A ceramic brick prepared from waste materials and its preparation method

A technology of ceramic tiles and waste materials, applied in the field of ceramic tiles prepared from waste materials and its preparation, can solve problems such as environmental pollution and waste of resources, achieve excellent physical and chemical properties, reduce waste of raw materials, and save production costs

Active Publication Date: 2017-12-29
OTTIMA CERAMIC
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Therefore, the technical problem to be solved by the present invention is that in the existing ceramic production, a large amount of ceramic waste is produced, and direct burial wastes resources and pollutes the environment, thereby proposing a kind of ceramics prepared from waste materials that reduces resource waste and is conducive to sustainable development. Bricks and methods of making them

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A ceramic brick prepared from waste materials and its preparation method
  • A ceramic brick prepared from waste materials and its preparation method
  • A ceramic brick prepared from waste materials and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] This embodiment provides a kind of ceramic brick prepared from waste materials, which is composed of the following components in terms of mass percentage: 30% of china clay, 18% of stone powder, 18% of sodium sand, 6% of potassium sand, 15% of high alumina sand, and talc mud 3%, recycled mud 10%. Wherein, the recycled mud is obtained by pulverizing and mixing brick adobe, edging waste residue, sewage treatment tank press cake and sewage sludge, specifically: in the recycled mud, the mass percentage of the brick adobe is 40%, and the The mass percentage of edging waste is 20%, the mass percentage of the press filter cake of the sewage treatment tank is 30%, the mass percentage of the sewage sludge is 10%, and the brick adobe is a green body that has not been fired in a kiln. .

[0029] Present embodiment also provides a kind of method for preparing described ceramic tile, it comprises the steps:

[0030] S1. Mixing the recycled mud with the china clay, stone powder, so...

Embodiment 2

[0040] This embodiment provides a ceramic tile prepared from waste materials, which is composed of the following components in terms of mass percentage: 28% of china clay, 20% of stone powder, 14% of sodium sand, 10% of potassium sand, 10% of high alumina sand, and talc mud 3%, recycled mud 15%. Wherein, the recycled mud is obtained by pulverizing and mixing brick adobe, edging waste residue, sewage treatment tank press cake and sewage sludge, specifically: in the recycled mud, the mass percentage of the brick adobe is 25%, and the The mass percentage of edging waste is 30%, the mass percentage of the press filter cake of the sewage treatment tank is 30%, the mass percentage of the ditch sludge is 15%, and the brick adobe is a green body that has not been fired in a kiln. .

[0041] Present embodiment also provides a kind of method for preparing described ceramic tile, it comprises the steps:

[0042] S1. Mixing the recycled mud with the china clay, stone powder, sodium sand...

Embodiment 3

[0052] This embodiment provides a ceramic tile prepared from waste materials, which is composed of the following components in terms of mass percentage: 35% of china clay, 15% of stone powder, 14% of sodium sand, 5% of potassium sand, 20% of high alumina sand, and talc mud 2%, recycled mud 9%. Wherein, the recycled mud is obtained by pulverizing and mixing brick adobe, edging waste residue, sewage treatment tank press cake and sewage sludge, specifically: in the recycled mud, the mass percentage of the brick adobe is 40%, and the The mass percentage of edging waste is 20%, the mass percentage of the press filter cake of the sewage treatment tank is 30%, the mass percentage of the sewage sludge is 10%, and the brick adobe is a green body that has not been fired in a kiln. .

[0053] Present embodiment also provides a kind of method for preparing described ceramic tile, it comprises the steps:

[0054] S1. Mixing the recycled mud with the china clay, stone powder, sodium sand,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramic tile manufactured by waste. The ceramic tile is prepared from, by mass, 25-30% of porcelain clay, 15-20% of mountain flour, 14-22% of sodium sand, 5-10% of potassium sand, 10-20% of high alumina sand, 2-3% of talc mud and 5-15% of recycling mud. The recycling mud is formed by smashing and mixing green bricks, edging waste residues, filter cakes of sewage treatment tanks and ditch sludge. The invention further provides a manufacturing method of the ceramic brick. The problem that waste of a ceramic plant is hard to dispose is solved, raw material waste is reduced, the production cost is saved, and the physical and chemical properties of the produced ceramic brick are excellent.

Description

technical field [0001] The invention belongs to the technical field of ceramic production, and relates to a ceramic and a preparation method thereof, in particular to a ceramic brick prepared from waste materials and a preparation method thereof. Background technique [0002] Ceramics are made of natural clay and various natural minerals as the main raw materials, and various products made of various materials after crushing, kneading, molding and calcination. The production of ceramics can be traced back to 4500 BC to 2500 BC. , with the development of modern science and technology, many new ceramic varieties have appeared in the past hundred years. In the course of the rapid development of ceramics, some problems have gradually arisen, that is, the increasing waste of the ceramic industry has not only caused huge pressure on the environment, but also It limits the development of urban economy and the sustainable development of ceramic industry. [0003] Ceramic waste main...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/132
CPCY02P40/60
Inventor 孙宇群
Owner OTTIMA CERAMIC