Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Transparent heat insulation coating with nanoparticles and preparation method thereof

A heat-insulating coating and nano-particle technology, applied in the direction of coating, etc., can solve the problems of unsatisfied coating light transmission performance, opaque hollow microspheres, and difficulty in popularization, and achieve environmental protection, energy saving, economic and social benefits, The effect of lowering the temperature and extending the life of the film layer

Inactive Publication Date: 2010-01-20
黎源
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this material is expensive and difficult to be popularized
In addition, some coatings added with hollow microspheres and nanoparticles, although their thermal conductivity is small, have good reflectivity for ultraviolet and near-infrared rays, and have good heat insulation, but due to the opacity of the hollow microspheres themselves, The light transmission performance of the coating cannot be satisfied

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Add 5 parts of aluminum oxide, cerium oxide, iron oxide, ATO nanoscale powder slurry and 20 parts of deionized water to 72 parts of water-based acrylic emulsion, adjust the pH value to 8.0 with ethanolamine solution; The water-based acrylic emulsion was mechanically stirred for 60 minutes, and 3 parts of defoamer, dispersant, and leveling agent were added at the same time; then stirred with a high-speed mixer for 20 minutes, and finally ultrasonically oscillated for 30 minutes to obtain a transparent heat-insulating coating containing nanoparticles.

[0019] The above-mentioned transparent heat-insulating paint containing nanoparticles is brushed on the transparent glass, the visible light transmittance is greater than 80%, and the temperature difference between the inside and outside of the test system in the heat insulation test is 3-5 degrees Celsius.

Embodiment 2

[0021] Add 20 parts of alumina, silicon oxide, ATO nanoscale powder slurry and 30 parts of deionized water to 45 parts of aqueous acrylic emulsion, and adjust the pH value to 9.0 with ammonia solution; the aqueous acrylic emulsion containing nano oxide Stir mechanically for 50 minutes, and add 5 parts of defoamer, dispersant, and leveling agent at the same time; then stir with a high-speed mixer for 30 minutes, and finally oscillate ultrasonically for 50 minutes to obtain a transparent heat-insulating coating containing nanoparticles.

[0022] The above-mentioned transparent heat-insulating paint containing nanoparticles is brushed on the transparent glass, the visible light transmittance is greater than 80%, and the temperature difference between the inside and outside of the test system is 5-8 degrees Celsius in the heat-insulation test.

Embodiment 3

[0024] Add 10 parts of aluminum oxide, titanium oxide, zinc oxide nano-scale powder slurry and 40 parts of deionized water to 45 parts of water-based acrylic emulsion, and adjust the pH value to 8.5 with ammonia solution; the water-based acrylic acid containing nano-oxide The emulsion was mechanically stirred for 30 minutes, and 5 parts of defoamer, dispersant, and leveling agent were added at the same time; then stirred with a high-speed mixer for 40 minutes, and finally ultrasonically oscillated for 30 minutes to obtain a transparent heat-insulating coating containing nanoparticles.

[0025] The above-mentioned transparent heat-insulating paint containing nanoparticles is brushed on the transparent glass, the visible light transmittance is greater than 75%, and the temperature difference between the inside and outside of the test system is 2-4 degrees Celsius in the heat-insulation test.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a transparent heat insulation coating with nanoparticles and a preparation method thereof; the preparation method comprises the following steps: adding nanoscale powder slurry of aluminum oxide, silicon oxide, titanium oxide, zinc oxide, cerium oxide, iron oxide, ATO and the like in water-based acrylic emulsion, adjusting the pH value to 5.5-9.0, stirring with a machine for 30-60min while adding defoaming agent, dispersant and flatting agent, then stirring with a high speed stirrer for 20-40min and finally performing ultrasonic vibration for 30-60min to obtain the transparent heat insulation coating. The invention has low cost and simple production process, after the coating is coated to form a film, the film has good transmission of light and outstanding heat-shielding performance; the coating has better self-cleaning ability, good durability and good washing resistance and brushing resistance; and the film has long life, good stability and simple maintenance.

Description

technical field [0001] The invention relates to a transparent heat-insulating paint containing nanoparticles and a preparation method thereof. After the paint is applied on the glass to form a film, it can ensure good light transmission and has excellent heat insulation performance; it is a new material for environmental protection and energy saving. Background technique [0002] In recent years, with the rapid development of my country's economy, urban construction is changing with each passing day, and new buildings are rising every day. Under the thermal radiation of sunlight, the temperature of glass windows and transparent ceilings of buildings will gradually rise, which will increase the utilization rate of air conditioners and increase energy consumption. According to statistics from the U.S. Department of Energy, 30% to 50% of the cooling energy of air conditioners is consumed by solar energy passing through windows. In addition, the ultraviolet rays in the sun wil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D7/12C09D5/00C03C17/32
Inventor 黎源
Owner 黎源
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com