Novel bonding agent for straw artificial board and production method of novel bonding agent

A technology of adhesives and wood-based panels, applied in the direction of adhesive types, inorganic adhesives, polymer adhesive additives, etc., can solve the problems of difficult adhesion of glue, reduce production process and pollution, and reduce costs Effect

Inactive Publication Date: 2016-05-04
ZHENGZHOU JINQI INFORMATION TECH CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the problem in the above-mentioned prior art that the general glue is difficult to bond because the surface of the straw contains substances such as wax and silicon

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The new type of adhesive for straw-based panels contains material components in the following weight ratio: adhesive: curing agent: modifier: phenolic resin is 10:60:1:30.

[0019] The curing agent is magnesium oxide, the content of which is above 80%, and the best active content is above 60%; the binder is magnesium chloride, and the content of magnesium chloride is 90%.

[0020] The modifier is redispersible latex powder or sodium hydroxymethylcellulose (CMC);

[0021] The production method of the adhesive for the novel straw-based panel comprises the following steps:

[0022] a. Put the binder magnesium chloride into the container, add water and stir evenly according to the weight ratio of 1:5 to make it liquefied and ready for use; the solution concentration is 25%;

[0023] b. Put the magnesium chloride liquid prepared in step a into the curing agent magnesium oxide, then add modifier redispersible latex powder or sodium hydroxymethylcellulose (CMC) phenolic resin...

Embodiment 2

[0026] The new type of adhesive for straw-based panels comprises material components in the following weight ratio: adhesive: curing agent: modifier: phenolic resin is 15:70:2:5.

[0027] The adhesive for the new straw-based panel, the curing agent is magnesium oxide, the content of which is more than 83%, and the best active content is more than 63%; the adhesive is magnesium chloride, and the content of magnesium chloride is 91%. good.

[0028] In the novel adhesive for straw-based panels, the modifier is redispersible latex powder or sodium hydroxymethylcellulose (CMC).

[0029] The production method of the adhesive for the novel straw-based panel comprises the following steps:

[0030] a. Put the binder magnesium chloride into the container, add water and stir evenly according to the weight ratio of 1:5 to make it liquefied and ready for use; the solution concentration is 27%;

[0031] b. Put the magnesium chloride liquid prepared in step a into the curing agent magnesiu...

Embodiment 3

[0034] Adhesive for novel straw-based panels, comprising material components in the following weight ratios:

[0035] Adhesive: curing agent: modifier: phenolic resin is 28:80:4:8.

[0036] The adhesive for the new straw-based panel, the curing agent is magnesium oxide, the content of which is more than 88%, and the active content is more than 68%. The adhesive is magnesium chloride, and the content of magnesium chloride is 94%. good.

[0037] In the novel adhesive for straw-based panels, the modifier is redispersible latex powder or sodium hydroxymethylcellulose (CMC).

[0038] The production method of the adhesive for the novel straw-based panel comprises the following steps:

[0039] a. Put the binder magnesium chloride into the container, add water and stir evenly according to the weight ratio of 1:5 to make it liquefied and ready for use; the solution concentration is 28.5%;

[0040] b. Put the magnesium chloride liquid prepared in step a into the curing agent magnesiu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel ecological non-toxic waterproof flame-retardant bonding agent for straw artificial board production. The bonding agent is prepared from the following ingredients in proportion by weight: 10 to 35 percent of bonding agents, 60 to 90 percent of curing agents, 1 to 5 percent of modifying agents and 3 to 10 percent of phenolic resin. Double ingredients of main bonding agents and the curing agents are used; the certain modifying agents are added so as to enhance the bonding force of the bonding agent and improve the anti-bending intensity and anti-impact and waterproof performance. The bonding agent breaks through the industry barrier that isocyanate is necessary for the production of a straw artificial board at present. The production cost is reduced; the product quality is improved, so that the product has the characteristics of non-toxicity, waterproof performance, flame-retardant performance and the like. All equipment and processes for producing the straw artificial board both at home and abroad adopt a hot pressing process for production, the pollution is great, and the production cost is increased. When the novel special non-toxic waterproof flame-retardant special bonding agent for the straw artificial board is used, a cold pressing process is used for production, and the problem of the complicated hot pressing production process is fundamentally solved; the production efficiency is greatly improved. In addition, the produced product has the advantages of non-toxicity, waterproof performance, flame-retardant performance and an ecological and environment-friendly effect; a new crop straw integral utilization and farmer yield increase path is opened up.

Description

technical field [0001] The invention relates to the field of artificial board manufacturing, in particular to a novel adhesive for straw artificial boards and a production method thereof. Background technique [0002] my country is a large agricultural country with an annual output of 800 million tons of crop straw. In the situation of wood shortage, waste of crop straw resources and strong demand for wood-based panels, using crop straw instead of wood to make wood-based panels is a green and environmentally friendly alternative that saves a lot of forest resources. [0003] As an ecological, environmentally friendly and new energy-saving material, the new environmentally friendly straw-based panel not only has excellent product performance, is non-toxic and harmless, and can reach A-level waterproof and fireproof. Moreover, it can eliminate the pollution of the environment caused by the burning of straw by farmers, and achieve the comprehensive utilization of resources. A...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J1/00C09J11/08C09J161/06C09J11/04
CPCC08L2201/02C09J1/00C09J11/04C09J11/08C09J161/06C08L1/284C08L21/00C08K2003/166C08K2003/222
Inventor 刘学民师洪伟夏永纪
Owner ZHENGZHOU JINQI INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap