Cauliflower seedling culture substrate

A technology for raising seedling substrate and cauliflower, applied in the field of raising seedlings, can solve the problem of not being able to satisfy the nutrients of cauliflower, and achieve the effect of rapid growth

Inactive Publication Date: 2015-12-09
南宁三达奥克化学有限责任公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a kind of cauliflower seedling-growing substrate, thereby overcome the shortcoming that the existing vegetable seedling-raising substrate cannot satisfy the cauliflower nutrient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The Chinese cabbage seedling raising substrate according to the specific embodiment of the present invention comprises the following components in parts by mass: 10 parts of slag, 10 parts of vermiculite, 4 parts of peat soil, 10 parts of plant ash, 10 parts of pig manure, and 5 parts of corn stalks , 5 parts of cassava straw, 5 parts of seaweed powder, 3 parts of nitrogen, phosphorus and potassium compound fertilizer, 3 parts of perlite and 3 parts of biogas residue.

[0016] The preparation method of above-mentioned Chinese cabbage seedling raising substrate comprises the following steps:

[0017] 1) crushing and mixing corn stalks, cassava stalks, vermiculite and perlite to obtain mixture I;

[0018] 2) After mixing the mixture I with slag, peat soil, plant ash, pig manure, seaweed powder, nitrogen, phosphorus and potassium compound fertilizer and biogas residue, heaping is carried out;

[0019] 3) adding microbial starter in the heap to ferment, the fermentation te...

Embodiment 2

[0023] The cabbage seedling raising substrate according to the specific embodiment of the present invention comprises the following components in parts by mass: 20 parts of slag, 20 parts of vermiculite, 7 parts of peat soil, 15 parts of plant ash, 20 parts of pig manure, and 10 parts of corn stalks , 8 parts of cassava straw, 10 parts of seaweed powder, 5 parts of nitrogen, phosphorus and potassium compound fertilizer, 5 parts of perlite and 5 parts of biogas residue.

[0024] The preparation method of above-mentioned Chinese cabbage seedling raising substrate comprises the following steps:

[0025] 1) crushing and mixing corn stalks, cassava stalks, vermiculite and perlite to obtain mixture I;

[0026] 2) After mixing the mixture I with slag, peat soil, plant ash, pig manure, seaweed powder, nitrogen, phosphorus and potassium compound fertilizer and biogas residue, heaping is carried out;

[0027] 3) adding microbial starter in the heap to ferment, the fermentation temperat...

Embodiment 3

[0031] The cabbage seedling raising substrate according to the specific embodiment of the present invention, in the above-mentioned technical scheme, comprises the following components by mass parts: 15 parts of slag, 15 parts of vermiculite, 6 parts of peat soil, 12 parts of plant ash, and 15 parts of pig manure , 8 parts of corn straw, 6 parts of cassava straw, 8 parts of seaweed powder, 4 parts of nitrogen, phosphorus and potassium compound fertilizer, 4 parts of perlite and 4 parts of biogas residue.

[0032] The preparation method of above-mentioned Chinese cabbage seedling raising substrate comprises the following steps:

[0033] 1) crushing and mixing corn stalks, cassava stalks, vermiculite and perlite to obtain mixture I;

[0034] 2) After mixing the mixture I with slag, peat soil, plant ash, pig manure, seaweed powder, nitrogen, phosphorus and potassium compound fertilizer and biogas residue, heaping is carried out;

[0035] 3) adding microbial starter in the heap t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a cauliflower seedling culture substrate which is characterized by comprising the following components in parts by mass: 10-20 parts of mushroom residues, 10-20 parts of vermiculite, 4-7 parts of peat soil, 10-15 parts of plant ash, 10-20 parts of pig manure, 5-10 parts of corn stalks, 5-8 parts of cassava stalks, 5-10 parts of an algae powder, 3-5 parts of a nitrogen-phosphorus-potassium compound fertilizer, 3-5 parts of perlite, and 3-5 parts of biogas residues. The cauliflower seedling culture substrate generally has no need of supplementing of nitrogen, phosphorus and potassium elements in a use process, and also has no need of supplementing of a large amount of trace elements in a whole seedling culture period, and flowering cabbage can obtain sufficient nutrients, so as to grow fast.

Description

technical field [0001] The invention relates to the field of seedling cultivation, in particular to a cauliflower seedling cultivation substrate. Background technique [0002] With the development of the vegetable industry, large-scale and commercial substrate seedling cultivation has gradually replaced the traditional soil seedling cultivation and has become the main method of seedling cultivation. At present, the substrate used for vegetable substrate seedling cultivation mainly uses straw as the main raw material. However, cauliflower is a vegetable Among the types that need more nutrients, the seedling substrates on the market need to add nutrient solution to the substrate when cauliflower seedlings are raised, which makes the cauliflower planting efficiency lower and slower growth. [0003] The information disclosed in this Background section is only for enhancing the understanding of the general background of the present invention and should not be taken as an acknowle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C05G3/00C05F17/00
CPCY02W30/40
Inventor 刘强
Owner 南宁三达奥克化学有限责任公司