A bisphosphine heterocyclic organic electroluminescent compound containing spirofluorene structure, its synthesis method and its application

A spirofluorene structure and compound technology, applied in the field of organic electroluminescent materials, to achieve the effect of simple route, prolonging life, and improving electron injection and transport capabilities

Active Publication Date: 2017-04-05
HENAN ACADEMY OF SCI CHEM RES INST CO LTD +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, there have been no relevant research reports on this type of compound

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A bisphosphine heterocyclic organic electroluminescent compound containing spirofluorene structure, its synthesis method and its application
  • A bisphosphine heterocyclic organic electroluminescent compound containing spirofluorene structure, its synthesis method and its application
  • A bisphosphine heterocyclic organic electroluminescent compound containing spirofluorene structure, its synthesis method and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The synthesis of embodiment 1 compound Ia

[0029]

[0030] Synthesis of compound Ⅳ

[0031] Under argon protection, 9-anthraceneboronic acid (2.2g), 2,5-dibromoiodobenzene (3.6g), tetrahydrofuran (30mL), water (30mL), tetrakis(triphenylphosphine) were added successively to the flask Palladium (100mg), potassium carbonate (2.7g), heated under reflux for 10h. Stop the reaction, extract three times with ethyl acetate, combine the organic phases, and then wash to neutrality; separate the organic phases, add anhydrous magnesium sulfate to dry, suction filter, and spin dry; silica gel column chromatography gives 3.6 g of white solids, the yield 88%.

[0032] Synthesis of compound V

[0033] Under argon protection, compound IV (3.0 g) and tetrahydrofuran (50 mL) were added to the flask, then the system was cooled to -78 ° C, and a 2.5 M n-hexane solution containing n-butyllithium (6 mL) was added dropwise to the system. ), react at -78°C for 1 hour after the dropwise a...

Embodiment 2

[0042] The synthesis of embodiment 2 compound 1b

[0043]

[0044] Synthesis of compound Ⅵb

[0045] Compound V (3.0 g) obtained according to the synthesis method of Example 1, toluene (20 mL), and 10% palladium carbon (100 mg) were added to the flask, and the reaction was heated under reflux for 10 hours. After returning to room temperature, excess sulfur powder was added to the system, reacted for 5 hours, and spin-dried; silica gel column chromatography yielded 2.0 g of a light yellow solid, with a yield of 78%.

[0046] Synthesis of Compound Ⅶb

[0047] Add compound VIb (2.0 g), glacial acetic acid (20 mL), and liquid bromine (2 g) into the flask, and heat to reflux for 5 hours. Stop the reaction, add saturated sodium thiosulfate solution (20 mL), extract three times with ethyl acetate, combine the organic phases, remove the solvent, add ethyl acetate (10 mL) again to dissolve, dry over anhydrous magnesium sulfate, filter with suction, and spin dry; Silica gel column c...

Embodiment 3

[0052] The synthesis of embodiment 3 compound Ic

[0053]

[0054] Synthesis of Compound Ⅵc

[0055] Compound V (3.0 g) obtained according to the synthesis method of Example 1, toluene (20 mL), and 10% palladium carbon (100 mg) were added to the flask, and the reaction was heated under reflux for 10 hours. After returning to room temperature, excess selenium powder was added to the system, reacted for 5 hours, and spin-dried; silica gel column chromatography yielded 2.3 g of a light yellow solid, with a yield of 76%.

[0056] Synthesis of Compound Ⅶc

[0057] Add compound VIc (2.0 g), glacial acetic acid (20 mL), and liquid bromine (2 g) into the flask, and heat to reflux for 7 hours. Stop the reaction, add saturated sodium thiosulfate solution (20 mL), extract three times with ethyl acetate, combine the organic phases, remove the solvent, add ethyl acetate (10 mL) again to dissolve, dry over anhydrous magnesium sulfate, filter with suction, and spin dry; Silica gel colu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bisphosphine heterocyclic organic electroluminescent compound containing a spirofluorene structure, a synthesis method and an application thereof, belonging to the field of organic electroluminescent materials. This type of compound has the general structural formula shown in formula I, wherein X is O, S or Se, and R is or. The organic electroluminescent compound of the present invention can be applied to the light-emitting layer of an organic electroluminescent device, and the luminescent performance of the corresponding device can be regulated by simple chemical modification of the phosphine atom; this type of compound has good thermal stability, and the existence of the spirofluorene structure effectively reduces the The stacking effect between molecules can significantly improve the efficiency and lifetime of the corresponding organic electroluminescent devices.

Description

technical field [0001] The invention relates to the field of organic electroluminescent materials, in particular to a phosphine-containing organic electroluminescent compound, in particular to a bisphosphine heterocyclic organic electroluminescent compound containing a spirofluorene structure, a synthesis method and an application thereof. Background technique [0002] As a new type of display technology, organic electroluminescent devices have self-illumination, wide viewing angles, low energy consumption, high efficiency, thinness, rich colors, fast response speed, wide applicable temperature range, low driving voltage, flexible, bendable and The unique advantages of transparent display panels and environmental friendliness can be applied to flat panel displays and new generation lighting, and can also be used as LCD backlight. Since their invention in the late 1980s, organic electroluminescent devices have found industrial applications, such as screens for cameras and mob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07F9/6568C09K11/06H01L51/54
CPCC09K11/06C07F9/65685C09K2211/1007C09K2211/1096H10K85/657
Inventor 陈辉杨瑞娜杨振强段征张银龙孙敏青
Owner HENAN ACADEMY OF SCI CHEM RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com