Vanadium alloying TAM steel and preparing method thereof

A technology of vanadium alloying and chemical composition, which is applied in the field of vanadium alloying TAM steel and its manufacturing process, can solve problems such as inability to meet requirements, and achieve the effects of improving comprehensive mechanical properties, stable steel structure and properties, and improving strength and toughness.

Active Publication Date: 2015-11-11
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Most of the research on TRIP steel in the prior art uses ordinary steel without adding vanadium, and the process only uses traditional technology. The comprehensive mechanical properties of the TRIP steel prepared by it, such as strength and plasticity, especially its resistance to hydrogen-induced delayed fracture, Neither can meet the requirements of the third generation of automotive steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vanadium alloying TAM steel and preparing method thereof
  • Vanadium alloying TAM steel and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] The preparation method of vanadium alloyed TAM steel specifically includes traditional mechanical rolling process smelting, hot rolling, cold rolling and new process Q&P process:

[0031]a. Mechanical rolling process: Smelting and casting steel billets into slabs, heating at 1150-1250°C for 70-90 minutes, then hot-rolling them into 3-5mm thick hot-rolled steel plates, and then cold-rolling them to 1- 1.5mm, the cold rolling reduction rate is 65-75%, and the ferrite + pearlite structure is obtained; among them, the hot rolling finishing temperature is 750-850°C, and the coiling temperature is 650-700°C;

[0032] b. Q&P process: heat the cold-rolled sheet obtained in step a to the austenitizing temperature of 900-920°C at 10°C / s, keep it warm for 600s, then cool it down to room temperature at 50°C / s; then heat it at 10°C / s s Reheat to annealing temperature of 760-850°C, hold for 600s, then cool down to partition temperature of 150-450°C at 50°C / s, hold for 50-200s, and fi...

Embodiment 1

[0040] The composition percentage of each composition of vanadium alloyed TAM steel of the present invention is shown in Table 1 with reference to:

[0041] Table 1 Composition percentage of vanadium alloyed TAM steel

[0042] serial number

[0043] According to the composition percentages of the vanadium alloyed TAM steel in Table 1, traditional mechanical rolling process smelting, hot rolling, cold rolling and new process Q&P process are carried out. The specific process parameters of the traditional mechanical rolling process are shown in Table 2:

[0044] Table 2 The specific process parameters of the mechanical rolling process

[0045]

[0046] The specific process parameters of the new process Q&P process are shown in Table 3:

[0047] Table 3 Q&P process specific process parameters

[0048]

[0049] According to the composition percentages of the vanadium alloyed TAM steel in Table 1 and the mechanical rolling process in Table 2 and the Q&P process in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to vanadium alloying TAM steel and a preparing method thereof, and belongs to the technical field of metal component designing and thermal processing. The vanadium alloying TAM steel comprises, by weight percentage, 0.18%-0.21% of C, 1.48%-1.55% of Si, 1.90%-2.20% of Mn, not larger than 0.020% of P, not larger than 0.015% of S, 0.19%-0.21% of V, not larger than 0.04% of Al and the balanced Fe and inevitable impurities. An appropriate amount of vanadium is added in a vanadium alloying manner, the toughness of the TAM steel is improved through precipitation of carbide of vanadium and the like, and therefore the comprehensive mechanical performance of vanadium-containing TAM steel is improved, and a steel plate has high strength and plasticity and especially has the superior hydrogen resisting and induced delaying fracture performance. According to the production of the vanadium-contained TAM steel, the steel organization performance is more stable through the new technology-Q&P technology.

Description

technical field [0001] The invention relates to a vanadium alloyed TAM steel and a manufacturing process thereof, belonging to the technical field of metal composition design and thermal processing. Background technique [0002] TAM steel, also known as TRIP type annealed martensitic steel (TRIP-aided Annealed Martensite Matrix), is a kind of Q&P steel. As the third-generation AHSS (Advanced High Strength Steels) steel, Q&P (Quenching and Partitioning) steel for automobiles has natural advantages and has achieved a good match between strength and plasticity. Laboratory data shows that the strength of Q&P steel for automobiles is above 1000 MPa, and the elongation reaches 18 % or more, fully capable of meeting the requirements of bumpers (anti-collision beams), side anti-collision beams (W-type) and other components. The biggest feature of TAM steel is that it breaks through the polygonal ferrite matrix or bainite matrix structure of traditional TRIP steel, and uses the anne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/12C21D8/02
Inventor 蔡晓文杨雄飞唐静杨小琴
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com