; by mass fraction, wherein: Components include: 35% water-based epoxy resin curing agent, 4% additives, 40% anti-rust pigments and 21% deionized water; component B includes: 90% solvent-based epoxy resin and 10% epoxy reactive diluent.

[0039] The above additives are composed of dispersant, wetting agent, defoamer, anti-flash corrosion agent, leveling agent, stabilizer and thickener, and the mass ratio of various components in the additive to the component A is 0.5% respectively , 0.2%, 0.3%, 1.0%, 0.2%, 1%, 0.8%.

[0040] The water-based epoxy resin curing agent is a water-dilutable amine curing agent without surfactant, and the amine value of the water-based epoxy resin curing agent is 220.

[0041] The anti-rust pigment is a composition of mica iron oxide, zinc phosphate, zinc oxide, composite iron-titanium powder and titaniu...

Embodiment 3

[0049] An oil-based water-based epoxy antirust primer, consisting of a component and a component B, the mass ratio of the component A to the component B is 6:1; by mass fraction, wherein: Components include: 30% water-based epoxy resin curing agent, 6% additives, 42% anti-rust pigment and 22% deionized water; component B includes: 91% solvent-based epoxy resin and 9% epoxy reactive diluent.

[0050] The above additives are composed of dispersant, wetting agent, defoamer, anti-flash corrosion agent, leveling agent, stabilizer and thickener, and the mass ratio of various components in the additive to the component A is 0.5% respectively , 0.2%, 0.3%, 1.5%, 0.5%, 2%, 1%.

[0051] The water-based epoxy resin curing agent is a water-dilutable amine curing agent without surfactant, and the amine value of the water-based epoxy resin curing agent is 190.

[0052] The anti-rust pigment is a combination of mica iron oxide, zinc phosphate, zinc oxide, composite iron-titanium powder and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses an oil-based modified water-based epoxy anti-rust primer and a preparation method thereof, belonging to the technical field of heavy-duty anti-corrosion coatings. Composed of component A and component B, the mass ratio of component A to component B is 5:1 to 7:1; in terms of mass fraction, component A includes 30 to 35% aqueous Epoxy resin curing agent, 4-6% additives, 40-45% antirust pigment and 20-25% deionized water; component B includes 90-92% solvent-based epoxy resin and 8-10% % epoxy reactive diluent. The oil-based water-based epoxy anti-rust primer provided by the invention has better resistance and construction performance than the existing water-based epoxy anti-rust primer and solvent-based epoxy anti-rust primer, and it has its own advantages in construction. The unique advantages, environmental protection characteristics and construction safety are unmatched by the existing solvent-based epoxy antirust primer.

Description

technical field [0001] The invention belongs to the technical field of heavy-duty anti-corrosion coatings, and in particular relates to an oil-based modified water-based epoxy antirust primer and a preparation method thereof. Background technique [0002] Epoxy anti-corrosion primers are widely used in heavy anti-corrosion fields such as ships, inner and outer walls of pipelines, mine steel frames, aircraft, and high-speed trains. In order to obtain a better anti-corrosion effect, the existing epoxy anti-corrosion primers are generally added with chromium-containing anti-rust pigments, such as chromate containing hexavalent chromium, to improve anti-corrosion performance. Disclosed two-component anticorrosion paint as Chinese patent application publication CN101457116A, CN100526406C, have adopted zinc yellow, chrome yellow, strontium yellow, zinc phosphochromate etc. Harmful to human body, especially hexavalent chromium is carcinogenic. Heavy metal pigments such as chromiu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D7/61C09D5/08
Inventor 李洪岩
Owner 镇江德昇新材料科技有限公司