Fireproof liquid of composite fireproof glass and preparation method thereof and composite fireproof glass

A technology of fire-resistant glass and fire-resistant liquid, which is applied in the direction of adhesive types, adhesive additives, ester copolymer adhesives, etc., which can solve the problem of low solid content, lower fire performance of composite fire-resistant glass, and affect the apparent quality of composite fire-resistant glass , optical properties, hardness and toughness, etc., to achieve good fire performance

Active Publication Date: 2015-12-09
CHINA BUILDING MATERIALS ACAD
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the prior art, the fireproof glue solidified by the fireproof liquid has many deficiencies in fireproof performance, such as water glass, which has a low modulus, low solid content, and high water content, which leads to a large number of fireproof glue in the composite fireproof glass. Microbubbles directl

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fireproof liquid of composite fireproof glass and preparation method thereof and composite fireproof glass
  • Fireproof liquid of composite fireproof glass and preparation method thereof and composite fireproof glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] First, accurately weigh 0.15kg of glycerin, 0.15kg of acrylic acid, 0.02kg of borax, 0.0005kg of sodium fluorosilicate, 0.02kg of sucrose and 0.08kg of deionized water, mix the above components, and stir thoroughly to obtain the first mixed emulsion. stand-by;

[0033] Accurately weigh 0.3kg of the above-mentioned first mixed emulsion and 0.2kg of hydrophilic nano-silica particles with a particle size of 60nm, and disperse the hydrophilic nano-silica particles in the first mixed emulsion through ultrasonic dispersion and high-speed stirring respectively , by standing for 5 hours to defoam and form a weight-stable nano-silica particle dispersion emulsion, stand-by;

[0034] Accurately weigh 0.1 kg of styrene, 0.15 kg of methyl methacrylate and 0.2 kg of butyl acrylate, mix the above components, and stir thoroughly to obtain a second mixed monomer emulsion for use;

[0035] Mix ammonium persulfate and sodium bisulfite at a molar ratio of 1:1, and use it as a redox initia...

Embodiment 2

[0041] First, accurately weigh 0.2kg of pentaerythritol, 0.2kg of methacrylic acid, 0.04kg of boric acid, 0.001kg of potassium fluorosilicate, 0.03kg of fructose and 0.12kg of deionized water, mix the above components, and stir thoroughly to obtain the first mixed lotion, ready to use;

[0042] Accurately weigh 0.32kg of the above-mentioned first mixed emulsion and 0.24kg of hydrophilic nano-silica particles with a particle size of 80nm, and disperse the hydrophilic nano-silica particles in the first mixed emulsion through ultrasonic dispersion and high-speed stirring respectively , by standing for 6 hours to defoam and form a dispersion emulsion of nano-silica particles with a stable weight, ready to use.

[0043] Accurately weigh 0.20 kg of styrene, 0.2 kg of methyl methacrylate and 0.3 kg of butyl acrylate, mix the above components, and stir thoroughly to obtain a second mixed monomer emulsion for use;

[0044] Mix ammonium persulfate and sodium bisulfite at a molar ratio ...

Embodiment 3

[0050] First, accurately weigh 0.23kg xylitol, 0.25kg polyacrylamide, 0.03kg borax, 0.03kg boric acid, 0.0015kg aluminum fluoride, 0.04kg glucose and 0.16kg deionized water, mix the above components, and stir thoroughly. Make the first mixed emulsion, stand-by;

[0051] Accurately measure 0.34kg of the above-mentioned first mixed emulsion and 0.28kg of hydrophilic nano-silica particles with a particle size of 100nm, and disperse the hydrophilic nano-silica particles in the first mixed emulsion through ultrasonic dispersion and high-speed stirring respectively , by standing for 7 hours to defoam and form a dispersion emulsion of nano-silica particles with a stable weight, ready for use.

[0052] Accurately weigh 0.20 kg of styrene, 0.25 kg of methyl methacrylate and 0.35 kg of butyl acrylate, mix the above components, and stir thoroughly to obtain a second mixed monomer emulsion for use;

[0053] Mix ammonium persulfate and sodium bisulfite at a molar ratio of 1:1 as a redox i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a fireproof liquid of composite fireproof glass and a preparation method thereof and a composite fireproof glass, relates to a field of safety glass, and solves the problems that a fireproof glue-line has micro bubbles and bad flame resistance. The main method of the invention is as follows: polyol, a functional monomer, deionized water and an auxiliary agent are mixed for obtaining a first mixed emulsion, silica is added, and a silica dispension emulsion is obtained; styrene, methyl methacrylate and butyl acrylate monomer are mixed, a second mixed monomer emulsion is obtained, a cross-linking agent, deionized water, the silica dispersion emulsion and an initiator are added, and a soap-free seeded emulsion is obtained after reaction; acrylic acid, styrene, methyl methacrylate and butyl acrylate monomer are mixed, a third mixed monomer emulsion is obtained, deionized water, the initiator, the cross-linking agent and the soap-free seeded emulsion are added, and a soap-free emulsion with core-shell structure is obtained after reaction; a potassium hydroxide solution and an auxiliary agent are added, after mixing, standing and refiltering, an obtained filtrate is the fireproof liquid of composite fireproof glass. The fireproof liquid provided by the invention can be solidified into a fireproof glue, which has good fireproof performance without micro bubbles.

Description

technical field [0001] The invention relates to the field of safety glass, in particular to a fireproof liquid for composite fireproof glass, a preparation method thereof and a composite fireproof glass prepared by using the fireproof liquid. Background technique [0002] Safety glass is an important new building material, mainly divided into tempered glass, laminated glass, bulletproof glass, anti-theft glass, fireproof glass, wired glass, protective glass and film glass; fireproof glass is a kind of building exterior with fireproof function Wall or door and window glass, which can keep for a long time without bursting under the impact of 1000 ℃ flame, so as to effectively prevent the spread of flame and smoke, help to find the fire at the first time, and ensure that the affected people have enough time to evacuate the scene. It is the most effective and safest fireproof glass product at present; fireproof glass is divided into composite fireproof glass and single piece fir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/08C09J133/12C09J11/04C08F220/14C08F220/18C08F220/06C08F212/08C03C27/12
Inventor 穆元春杜大艳徐志伟付静左岩张凡陈玮张洋安远张延芳于萍
Owner CHINA BUILDING MATERIALS ACAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap