Polymer nano wheel aligner and preparation method thereof

A polymer and locator technology, applied in the direction of coating, etc., can solve the problems of easy aging service life, general buffer capacity, easy excessive deformation, etc., and achieve the effect of high mixing uniformity, long service life, high strength and toughness

Active Publication Date: 2018-07-31
陈鹤忠
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, although the rubber positioner has a certain toughness, it is too soft, and it is easy to be deformed excessively and cannot be recovered. At the same time, it has the disadvantages of easy wear, weak toughness, general buffering capacity, and short service life due to aging.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer nano wheel aligner and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The preparation method of the polymer nano wheel aligner of this embodiment is as follows: weigh 65kg polypropylene and 20kg ABS resin, grind them and mix them uniformly to obtain the main ingredients. Weigh 8kg carbon fiber, 3kg polyvinyl butyral, 1kg weight portion of antioxidant, 1kg antiaging agent, 3kg flame retardant, 0.5kg ultraviolet absorber, 0.5kg light stabilizer and 0.5kg plastic antistatic agent and mix After homogenization, the auxiliary materials are obtained. The main material and the auxiliary material are respectively melted and kneaded to obtain a molten compound. Inject the melted mixture into the molding mold, pressurize the molding mold until the pressure in the mold reaches 20Mpa, turn on the cooling system to cool the molding mold, and keep the pressure at 20Mpa for 20min, cool down and remove the mold.

Embodiment 2

[0033] The antioxidant 1010, ultraviolet absorber uv-623 and light stabilizer 770 of this embodiment were all purchased from Nanjing Hualiming Chemical Co., Ltd., and the anti-aging agent MBP was purchased from Qingdao Huaen Chemical Co., Ltd. as a plastic anti-aging agent. Melamine pyrophosphate was purchased from Shenzhen Hongtaiji Industrial Co., Ltd.

[0034]The preparation method of the polymer nano wheel aligner of this embodiment is as follows: Weigh 70kg of waste polypropylene and 25kg of waste ABS resin and pulverize them into 2mm×2mm×2mm particles respectively, then add the main material to a high-speed mixer, start the main material The high-speed mixer adjusts the rotation speed to 700r / min, rotates for 15min, then adjusts the rotation speed to 400r / min, continues to rotate for 5min, and cools to obtain the main ingredient. Weigh 9kg carbon fiber, 4kg polyvinyl butyral, 1.5kg antioxidant, 1.5kg antiaging agent, 3.5kg flame retardant, 0.8kg ultraviolet absorber, 0.8...

Embodiment 3

[0036] The preparation method of the polymer nano wheel aligner of this embodiment is as follows: Weigh 75kg of polypropylene and 30kg of ABS resin and pulverize them into 2mm×2mm×2mm particles respectively, then add the main material to the high-speed mixer, and start the main material to the high-speed mixer Adjust the rotation speed to 800r / min, rotate for 10min, then adjust the rotation speed to 500r / min, continue to rotate for 4min, and cool to obtain the main ingredient. Weigh 10kg of carbon fiber, 5kg of polyvinyl butyral, 2kg of antioxidant, 2kg of antiaging agent, 4kg of flame retardant, 1kg of ultraviolet absorber, 1kg of light stabilizer and 1kg of plastic antistatic agent and add auxiliary materials to a high-speed mixer, Start the auxiliary material with a high-speed mixer to adjust the rotating speed to 800r / min, rotate for 10min, then adjust the rotating speed to 500r / min, continue to rotate for 4min, and cool to obtain the auxiliary material. The main material ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of auxiliary parking equipment for parking lots and particularly provides a macromolecular nano wheel positioner. The macromolecular nano wheel positioner is mainly prepared from, by weight, 65-75 parts of polypropylene, 20-30 parts of ABS resin, 8-10 parts of carbon fiber, 3-5 parts of polyvinyl butyral and the like. In addition, the invention further provides a preparation method of the macromolecular nano wheel positioner. The macromolecular nano wheel positioner has the advantages that the macromolecular nano wheel positioner is low in manufacturing cost, good in toughness and long in service life, is resistant to abrasion and can be detachably arranged on the peripheral side of each parking place. Furthermore, the preparation method is high in mixing uniformity and high in production stabilization efficiency and comprises simple production steps, and the macromolecular nano wheel positioner having denser texture and higher strength and toughness can be obtained and is suitable for industrial popularization and application.

Description

technical field [0001] The invention belongs to the field of auxiliary parking equipment in parking lots, and in particular relates to a polymer nanometer wheel positioner and a preparation method thereof. Background technique [0002] Wheel aligner is a kind of equipment that assists in determining the correct parking of vehicles. Mainly used in parking lots and garages, it can be used to park vehicles accurately and neatly, reduce vibration and avoid collisions, so as to avoid collisions between vehicles or between vehicles and walls when vehicles are parked and started, or reduce the distance between vehicles. , The damage caused by the collision between the vehicle and the wall. [0003] Traditional wheel locators are mainly divided into cement locators and rubber locators. The cement locator is made of cement, and the masonry is fixed on the side of the parking space. Its disadvantages are high production cost, lack of toughness and inability to play a buffering role...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08L55/02C08L29/14C08K13/04C08K7/06C08K5/3492C08K5/134B29C45/00B29C45/57B29B7/02B29C47/10
CPCB29B7/02B29C45/0001B29C45/57B29C48/288C08L23/12C08L2205/03C08L55/02C08L29/14C08K13/04C08K7/06C08K5/34922C08K5/1345
Inventor 陈鹤忠
Owner 陈鹤忠