A kind of organosilicon dipping paint and its preparation method and application

A technology of organosilicon impregnation and organosilicon, which is applied in the direction of coating, etc., can solve the problem of low mechanical strength of cured products, and achieve the effect of good application process performance and good comprehensive performance

Active Publication Date: 2017-12-12
ZHUZHOU TIMES ELECTRIC INSULATION
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Organosilicon material is a general-purpose insulating material at present, widely used in impregnating varnishes, coatings, mica tape adhesives and other fields, but organosilicon materials have their own defects, and the problem of low mechanical strength of the cured products has been criticized

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of organosilicon dipping paint and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Take 1 mol of 1-phenyltrichlorosilane, 0.1 mol of dimethyldichlorosilane, 0.5 mol of methylvinyldichlorosilane, 0.2 mol of diphenyldichlorosilane, and 0.2 mol of hexamethyldisiloxane at 10°C Add the organosilicon monomer dropwise to the flask with rapid stirring at a speed of 5L / min under certain conditions, and the dropwise hydrolysis reaction lasts for 4 hours, then reflux concentration and aging reaction at 120°C for 4 hours, and then wash with water until neutral , vacuumize the upper paint layer to remove solvent and low boiling matter, and take samples to measure the viscosity. When the viscosity reaches the target range, stop heating, cool to below 60°C and discharge to obtain component A. After NDJ-79 rotational viscosity Meter (Wuhan Glamo Testing Equipment Co., Ltd.) measures the viscosity of component A as 8120CP / 60°C.

[0037]Take 0.5mol of phenyltrichlorosilane, 0.1mol of dimethyldichlorosilane, 0.4mol of methylhydrogendichlorosilane, 0.1mol of methylphenyl...

Embodiment 2

[0040] Take 0.2mol of monophenyltrichlorosilane, 0.1mol of dimethyldichlorosilane, 0.4mol of methylvinyldichlorosilane, 0.2mol of diphenyldiethoxysilane, and 0.3mol of hexamethyldisiloxane, Add the organosilicon monomer dropwise to the flask with rapid stirring at a rate of 6L / min at 10°C, and the dropwise hydrolysis reaction lasts for 4 hours, then reflux concentration and aging reaction at 120°C for 4 hours, and then wash with water To neutral, vacuumize the upper paint layer to remove solvent and low boiling matter, and take a sample to measure the viscosity. When the viscosity reaches the target range, stop heating, cool to below 60°C and discharge to obtain component A. After NDJ- 79 rotational viscometer measures the viscosity of component A as 35CP / 23℃.

[0041] Take 1.2mol of monophenyltrichlorosilane, 0.1mol of dimethyldichlorosilane, 0.4mol of methylhydrogendichlorosilane, 0.1mol of methylphenyldiethoxysilane, and 0.1mol of hexamethyldisiloxane, Add the organosilico...

Embodiment 3

[0044] Take 1.2mol of phenyltrichlorosilane, 0.1mol of dimethyldichlorosilane, 0.5mol of methylvinyldichlorosilane, 0.2mol of methylphenyldichlorosilane, and 0.2mol of hexamethyldisiloxane in Add the organosilicon monomer dropwise to the flask with rapid stirring at a rate of 8L / min at 20°C, and the hydrolysis reaction lasts for 4 hours, then reflux concentration and aging reaction at 120°C for 4 hours, and then wash with water until Neutral, vacuumize the upper paint layer to remove solvent and low boiling matter, and take a sample to measure the viscosity. When the viscosity reaches the target range, stop heating, cool to below 60°C and discharge to obtain component A. After NDJ-79 Rotational viscometer measures the viscosity of component A as 9050CP / 60°C.

[0045] Take 0.3mol of phenyltrichlorosilane, 0.2mol of dimethyldichlorosilane, 0.5mol of methylhydrogendichlorosilane, 0.2mol of methylphenyldichlorosilane, and 0.3mol of hexamethyldisiloxane at 15 Add the organosilicon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of paint chemical industry, in particular to an organosilicon impregnating paint and its preparation method and application. The tensile strength of the cured product of the organosilicon impregnating varnish is above 15MPa, preferably in the range of 15-20MPa, and the bending strength of the cured product of the organosilicon impregnating varnish is above 25MPa, preferably in the range of 25-35MPa. The mechanical strength of the organosilicon impregnating paint of the invention has been greatly improved.

Description

technical field [0001] The invention relates to the field of paint chemical industry, in particular to an organosilicon impregnating paint and its preparation method and application. Background technique [0002] Silicone material is currently a general-purpose insulating material variety, widely used in impregnating varnishes, coatings, mica tape adhesives, etc., but silicone materials have their own defects, and the problem of low mechanical strength of the cured product has been criticized. [0003] Silicone hydrosilicon addition silicone paint products are a large class of products in the silicone system, which obtain the final cured product through the addition reaction between silicon vinyl and silicon hydrogen, usually made of silicon vinyl Components and silicon hydrogen components, in order to obtain a suitable paint viscosity, for example, to obtain a paint viscosity of 1000CP, generally use the silicone vinyl component and silicon hydrogen component to achieve a v...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/07C09D183/05C09D5/25C08G77/20C08G77/12
Inventor 衷敬和陈磊陈晓周光红姜其斌
Owner ZHUZHOU TIMES ELECTRIC INSULATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap