A kind of thermal insulation coating for architectural glass and preparation method thereof

A technology for thermal insulation coatings and architectural glass, applied in the field of coatings, can solve problems such as poor dispersion of coatings and uneven film formation, and achieve the effects of strong adhesion, uniform film formation, and excellent heat insulation effect.

Active Publication Date: 2017-11-07
TIANJIN BINTAI TECH DEV CO LTD
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this technical solution has defects such as poor coating dispersion and uneven film formation. Although the heat insulation effect is obvious, it needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A preparation method for thermal insulation coating for architectural glass, comprising the steps of:

[0029] The first step is to prepare ATO alcohol slurry:

[0030] Put the ATO powder with a particle size of 5-50nm into absolute ethanol, stir evenly, add BYK180 dispersant, stir again, add cationic polyacrylamide, and then adjust the pH to 9 with a pH regulator (sodium hydroxide or hydrochloric acid) After stirring evenly, ultrasonically disperse for 10 minutes, then disperse with a high-speed disperser for 100 minutes, and finally disperse with a ball mill for 100 minutes. The weight percentage of ATO in the obtained alcohol slurry is 10%, the weight percentage of BYK180 dispersant is 2.5%, and the weight percentage of polyacrylamide The percentage is 0.5%;

[0031] The second step is to prepare ATO thermal insulation coating:

[0032] Add the ATO alcohol slurry obtained in the first step into polyvinyl butyral and add coating additives, mix and stir evenly. The w...

Embodiment 2

[0035] A preparation method for thermal insulation coating for architectural glass, comprising the steps of:

[0036] The first step is to prepare ATO alcohol slurry:

[0037] Put ATO powder with a particle size of 5-50nm into isopropanol, stir evenly, add polymer polysiloxane HX-4030 dispersant, stir again, add cationic polyacrylamide, and then use pH regulator ( sodium hydroxide or hydrochloric acid) to adjust the pH to be 9, after stirring evenly, ultrasonically disperse for 20min, then disperse for 120min with a high-speed disperser, and finally disperse for 120min with a ball mill, and the weight percentage of ATO in the obtained alcohol slurry is 30%. The weight percentage of silicone HX-4030 dispersant is 6%, and the weight percentage of polyacrylamide is 3%;

[0038] The second step is to prepare ATO thermal insulation coating:

[0039] Add the ATO alcohol slurry obtained in the first step into the urea-formaldehyde resin and add coating additives, mix and stir evenl...

Embodiment 3

[0042] A preparation method for thermal insulation coating for architectural glass, comprising the steps of:

[0043] The first step is to prepare ATO alcohol slurry:

[0044] Put the ATO powder with a particle size of 5-50nm into isobutanol, stir evenly, add polymer polysiloxane HX-4030 dispersant, stir again, add cationic polyacrylamide, and then use pH regulator ( sodium hydroxide or hydrochloric acid) to adjust the pH to be 9, after stirring evenly, ultrasonically disperse for 20min, then disperse with a high-speed disperser for 120min, and finally disperse with a ball mill for 120min, and the weight percentage of ATO in the obtained alcohol slurry is 20%. The weight percentage of silicone HX-4030 dispersant is 3%, and the weight percentage of polyacrylamide is 1.5%;

[0045] The second step is to prepare ATO thermal insulation coating:

[0046] Add the ATO alcohol slurry obtained in the first step into the rosin-modified alkyd resin and add coating additives, mix and stir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
adhesivityaaaaaaaaaa
adhesivityaaaaaaaaaa
Login to view more

Abstract

The invention proposes a method for preparing thermal insulation coatings for architectural glass, comprising: preparing ATO alcohol slurry: putting ATO powder into an alcoholic solvent, stirring evenly, adding a polymer cationic dispersant, stirring again evenly, adding Cationic surfactant, then use a pH regulator to adjust the pH to 9, and then use ultrasonic dispersion, high-speed disperser dispersion and ball mill dispersion to carry out staged dispersion after stirring evenly, and the weight percentage of ATO in the obtained alcohol slurry is 10-30% , the weight percentage of polymeric cationic dispersant is 2.5-6%, and the weight percentage of cationic surfactant is 0.5-3%; Add alcoholic resin and coating auxiliary agent to prepare ATO thermal insulation coating afterwards, final product is environment-friendly insulation Thermal coating has good dispersibility, high stability, uniform film formation, and better heat insulation effect.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a thermal insulation coating for architectural glass and a preparation method thereof. Background technique [0002] With the development of the construction industry, building energy efficiency has been paid more and more attention. Among the four enclosure components of doors, windows, walls, roof, and ground that affect building energy consumption, doors and windows have the worst thermal insulation performance, which is one of the important factors affecting indoor thermal environment comfort and building energy consumption. As the main component of the door frame, the glass has poor heat insulation effect, which is the main reason for the energy loss of buildings. [0003] Patent: A high-performance thermal insulation coating and its preparation method (application number 201110157311.5) provides thermal insulation coatings with the following component weight ratios: film-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D129/14C09D161/24C09D167/08C09D7/12C03C17/32
Inventor 么文新杨秋良
Owner TIANJIN BINTAI TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap