Preparation method of high-gloss environment-friendly organic pigment slurry for natural latex balloons

A technology of organic pigments and natural latex, applied in the direction of pigment paste, etc., can solve the problems of no research, no consideration of gloss problems, etc., and achieve the effect of good environmental protection, bright colors and high gloss

Active Publication Date: 2016-06-29
ZHEJIANG NAMEI MATERIAL TECH
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The current patent ZL201210050474.8 on the environmental protection of colorants for latex products focuses on heavy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] a. Weigh 42.0% deionized water, 5.5% wetting and dispersing agent (Wenkel HLD-8 / KS), 6.0% wetting and dispersing agent (sunrise TG), 6.0% brightener ( Wenkel E-360), 10.0% ethylene glycol, 0.5% ammonia water and 0.2% ProxelBZplus were placed in the dispersion tank, stirred and dispersed at a speed of 450rpm for 12min, and a uniform transparent solution was obtained;

[0020] b. Add 35.0% Pigment Red 122 (Jinyuan Pigment Red 1221D) into the homogeneous transparent solution obtained in step a during the dispersion and stirring process, disperse at a speed of 1800 rpm, and disperse for 45 minutes to obtain an environmentally friendly organic pigment pre-dispersed color paste ;

[0021] c. Grind the pre-dispersed environment-friendly organic pigment color paste obtained in step b. The method used for grinding is horizontal grinding, and the grinding medium is high-purity zirconium beads of 0.6 to 0.8 mm. When the average particle size of the color paste is D 80 <0.5μm, whe...

Embodiment 2

[0024] a. Weigh 34.0% deionized water, 5.0% wetting and dispersing agent (Wenkaier HLD-25), 7.0% wetting and dispersing agent (Sunrise TG), 1.0% brightening agent (Wenkaier HLD-25) according to the above weight percentage E-360), 10.0% propylene glycol, 0.8% monoethanolamine and 0.2% ProxelBZplus were placed in the dispersion tank, stirred and dispersed at a speed of 450rpm for 15min to obtain a uniform transparent solution;

[0025] b. Add 42.0% phthalocyanine blue B (Shuangle blue 7502) into the homogeneous transparent solution obtained in step a during the dispersion and stirring process, disperse at a speed of 2000 rpm, and disperse for 40 minutes to obtain an environmentally friendly organic pigment pre-dispersed color paste ;

[0026] c. Grind the pre-dispersed environment-friendly organic pigment color paste obtained in step b. The method used for grinding is horizontal grinding, and the grinding medium is high-purity zirconium beads of 0.6 to 0.8 mm. When the average p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of high-gloss environment-friendly organic pigment slurry for natural latex balloons. The high-gloss environment-friendly organic pigment slurry comprises organic pigment, wetting dispersant, brightener, humectant, anti-mildew bactericide, pH regulator and deionized water. The preparation method includes: pre-dispersing and grinding the components, and then performing quality inspection, vacuum defoaming and filtration to obtain the required environment-friendly organic pigment slurry. The high-gloss environment-friendly organic pigment slurry prepared by the method has the advantages that the slurry is high in glossiness and good in environment protection performance, the deionized water is used as the solvent, and the slurry conforms to the environment-friendly requirement of China.

Description

technical field [0001] The invention relates to the field of fine chemicals, in particular to the field of natural latex in the rubber industry. Background technique [0002] With the development of the latex products industry, especially the continuous development of the natural latex balloon industry, the use of pigments and ordinary colorants to color natural latex balloons has been unable to meet environmental protection and application requirements. The use of pigments for coloring has the problems of dust pollution and high toxicity. Ordinary colorants contain unhealthy and environmentally unfriendly factors such as alkylphenol polyoxyethylene ether (APEO), azo compounds (AZO), heavy metals, and volatile organic components (VOC), which affect the environmental protection of natural latex balloon coloring. Great security risk. American toy safety standard ASTMF963, European Union toy safety standard EN71, REACH regulations and "National Toy Safety Technical Specificat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08K13/02C08J3/215C09D17/00
Inventor 郭小春张开瑞刘彦雷赵磊张涛何贵平
Owner ZHEJIANG NAMEI MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap