Alumina ceramic wafer treatment process

An alumina ceramics and processing technology, applied in chemical instruments and methods, cleaning methods and utensils, cleaning methods using liquids, etc. Firmness and other problems, to achieve the effect of strong surface adsorption, light weight, and prolong the service life of the equipment

Inactive Publication Date: 2016-07-06
杨莉
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The hardness of the ceramic patch is ≥ HRA85, second only to the hardness of diamond, and the surface is smooth, the friction coefficient is small, and the wear resistance is very ideal, especially in the high temperature oxidizing medium or corrosive medi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0025] Example 1

[0026] A process for processing an alumina ceramic sheet, the steps are as follows:

[0027] (1) Distilled water cleaning: completely place the ceramic sheet in 100% pure water for cleaning and drying;

[0028] (2) Ketone washing: soak the cleaned ceramic sheet in 30% acetone for half an hour and dry it;

[0029] (3) Alkaline washing: soak the ketone-washed ceramic sheet in 60% sodium carbonate solution for half an hour, and dry it;

[0030] (4) Pickling: soak the ceramic sheet dried in step (3) in an 8% sulfuric acid solution and dry.

Example Embodiment

[0031] Example 2

[0032] A process for processing an alumina ceramic sheet, the steps are as follows:

[0033] (1) Distilled water cleaning: completely place the ceramic sheet in 100% pure water for cleaning and drying;

[0034] (2) Ketone washing: soak the cleaned ceramic sheet in 35% acetone for half an hour and dry it;

[0035] (3) Alkaline washing: soak the ketone-washed ceramic sheet in 65% sodium carbonate solution for half an hour, and dry it;

[0036] (4) Pickling: soak the ceramic sheet dried in step (3) in a 10% sulfuric acid solution and dry.

Example Embodiment

[0037] Example 3

[0038] A process for processing an alumina ceramic sheet, the steps are as follows:

[0039] (1) Distilled water cleaning: completely place the ceramic sheet in 100% pure water for cleaning and drying;

[0040] (2) Ketone washing: soak the cleaned ceramic sheet in 40% acetone for half an hour, and then dry it;

[0041] (3) Alkaline washing: soak the ketone-washed ceramic sheet in 70% sodium carbonate solution for half an hour, and dry it;

[0042] (4) Pickling: soak the ceramic sheet dried in step (3) in a 12% sulfuric acid solution and dry.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A treatment process for alumina ceramic sheets, the steps are as follows: (1) Distilled water cleaning: wash and dry the ceramic sheets in 100% pure water; (2) Ketone washing: place the cleaned ceramic sheets in a 30-40 % acetone and dried; (3) Alkaline cleaning: Soak the ketone-washed ceramic sheet in 60-70% sodium carbonate solution and dry; (4) Pickling: Dry the ceramic sheet in step (3) The ceramic sheet is soaked in 10% sulfuric acid solution and dried; the beneficial effects of the present invention are: high hardness, excellent wear resistance, light weight, strong surface adsorption force, which is the highest surface adsorption force of untreated ceramic sheet 10‑20, very strong and durable after being combined with rubber by glue.

Description

technical field [0001] The invention relates to the technical field of alumina ceramic sheet processing, in particular to an alumina ceramic sheet processing process. Background technique [0002] Alumina ceramics: high alumina content, relatively dense structure, and special properties, so it is called special ceramics. Al2O3. The ceramic material is a close-packed hexagonal structure composed of oxygen ions, and aluminum ions are filled in two-thirds of the octahedral gaps. This is the same stable α-Al2O3 structure as natural corundum, so the ceramic has a high melting point, high Hardness, with excellent wear resistance. The hardness of the ceramic patch is ≥ HRA85, second only to the hardness of diamond, and the surface is smooth, the friction coefficient is small, and the wear resistance is very ideal, especially in the high temperature oxidizing medium or corrosive medium, the material of the ceramic patch has better performance than other metal materials. It is much...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/80B08B3/04B08B3/08
CPCC04B41/00B08B3/04B08B3/08C04B41/009C04B41/80
Inventor 杨莉
Owner 杨莉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap