Efficient ultraviolet-proof automotive window film

A technology of anti-ultraviolet and car film, applied in the field of auto parts, can solve the problems of no anti-ultraviolet and low bonding performance, and achieve the effect of blocking ultraviolet rays and not being easy to age

Inactive Publication Date: 2016-03-16
QINGDAO WENSHENG AUTOMOBILE COMPONENTS & PARTS
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the ordinary film on the market has low adhesion performance, can only play the role of sunshade, and does not have the function of anti-ultraviolet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] A high-efficiency anti-ultraviolet car film, which is composed of the following raw materials in parts by weight: 3 parts of high-density polyethylene, 5 parts of rosin resin, 3 parts of ethyl cellulose, 3 parts of nano-silica, 4 parts of titanium dioxide, and 0.5 parts of nano-silver , 5 parts of aluminum oxide, 2 parts of barium-zinc composite stabilizer, 0.3 part of sodium lauryl sulfate, 0.05 part of antioxidant, 2 parts of plasticizer, 1 part of coupling agent, 1 part of barium carbonate, 2 parts of sodium molybdate share.

Embodiment 2

[0010] A high-efficiency anti-ultraviolet car film, which is composed of the following raw materials in parts by weight: 4 parts of high-density polyethylene, 6 parts of rosin resin, 4 parts of ethyl cellulose, 4 parts of nano-silica, 5 parts of titanium dioxide, and 0.7 parts of nano-silver , 7 parts of aluminum oxide, 5 parts of barium-zinc composite stabilizer, 0.4 part of sodium lauryl sulfate, 0.07 part of antioxidant, 3 parts of plasticizer, 5 parts of coupling agent, 3 parts of barium carbonate, 3 parts of sodium molybdate share.

Embodiment 3

[0012] A high-efficiency anti-ultraviolet car film, which is composed of the following raw materials in parts by weight: 5 parts of high-density polyethylene, 7 parts of rosin resin, 5 parts of ethyl cellulose, 5 parts of nano-silica, 9 parts of titanium dioxide, and 1 part of nano-silver 10 parts of aluminum oxide, 6 parts of barium zinc composite stabilizer, 0.6 part of sodium lauryl sulfate, 0.1 part of antioxidant, 5 parts of plasticizer, 7 parts of coupling agent, 5 parts of barium carbonate, 5 parts of sodium molybdate share.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Efficient ultraviolet-proof automotive window film is disclosed. The automotive window film is prepared from following raw materials by weight: 3-5 parts of high-density polyethylene, 5-7 parts of rosin resin, 3-5 parts of ethyl cellulose, 3-5 parts of nanometer silica, 4-9 parts of titanium dioxide, 0.5-1 part of nano-silver, 5-10 parts of aluminum oxide, 2-6 parts of a barium-zinc composite stabilizing agent, 0.3-0.6 part of sodium dodecyl sulfate, 0.05-0.1 part of an antioxidant, 2-5 parts of a plasticizer, 1-7 parts of a coupling agent, 1-5 parts of barium carbonate and 2-5 parts of sodium molybdate. The automotive window film is high-temperature resisting, not liable to age and capable of effectively resisting ultraviolet.

Description

technical field [0001] The invention belongs to the field of auto parts, and in particular relates to a high-efficiency anti-ultraviolet auto film. Background technique [0002] Car film is a film that is attached to the car glass for aesthetics, safety, and heat insulation. Its main function is to block ultraviolet rays, block part of the heat, and prevent injuries caused by sudden glass bursts. Perspective performance, to achieve the purpose of protecting personal privacy. At present, the ordinary film on the market has low bonding performance, can only play the role of sunshade, and does not have the function of preventing ultraviolet rays. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the invention provides an efficient anti-ultraviolet car film. [0004] The technical solution of the present invention is: a high-efficiency anti-ultraviolet car film, which is composed of the following raw materials in parts by weight: 3-5 parts of hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L93/04C08L23/06C08L1/28C08K13/02C08K3/36C08K3/22C08K3/08C08K5/41C08K3/26C08K3/24
CPCC08L93/04C08L2201/08C08L2203/16C08L2205/03C08L2207/062
Inventor 吕玲霞
Owner QINGDAO WENSHENG AUTOMOBILE COMPONENTS & PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products