Foam substrate dressing and preparation method thereof

A foam and base frame technology, applied in the field of foam-based dressings and its preparation, can solve the problems of medical workers and patients, large differences in production processes and equipment, and different ways of use, etc., to achieve good ease of use and low cost , good effect

Active Publication Date: 2016-05-04
厦门百美特生物材料科技有限公司
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the materials used for these major types of dressings are very different, the production processes and equipment are so different that they are not compatible, and the methods of use are also different, which has caused great troubles to medical workers and patients.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Example 1: Preparation of Foam-Based Vertical Absorbent Dressing

[0038] A foam-based dressing, which is a foam-based vertical absorbent dressing with a water content not higher than 22wt%, is composed of a base frame made of a sheet-shaped polyurethane foam dressing and a gel material filled and attached to the cells of the base frame, and the gel material Including 75wt% sodium alginate, 7.5wt% hydrophilic synthetic polymer polyacrylamide and 17.5wt% carboxymethylcellulose sodium (CMC-Na); the specific preparation method is as follows:

[0039] 1) The above-mentioned gel material, that is, 75wt% sodium alginate, 7.5wt% polyacrylamide and 17.5wt% carboxymethylcellulose sodium, was dissolved in water, and the solid content was 3.6 after stirring, filtering, defoaming, and standing. The gel stock solution of wt%; The sheet polyurethane foam dressing that commercially available thickness is 5mm is immersed in this gel stock solution;

[0040] 2) Use a pressure roller to...

Embodiment 2

[0046] Example 2: Preparation of Foam-Based Hydrocolloid Dressing

[0047] A foam-based dressing, which is a foam-based hydrocolloid dressing with a water content of 22 to 50 wt%, is composed of a base frame made of a sheet-shaped polyurethane foam dressing and a gel material filled and attached to the cells of the base frame, and the gel material includes 75 wt% % sodium carboxymethylcellulose, 10wt% xanthan gum and 15wt% sodium alginate; the specific preparation method is as follows:

[0048] 1) The above-mentioned gel material, i.e. 5wt% sodium carboxymethylcellulose, 10wt% xanthan gum and 15wt% sodium alginate, are dissolved in water, stirred, filtered, defoamed, and left to stand to make a solid content of 6wt%. Gel stock solution; a commercially available sheet-shaped polyurethane foam dressing with a thickness of 3 mm is immersed in the gel stock solution;

[0049] 2) Use a pressure roller to squeeze evenly from one side of the sheet-shaped polyurethane foam dressing t...

Embodiment 3

[0054] Example 3: Preparation of Foam-Based Hydrogel Dressing

[0055] A foam-based dressing, which is a foam-based hydrogel dressing with a water content of 50-90 wt%, is composed of a base frame made of a sheet-shaped polyurethane foam dressing and a gel material filled and attached to the cells of the base frame, and the gel material includes 55wt% k-type carrageenan, 25wt% gelatin and 20wt% sodium alginate; the specific preparation method is as follows:

[0056] 1) The above-mentioned gel material, that is, 55wt% k-type carrageenan, 25wt% gelatin and 20wt% sodium alginate, are dissolved in water at 90°C, stirred, filtered, defoamed, and left to stand to make a solid content of 4wt%. Collagen solution; a commercially available sheet-shaped polyurethane foam dressing with a thickness of 2mm is immersed in the gel stock solution;

[0057] 2) Use a pressure roller to squeeze evenly from one side of the sheet-shaped polyurethane foam dressing to the other side in parallel to g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Water contentaaaaaaaaaa
Water contentaaaaaaaaaa
Login to View More

Abstract

The invention discloses foam substrate dressing and a preparation method thereof. The foam substrate dressing is formed by a base frame made from platy foam dressing and a gel material filled and attached into base frame holes, contains foam substrate vertical absorption dressing with water content being not higher than 22wt%, foam substrate hydrocolloid dressing with water content being 22 to 50wt%, and foam substrate hydrogel dressing with water content being 50 to 90wt%, and is suitable for wounds of different seepage amounts. According to the dressing and the preparation method thereof, platy foam dressing is used as the base frame, and the holes are filled with the gel material in an attachment manner, so as to prepare novel wet dressing meeting the application of different wounds and different healing phases; meanwhile, the preparation process is similar, the required devices are mutually compatible, and the production is simple and easy.

Description

technical field [0001] The invention belongs to the field of medical dressings, in particular to a foam-based dressing and a preparation method thereof. Background technique [0002] The core concept of modern wound dressing design is exudate management, and various dressings have been developed and applied for wounds with different exudate volumes. [0003] The main varieties of modern wet dressings are: (1) alginate dressing and foam dressing, which are suitable for the care of moderate to severe exudate wounds. They are prepared by foaming alginate fiber and polyurethane or polyurethane or polyvinyl alcohol respectively. Silver ions also have an antibacterial function; (2) hydrocolloid dressings, suitable for the care of small to moderate exudate wounds, mainly prepared into sheets with CMC and hot-melt elastic polymers such as rubber and polyisobutylene, and backed with polyurethane Film, or, attaching hydrocolloid particles on oily gauze; (3) hydrogel dressing, suitabl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61L26/00
CPCA61L26/0014A61L26/0019A61L26/0023A61L26/0038A61L26/0066A61L26/008A61L26/0085A61L2300/102A61L2300/104A61L2300/404C08L75/04C08L29/04C08L5/08C08L1/26C08L5/04C08L3/02C08L5/06C08L5/12C08L5/00
Inventor 蓝煌琴吴晓玲刘澄胜邱冬刘松林黄福龙
Owner 厦门百美特生物材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com