Sapphire substrate with colors and preparing method thereof

A sapphire and base material technology, applied in metal material coating process, ion implantation plating, coating, etc., can solve the problems of low product yield, poor surface flatness of sapphire color surface, poor reliability, etc., and achieve product reliability High performance, easy control of environmental cleanliness, good bonding force and flatness effect

Active Publication Date: 2015-11-11
LENS TECH CHANGSHA
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention solves the problems of poor surface flatness, low product yield and poor reliability of the sapphire color surface caused by silk screen printing in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sapphire substrate with colors and preparing method thereof
  • Sapphire substrate with colors and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] This embodiment discloses a method for electroplating metallic aluminum on a circular sapphire substrate to form a white glossy sapphire substrate with metallic aluminum. Specific steps are as follows:

[0037] 1. Clean the sapphire substrate: use a special lotion for sapphire materials to clean through an automatic cleaning machine;

[0038] 2. Install the cleaned sapphire on the jig, and then load the jig with sapphire on the coating rack of the coating equipment;

[0039] 3. Close the door of the coating machine, evacuate the first cavity (not shown in the figure), the vacuum degree is 8.0E-3Pa, the heating pretreatment temperature is 120°C, and the time is 30 minutes;

[0040] 4. After the pretreatment is completed, open the gate of the second cavity (the gate separates the first cavity from the second cavity), transfer the coating frame loaded with sapphire into the second cavity, and vacuumize again, the vacuum degree is 2.0 E-4Pa;

[0041]5. Pretreatment of sa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention firstly provides a sapphire substrate with colors. The sapphire substrate comprises a sapphire substrate body, a first layer, a second layer and a third layer; the first layer, the second layer and the third layer are located on the outer surface of the sapphire substrate body and are sequentially arranged from interior to exterior. The first layer serves as a silicon-dioxide layer, the second layer is a metal film layer, and the third layer is a silicon dioxide layer. The invention further provides a preparing method of the sapphire substrate with the colors. The sapphire substrate which is smooth in surface, does not contain patterns and has the colors is obtained through a coating method. The problems that in the prior art, a sapphire color face brought through silk screen is poor in surface flatness, low in product yield and poor in reliability are solved.

Description

technical field [0001] The invention relates to the field of sapphire processing, in particular to a colored sapphire substrate and a preparation method thereof. Background technique [0002] Due to its high hardness, high light transmittance, and good physical, chemical and optical properties, sapphire has been widely used in electronic devices such as mobile phones and tablet computers. However, since sapphire itself is colorless and transparent, while making full use of its high hardness and other physical and chemical properties, in order to achieve the diversity of appearance colors, it is generally used to obtain sapphire materials with different appearance colors by using silk screen printing inks of different colors. However, the particles of the ink are generally thick, and it is difficult to obtain a smooth and smooth printing surface. At the same time, due to the influence of the particles of the ink itself and the dust particles in the environment, it is easy to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine