Paint for vacuum coating of car lights

A vacuum and finishing technology, applied in the direction of polyester paint, coating, etc., can solve the problems of insufficient brightness of car lights, failure to meet special requirements, anti-yellowing of paint film, etc., achieve high one-time pass rate and improve clarity , the effect of cost reduction

Inactive Publication Date: 2015-12-30
江苏飞翔涂料有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] There are many kinds of light-curing coatings, most of which are used for exterior decoration of light industrial products, such as televisions, refrigerators, washing machines, electric vehicles and other products, but for interior decoration of automobile lamps, they cannot meet special requirements, such as coating combination Adhesion, there are paint peeling and moiré spots in hot light, causing the light source to be unable to focus, and the paint film itself turns yellow after long-term use, which brings serious problems such as insufficient brightness of car lights

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The paint of the car lamp vacuum finishing of the present embodiment, its component and weight percent are as follows: polyester acrylic resin 40%, TM acrylic monomer 15%, TP acrylic monomer 18%, novolak epoxy resin 10%, photoinitiator 11%, additive 1%, solvent 5%.

[0015] The solvent is formed by mixing propyl butyl ester and ethyl ester in a ratio of 1:2.4.

[0016] The photoinitiator is an ultraviolet absorber.

[0017] The auxiliary agent includes one or more of drier, toughener, defoamer, leveling agent, light stabilizer, accelerator, dispersant and the like.

[0018] The preparation method of the coating for the vacuum coating of the above-mentioned car lights comprises the following steps:

[0019] (1) Take propyl butyl ester and ethyl ester and mix and stir according to the ratio of 1:2.4 to form solvent a;

[0020] (2) First mix polyester acrylic resin with solvent a to form resin mixture b;

[0021] (3) Add M acrylic acid monomer, TP acrylic monomer and n...

Embodiment 2

[0023] The paint of the car lamp vacuum coating of the present embodiment, its component and percentage by weight are as follows: polyester acrylic resin 45%, TM acrylic monomer 10%, TP acrylic monomer 20%, novolak epoxy resin 6%, photoinitiator 8%, additive 1%, solvent 10%.

[0024] The solvent is formed by mixing propyl butyl ester and ethyl ester in a ratio of 1:2.4.

[0025] The photoinitiator is an ultraviolet absorber.

[0026] The auxiliary agent includes one or more of drier, toughener, defoamer, leveling agent, light stabilizer, accelerator, dispersant and the like.

[0027] The preparation method of the coating for the vacuum coating of the above-mentioned car lights comprises the following steps:

[0028] (1) Take propyl butyl ester and ethyl ester and mix and stir according to the ratio of 1:2.4 to form solvent a;

[0029] (2) First mix polyester acrylic resin with solvent a to form resin mixture b;

[0030] (3) Add M acrylic acid monomer, TP acrylic monomer an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to paint for vacuum coating of car lights. The paint comprises the following ingredients in percentage by weight: 40-50% of polyester acrylic resin, 10-15% of a TM acrylic monomer, 18-25% of a TP acrylic monomer, 5-10% of phenolic aldehyde epoxy resin, 6-11% of a photoinitiator, 0.5-1.5% of one or additives, 5-10% of ethyl ester and the balance of a solvent, wherein the solvent is a mixture of butyl propionate and ethyl ester; the ratio of butyl propionate to ethyl ester is 1:2.4; the photoinitiator is an ultraviolet light absorbent; the additives comprise one or more of a drying agent, a toughening agent, an antifoaming agent, a leveling agent, a photostabilizer, an accelerating agent, a dispersing agent and the like. Compared with like vacuum paint, the paint provided by the invention has the advantages that the cost is reduced by about 40%, convenience is brought for construction, and the one-time qualification rate is high.

Description

technical field [0001] The invention relates to a light-curing coating mainly composed of acrylic resin, polyester resin and phenolic epoxy resin, which is especially suitable for vacuum spraying in various automobile lamps. Background technique [0002] There are many kinds of light-curing coatings, most of which are used for exterior decoration of light industrial products, such as televisions, refrigerators, washing machines, electric vehicles and other products, but for interior decoration of automobile lamps, they cannot meet special requirements, such as coating combination Adhesion, there are paint peeling and moiré spots in hot light, causing the light source to be unable to focus, and the paint film itself turns yellow after long-term use, which brings serious problems such as insufficient brightness of the car lights. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a paint for car lamp vacuum finishing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/06C09D163/04C09D7/12
Inventor 庄建平
Owner 江苏飞翔涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap