Gamma-MnO2 loaded mixed non-metal ore clay low-temperature denitration catalyst and preparation method thereof

A non-metal ore, low temperature denitration technology, applied in the field of denitration catalysis, can solve the problems of expensive catalyst carrier and high reaction activity temperature, and achieve the effects of abundant reserves, low activity temperature and convenient installation.

Active Publication Date: 2016-05-11
CHANGZHOU UNIV
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims at the disadvantages of expensive catalyst carrier and high reaction temperature in the prior art, and provides a mixed non-metallic ore clay-loaded γ-MnO 2 Low-temperature denitrification catalyst and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gamma-MnO2 loaded mixed non-metal ore clay low-temperature denitration catalyst and preparation method thereof
  • Gamma-MnO2 loaded mixed non-metal ore clay low-temperature denitration catalyst and preparation method thereof
  • Gamma-MnO2 loaded mixed non-metal ore clay low-temperature denitration catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] 1. Dissolve 10g of sepiolite clay and 10g of attapulgite clay in 1.5mol / L HCl until the solution does not produce bubbles, and let stand for 18h. Disperse the acidified non-metallic mineral clay in deionized water, use a 4000r / min emulsifier to pulp, and select the supernatant to obtain a 4g / 100mL suspension slurry;

[0018] 2. At room temperature, dissolve 100mL of MnSO with a mass concentration of 3g / 100mL 4 ·H 2 O and 130mL mass concentration of 3g / 100mL (NH 4 ) 2 S 2 o 8 Put the solution in 500mL step (1) slurry, keep stirring, raise the temperature to 80°C for 2h; after the reaction is complete, filter the product with suction, wash and dry to obtain 7wt.% γ-MnO 2 -Sepiolite clay / attapulgite clay low-temperature denitrification catalyst.

[0019] figure 1 It is the XRD pattern of sepiolite before and after acidification. According to the preparation method in Example 1, sepiolite was reacted in 1.5mol / LHCl; from the figure, it can be clearly seen that the 2θ...

Embodiment 2

[0022] 1. Dissolve 15g of sepiolite clay and 5g of montmorillonite clay in 1.5mol / L HCl until the solution does not produce bubbles, and let it stand for 24 hours. Disperse the acidified non-metallic mineral clay in deionized water, use a 5000r / min emulsifier to pulp, and select the supernatant to obtain a 5g / 100mL suspension slurry;

[0023] 2. At room temperature, dissolve 60mL of MnSO with a mass concentration of 5g / 100mL 4 ·H 2 O and 80mL mass concentration of 5g / 100mL (NH 4 ) 2 S 2 o 8 Put the solution in 400mL of step (1) slurry, keep stirring, raise the temperature to 75°C for 2.5h; after the reaction is complete, filter the product with suction, wash and dry to obtain 7wt.% γ-MnO 2 -Sepiolite clay / montmorillonite clay low-temperature denitrification catalyst.

Embodiment 3

[0025] 1. Dissolve 10g of sepiolite clay and 10g of cordierite clay in 2.5mol / L HCl until the solution does not produce bubbles, and let stand for 20h. Disperse the acidified non-metallic mineral clay in deionized water, use a 4000r / min emulsifier to pulp, and select the supernatant to obtain a 8g / 100mL suspension slurry;

[0026] 2. At room temperature, dissolve 75mL of MnSO with a mass concentration of 4g / 100mL 4 ·H 2 O and 100mL mass concentration of 4g / 100mL (NH 4 ) 2 S 2 o 8 Put the solution in 250mL step (1) slurry, keep stirring, raise the temperature to 85°C and react for 1.5h; after the reaction is complete, filter the product with suction, wash and dry to obtain 7wt.% γ-MnO 2 -Sepiolite clay / cordierite clay low-temperature denitrification catalyst.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of denitration catalyzing, and provides a gamma-MnO2 loaded mixed non-metal ore clay low-temperature denitration catalyst and a preparation method thereof. According to the catalyst, mixed non-metal ore clay is adopted as a carrier, an active component gamma-MnO2 is loaded, and the gamma-MnO2 loaded mixed non-metal ore clay low-temperature denitration catalyst is prepared. The catalyst is simple in preparation process, the prepared catalyst can achieve the effects of increasing the specific area, the pore volume and the aperture, and the strength of the catalyst is increased, so that the catalyst is easy to form and convenient to mount. In addition, the non-metal ore clay is low in price, and therefore the cost of the catalyst is greatly reduced.

Description

technical field [0001] The invention belongs to the field of denitrification catalysis, in particular to a mixed non-metallic ore clay loaded γ-MnO 2 Low temperature denitrification catalyst. Background technique [0002] Ammonia Selective Catalytic Reduction of NO x (NH 3 -SCR) is considered to be the most widely used flue gas denitrification technology in the world. This method has the advantages of no side effects, no secondary pollution, simple device structure, and high removal rate. However, the currently used V-W-Ti series of commercial catalysts have carrier TiO 2 Expensive, poor mechanical strength, difficult to shape and other disadvantages; at the same time V 2 o 5 As an active component, the reaction temperature required is relatively high, generally required to be controlled at 573-673K, and it is toxic. Therefore, it is necessary to develop low-temperature, cheap and pollution-free SCR catalyst technology. Chinese patent CN103381362A discloses a nano-TiO...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/34
CPCB01J23/34
Inventor 罗士平周文挺周兴蒙吴凤芹姚超左士祥刘文杰李霞章
Owner CHANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com