Process of making glass goblets by machine blowing first and then machine pressing

A goblet and glass technology, applied in the field of making glass goblets by machine blowing and then machine pressing, can solve the problems of less shape change of cup holders, low production efficiency, and bulky products, and achieve significant economic benefits and improve production capacity, and the effect of improving product quality

Active Publication Date: 2017-11-14
CHONGQING JIANLI GLASS PROD CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Manually made glass goblets have low output, low authenticity rate, large amount of labor, low production efficiency, high cost, and little change in the shape of the cup stem and cup holder.
Although the machine-pressed glass goblet has high production efficiency and low cost, the product is relatively bulky, the cup body is large and the mouth is small, and the variety is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process of making glass goblets by machine blowing first and then machine pressing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A process of making glass goblets by machine blowing and then machine pressing. The glass goblet is composed of a cup body, a cup stem and a cup holder. Its production process is: glass raw material→furnace melting material→feeding machine for cup body material → Blowing machine blows the cup body → Manually transfer the cup body to the fire cutting start-up incision → Manually transfer the cup body to the mold of the compression molding machine → The feeding machine supplies the cup stem and cup holder material → The compression molding machine presses and forms the cup stem And the cup holder and connect the cup stem with the outer bottom of the cup body→manually transfer the cup to the fire polishing machine for polishing→manually transfer the polished cup to the annealing furnace for annealing→exit the annealing furnace→inspect→package. The mold of the compression molding machine has two open molds. When the left module 5 and the right module 3 are closed, the inside...

Embodiment 2

[0020] A process of making glass goblets by machine blowing and then machine pressing. The glass goblet is composed of a cup body, a cup stem and a cup holder. Its production process is: glass raw material→furnace melting material→feeding machine for cup body material → Blowing machine blows the cup body → Manually transfer the cup body to the fire cutting start-up incision → Manually transfer the cup body to the mold of the compression molding machine → The feeding machine supplies the cup stem and cup holder material → The compression molding machine presses and forms the cup stem And the cup holder and connect the cup stem with the outer bottom of the cup body→manually transfer the cup to the fire polishing machine for polishing→manually transfer the polished cup to the annealing furnace for annealing→exit the annealing furnace→inspect→package. The mold of the compression molding machine has two open molds. When the left module 5 and the right module 3 are closed, the inside...

Embodiment 3

[0022] A process of making glass goblets by machine blowing and then machine pressing. The glass goblet is composed of a cup body, a cup stem and a cup holder. Its production process is: glass raw material→furnace melting material→feeding machine for cup body material → Blowing machine blows the cup body → Manually transfer the cup body to the fire cutting start-up incision → Manually transfer the cup body to the mold of the compression molding machine → The feeding machine supplies the cup stem and cup holder material → The compression molding machine presses and forms the cup stem And the cup holder and connect the cup stem with the outer bottom of the cup body→manually transfer the cup to the fire polishing machine for polishing→manually transfer the polished cup to the annealing furnace for annealing→exit the annealing furnace→inspect→package. The mold of the compression molding machine has two open molds. When the left module 5 and the right module 3 are closed, the inside...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The process of making glass goblets by machine blowing and then machine pressing of the present invention relates to the preparation method of glass cups. Cup body→Manually turn the cup body into the fire-cut power cut→Manually turn the cup body into the mold of the compression molding machine→Feeder supplies the cup stem and cup holder→The compression molding machine presses the cup stem and cup holder and puts the cup The rod is connected with the outer bottom of the cup body→manually transfer the cup to the fire polishing machine for polishing→manually transfer the polished cup to the annealing furnace for annealing→out of the annealing furnace→inspection→package. The invention successfully realizes the combination of machine blowing and pressing to make glass goblets, which significantly improves product quality, greatly reduces production costs, and greatly reduces the amount of labor. variety, has significant economic and social benefits, and has promotional value.

Description

technical field [0001] The invention relates to a preparation method for making glass cups, and more particularly relates to a process for making glass goblets by machine blowing and then machine pressing. Background technique [0002] The glass goblet is composed of three parts: the cup body, the cup stem, and the cup holder. The glass goblet has many shapes. Different glass goblets should hold different wines or drinks. At present, there are two kinds of glass goblet production processes: manual production and machine pressing. The so-called manual production is to manually blow the cup body or machine blown cup body, and then manually connect the cup stem and cup holder, and then manually make the cup. The body can be of any size; the so-called machine pressing means that the cup body, cup stem, and cup holder are pressed into shape at one time. The artificially produced glass goblet has low output, low authenticity rate, large amount of labor, low production efficiency,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03B9/197
CPCY02P40/57
Inventor 唐建
Owner CHONGQING JIANLI GLASS PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com