Auxiliary seal ring for pump mechanical seal moving ring
An auxiliary seal ring and mechanical seal technology, applied in other chemical processes, chemical instruments and methods, etc., can solve the problems of springback, insignificant cushioning effect, unsatisfactory service life, increased cost, etc., to achieve good sealing and use The effect of long life and improved fit
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] (1) Add 20 parts of epoxy resin and 15 parts of maleic anhydride to 75 parts of nitrile rubber, mix well, and then microwave at a frequency of 2450MHz and a power of 600W for 15 minutes. After the mixture is cooled to 70-80°C, add 8 parts Lanolin and 4 parts of nano zinc oxide are mixed uniformly to obtain material I;
[0017] (2) Fully mix 10 parts of stone powder and 6 parts of volcanic ash, heat it to 60-70°C and keep it for 10 minutes, then add 10 parts of microcrystalline cellulose and 8 parts of nano-silica powder, continue heating to 90-100°C and keep it for 10 minutes to get Material II;
[0018] (3) Add material II, 6 parts of epoxidized soybean oil, 3 parts of hemp stalk ash, 3 parts of calcium chloride, 3 parts of polyacrylamide and 1 part of vulcanizing agent into material I, mix well and add in the internal mixer, After the banbury rubber is obtained, it is vulcanized by a vulcanizing machine.
[0019] Preparation of stone powder: Add 20 parts of zeolite ...
Embodiment 2
[0021] (1) Add 25 parts of epoxy resin and 20 parts of maleic anhydride to 85 parts of nitrile rubber, mix well and then microwave at microwave frequency 2450MHz and power 600W for 15min, and add 6 parts after the mixture is cooled to 70-80°C Lanolin and 6 parts of nanometer zinc oxide are mixed uniformly to obtain material I;
[0022] (2) Fully mix 12 parts of stone powder and 8 parts of volcanic ash, heat it to 60-70°C and keep it for 10 minutes, then add 12 parts of microcrystalline cellulose and 5 parts of nano-silica micropowder, continue heating to 90-100°C and keep it for 10 minutes. Material II;
[0023] (3) Add material II, 8 parts of epoxidized soybean oil, 5 parts of hemp stalk ash, 4 parts of calcium chloride, 2 parts of polyacrylamide and 1 part of vulcanizing agent into material I, mix well and add in the internal mixer, After the banbury rubber is obtained, it is vulcanized by a vulcanizing machine.
[0024] Preparation of stone powder: add 25 parts of zeolite...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com