Zinc-oxide-based nanometer particle ink and preparation method thereof

A nano-particle, zinc oxide-based technology, used in inks, household appliances, applications, etc., can solve the problems of fast volatilization speed, low viscosity, unsuitable for inkjet printing requirements, etc., to achieve uniform and stable dispersion.

Inactive Publication Date: 2017-02-08
TCL CORPORATION
View PDF3 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In view of the above-mentioned deficiencies in the prior art, the object of the present invention is to provide a zinc oxide-based nanoparticle ink and its preparation method, aiming to solve the problem that the existing zinc oxide-based nano-solution has low viscosity and too fast volatilization speed, which is not suitable for inkjet printing. asked questions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] ZnO nanoparticles are prepared by liquid phase method (the existing technology has been published, so I won’t go into details here)

[0049] The low-boiling point alcohol solvent uses methanol, the boiling point is 64.7°C, the viscosity is 0.59 (20°C), and the density is 0.79 g / ml; the high-boiling point alcohol solvent uses ethylene glycol, the boiling point is 197°C, the viscosity is 19.9 (20°C) , with a density of 1.12 g / ml.

[0050] The ZnO nanoparticle solution prepared by the liquid phase method was added with a precipitant, centrifuged and dried to obtain the ZnO nanoparticle, and 1 g of the ZnO nanoparticle was weighed for use. Measure 62.7 ml (49.5 g) of methanol and pour it into a 200 ml single-necked flask, then pour 1 g of ZnO nanoparticles into the methanol, and shake or stir fully to disperse the ZnO nanoparticles into the methanol. Finally, 44.2 milliliters (49.5 grams) of ethylene glycol was added, and fully oscillated or stirred to prepare 107 millilit...

Embodiment 2

[0052] Zn x Mg 1-x O nanoparticle ink

[0053] Zn x Mg 1-x O nanoparticles can be prepared by liquid phase method (the prior art has been published, so I won’t go into details here)

[0054] The low-boiling point alcohol solvent is ethanol, with a boiling point of 78.3°C, a viscosity of 1.17 (20°C), and a density of 0.79 g / ml; a high-boiling point alcohol solvent is n-octanol, with a boiling point of 195°C and a viscosity of 8.71 (20°C). , with a density of 0.83 g / ml.

[0055] Zn prepared by liquid phase method x Mg 1-x The O nanoparticles solution was added with precipitant and centrifuged and dried to obtain Zn x Mg 1-x O nanoparticles, weighed Zn x Mg 1-x O nanoparticle 1 gram, stand-by. Measure 25.1 ml (19.8 g) of ethanol and pour it into a 200 ml one-necked flask, then add 1 g of Zn x Mg 1-x Pour the O nanoparticles into ethanol and shake or stir well to make the Zn x Mg 1-x O particles dispersed in ethanol solution. Finally, 95.4 ml (79.2 g) of n-octanol ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
boiling pointaaaaaaaaaa
particle diameteraaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a zinc-oxide-based nanometer particle ink and a preparation method thereof. The zinc-oxide-based nanometer particle ink comprises the following components, by weight percentage, 0.01-20.0% of zinc-oxide-based nanometer particles and 80.0-99.99% of a solvent. The solvent comprises at least one low-boiling-point alcohols solvent and at least one high-boiling-point alcohols solvent, wherein the amount of low-boiling-point alcohols solvent is 1.0-80.0% of the total amount of the solvent. According to an ink formula in the invention, zinc-oxide-based nanometer particles can be dispersed in the solvent, and the viscosity of the solvent is improved and the volatilization speed of the solvent is lowered by adjusting low-boiling-point alcohols with high-boiling-point alcohols. The ink can meet the index requirements, such as ink viscosity and volatilization speed, of ink-jet printing, and zinc-oxide-based nanometer particles of the ink can be uniformly stably dispersed in the solvent.

Description

technical field [0001] The invention relates to the field of ink for inkjet printing, in particular to a zinc oxide-based nano particle ink and a preparation method thereof. Background technique [0002] Zinc oxide is a kind of II-VI compound semiconductor material with wide bandgap and direct bandgap. The bandgap width at room temperature is 3.37eV. It is an important semiconductor optoelectronic material. Electrically behaves as an n-type conductivity type with a resistivity as low as 10 -4 Ω / cm. Because of its excellent photoelectric properties, it has great application value in photoelectric devices, such as its high transmittance to visible light, it can be used as a transparent conductive coating; it has a photoelectric effect, and can be used in ultraviolet laser devices and solar energy Batteries, etc.; have good electron transport properties, and can be used as charge transport materials for flat panel display devices such as organic electroluminescence (OLED) and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/30C09D11/36C09D11/52
CPCC09D11/30C09D11/36C09D11/52
Inventor 谢相伟
Owner TCL CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap