Crystal tombstone and manufacturing method thereof

A tombstone and crystal technology, applied in the field of tombstone and its preparation, can solve problems such as fracture and deformation, pollute the environment, easy to fade, etc., and achieve the effects of fast processing speed, high processing accuracy, and various processing techniques

Inactive Publication Date: 2016-06-22
段然
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Artificial stone tombstones usually use industrial resin and calcium carbonate as raw materials, and a large number of auxiliary materials are added in the processing process, which will not only cause a certain degree of pollution to the environment, but also easily fade,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Crystal tombstone and manufacturing method thereof
  • Crystal tombstone and manufacturing method thereof
  • Crystal tombstone and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0056] Example 1:

[0057] An artificial crystal tombstone is prepared by the following method:

[0058] (1) Cleaning the mold: Use the glass fiber reinforced plastic mold as the preparation mold, thoroughly clean and refurbish it before use, brush the gel coat resin on the area that needs to be refurbished, cover it with polyester film, roll it, and polish the surface after curing;

[0059] (2) Waxing: After finishing the mold cleaning step described in step (1), stick a little 99 polish wax with a soft cloth or sponge, and wipe the inner surface of the mold once. After the polishing wax dries, polish the inner surface of the mold. ;

[0060] (3) Apply mold release agent: After the waxing step described in step (2), apply a layer of mold release agent on the inner surface of the waxed mold. After the mold release agent dries, apply it to the mold release agent. Brush a layer of gel coat resin on the outer layer, and proceed to the next step after the gel coat resin is dry;

[0061] (...

Example Embodiment

[0074] Example 2:

[0075] An artificial crystal tombstone is prepared by the following method:

[0076] (1) Cleaning the mold: Use the glass fiber reinforced plastic mold as the preparation mold, thoroughly clean and refurbish it before use, brush the gel coat resin on the area that needs to be refurbished, cover it with polyester film, roll it, and polish the surface after curing;

[0077] (2) Waxing: After the mold cleaning step described in step (1), stick a little American carnauba wax with a soft cloth or sponge, wipe the inner surface of the mold once, and polish the inner surface of the mold after the palm wax is slightly dry ;

[0078] (3) Apply mold release agent: After the waxing step described in step (2), apply a layer of mold release agent on the inner surface of the waxed mold. After the mold release agent dries, apply it to the mold release agent. Brush a layer of gel coat resin on the outer layer, and proceed to the next step after the gel coat resin is dry;

[0079] ...

Example Embodiment

[0089] Example 3:

[0090] An artificial crystal tombstone is prepared by the following method:

[0091] (1) Cleaning the mold: Use the glass fiber reinforced plastic mold as the preparation mold, thoroughly clean and refurbish it before use, brush the gel coat resin on the area that needs to be refurbished, cover it with polyester film, roll it, and polish the surface after curing;

[0092] (2) Waxing: After the mold cleaning step described in step (1) is finished, use a soft cloth or sponge to stick a little Samsung brand wax, and wipe the inner surface of the mold once. After the Samsung brand wax dries, polish the inner surface of the mold;

[0093] (3) Apply mold release agent: After the waxing step described in step (2), apply a layer of mold release agent on the inner surface of the waxed mold. After the mold release agent dries, apply it to the mold release agent. Brush a layer of gel coat resin on the outer layer, and proceed to the next step after the gel coat resin is dry; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a crystal tombstone and a manufacturing method thereof. The crystal tombstone is manufactured through artificial crystals. A tombstone body of the crystal tombstone is solid. The surface of the tombstone body of the crystal tombstone is provided with a plane and/or three-dimensional colored or colorless patterns and/or characters, wherein the plane is carved through a laser carving machine and/or a rotating carving machine. The surface of the tombstone body is further provided with a colored or colorless departed saint picture carved through the laser carving machine. According to the crystal tombstone, a traditional stone or artificial stone tombstone is replaced with artificial crystal glass, the tombstone body is completely transparent and can reflect sunlight, a fashionable sunny tombstone group with the modern characteristics and the innovated idea is made, the visual impact, the good light transmittance, the whole shocking sense and the obvious image are achieved, a deep impression is given to people, the people will feel conspicuous, and a forerunner path is developed for the future funeral and interment industry. The patterns, the characters and the picture can be carved on the tombstone body and never fade, the crystal tombstone is exquisite and is like artware, the personal character is demonstrated, and people are made to be reluctant to leave.

Description

technical field [0001] The invention relates to a tombstone and a preparation method thereof, in particular to a crystal tombstone and a preparation method thereof, belonging to funeral supplies. Background technique [0002] After the death of a relative, they must be buried in the ground for peace. People generally buy a cemetery and erect a tombstone for the deceased relative to commemorate and sacrifice. At present, the tombstone is usually made of stone, mostly natural marble tombstone, natural granite tombstone or artificial stone tombstone. Natural marble tombstones are compact and hard, easy to carve, wear-resistant and not deformed; however, natural marble generally contains impurities such as calcium carbonate, and calcium carbonate is easily weathered and eroded by carbon dioxide, water vapor, etc. in the atmosphere, so natural marble tombstones The anti-acid, rainproof, sunscreen, mothproof and anti-erosion properties are relatively poor. The natural granite to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): E04H13/00C08L67/06C08K5/07C08K5/17C08K5/405C08K5/098
CPCC08K5/07C08K5/098C08K5/17C08K5/405E04H13/003C08L67/06
Inventor 段然
Owner 段然
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka