Lithium ion battery and preparing method thereof

A lithium-ion battery and battery case technology, which is applied in the field of lithium-ion batteries, can solve the problems of the performance degradation of lithium-ion batteries, the inability to guarantee the SEI film of lithium-ion batteries, etc., so as to facilitate mass production, reduce irreversible capacity loss, and avoid performance. the effect of falling

Active Publication Date: 2015-12-30
CHINA AVIATION LITHIUM BATTERY LUOYANG
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, adding the above-mentioned film-forming additives in the electrolyte is greatly affected by the solubility of the film-forming additives in the electrolyte solvent. After the electrolyte solvent type changes, the amount of the film-forming additives that can be dissolved in the electrolyte is affected. There is no guarantee that there is sufficient SEI film on the surface of the negative electrode of the lithium-ion battery, especially during the charging and discharging process of the battery, with the consumption of the SEI film, the performance of the lithium-ion battery will decline again

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium ion battery and preparing method thereof
  • Lithium ion battery and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The lithium-ion battery of this embodiment is a soft-packed ternary material lithium-ion battery, comprising a sealed battery case and an electric core contained in the battery case, the electric core such as figure 1 As shown in middle A, the battery casing of this embodiment is an aluminum-plastic film soft bag, and the aluminum-plastic film soft bag is filled with a mixed gas of film-forming gas and argon, and the film-forming gas is CO 2 Gas, film-forming gas CO in mixed gas 2 The volume percent concentration is 1%, and the pressure of the mixed gas in the aluminum-plastic film soft bag is 120kPa.

[0024] The preparation method of the lithium ion battery of the present embodiment comprises the steps:

[0025] 1) Put the ternary material soft-packed lithium-ion battery after one-time formation in a vacuum static box, and pump air into the aluminum-plastic film soft bag of the soft-packed lithium-ion battery. The pumping time is 5 minutes, and the pumping is complet...

Embodiment 2

[0028] The lithium-ion battery of this embodiment is a soft-packed ternary material lithium-ion battery, including a sealed battery case and an electric cell housed in the battery case. The battery case of this embodiment is an aluminum-plastic film soft case, and an aluminum-plastic film The soft bag is filled with a mixed gas of film-forming gas and argon, and the film-forming gas is SO 2 Gas, film-forming gas SO in mixed gas 2 The volume percent concentration is 0.5%, and the pressure of the mixed gas in the aluminum-plastic film soft bag is 105kPa.

[0029] The preparation method of the lithium ion battery of the present embodiment comprises the steps:

[0030] 1) Place the ternary material soft-packed lithium-ion battery after one-time formation in a vacuum static box, and pump air into the aluminum-plastic film soft bag of the soft-packed lithium-ion battery. The pumping time is 1 minute, and the pumping is completed. Afterwards, the vacuum degree in the aluminum-plast...

Embodiment 3

[0033] The lithium-ion battery of this embodiment is a soft-packed ternary material lithium-ion battery, including a sealed battery case and an electric cell housed in the battery case. The battery case of this embodiment is an aluminum-plastic film soft case, and an aluminum-plastic film The soft bag is filled with a mixed gas of film-forming gas and argon, and the film-forming gas is N 2 O gas, film-forming gas N in the mixed gas 2The volume percent concentration of O is 2%, and the pressure of the mixed gas in the aluminum-plastic film soft bag is 150kPa.

[0034] The preparation method of the lithium ion battery of the present embodiment comprises the steps:

[0035] 1) Place the ternary material soft-packed lithium-ion battery after one-time formation in a vacuum static box, and pump air into the aluminum-plastic film soft bag of the soft-packed lithium-ion battery. The pumping time is 10 minutes, and the pumping is completed Afterwards, the vacuum degree in the aluminu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
percent by volumeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a lithium ion battery and a preparing method thereof, and belongs to the technical field of lithium ion batteries. The lithium ion battery comprises a sealed battery shell, the battery shell is filled with film forming gas, and the film forming gas is CO2 or SO2 or NO2. As the lithium ion battery is internally filled with the film forming gas, the first-time discharge efficiency and the cycle performance of the battery are obviously improved, the first-time charge and discharge efficiency is 89.70% or more, and the capacity retention ratio after 500 cycles at the temperature of 60 DEG C is 94.7% or more. The safety performance of the lithium ion battery is substantially improved.

Description

technical field [0001] The invention relates to a lithium ion battery and a preparation method thereof, belonging to the technical field of lithium ion batteries. Background technique [0002] During the charging and discharging process of the lithium-ion battery, the electrode material and the electrolyte react on the solid-liquid phase interface, the electrolyte is reduced and decomposed, and a passivation film is formed on the surface of the negative electrode material, which is usually called the solid electrolyte interface (solid electrolyte interface). ) film, that is, the SEI film, the thickness of the SEI film is about 100-120nm, and the film mainly contains Li 2 CO 3 , LiF, Li 2 O, LiOH and other inorganic components and ROCO 2 Li, ROLi, (ROCO 2 Li) 2 and other organic ingredients. The charging and discharging process of lithium-ion batteries includes the insertion or extraction of lithium ions in the negative electrode material, and the insertion or extractio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/0525H01M10/0567H01M10/058
CPCH01M10/0525H01M10/0567H01M10/058Y02E60/10Y02P70/50
Inventor 赵晓锋张方方
Owner CHINA AVIATION LITHIUM BATTERY LUOYANG
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com