Method for washing aluminum alloy oxidation film to be welded via laser

A laser cleaning and oxide film technology, applied in cleaning methods and utensils, chemical instruments and methods, laser welding equipment, etc., can solve the problems of polluted environment, many processes, surface scratches and damage, achieve a high degree of automation, improve cleaning The effect of efficiency

Active Publication Date: 2016-07-20
上海临仕激光科技有限公司 +1
View PDF6 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0027] The purpose of the present invention is to provide a method for laser cleaning of aluminum alloy oxide film before welding, provide a high-efficiency, high-quality, environmentally friendly, stable laser cleaning process for al...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for washing aluminum alloy oxidation film to be welded via laser
  • Method for washing aluminum alloy oxidation film to be welded via laser
  • Method for washing aluminum alloy oxidation film to be welded via laser

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0052] figure 1 is a flow chart of the steps of a method embodiment of the present invention, figure 2 is a schematic diagram of laser cleaning, such as figure 1 and figure 2 As shown, the embodiment of the present invention provides a method for laser cleaning aluminum oxide film before welding, including:

[0053]Position setting step 10: setting the positions of the aluminum alloy workpiece and the laser oscillating lens, the laser oscillating lens can emit a laser beam 101 of short nanosecond pulses, the optical axis of the laser beam 101 is in contact with the aluminum alloy workpiece to be cleaned The surfaces 102 intersect and form an angle α at the intersection point, 30°≤α≤60°; set the compressed air nozzle 103 to point to the intersection point, and make the compressed air nozzle 103 form an angle β with the surface to be cleaned 102 , 10°≤β≤20°; set the suction nozzle 104 of the vacuum system to point to the intersection point, and make the suction nozzle 104 f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Lengthaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for washing an aluminum alloy oxidation film to be welded via laser, relates to an efficient, high-quality, environmentally-friendly and stable washing process and solves the problems such as multiple processes, low efficiency, surface scratch damage, low stability and environmental pollution and the like of the chemical and mechanical washing methods at present. The method comprises the following steps: a position setting step, wherein a laser galvanometer head is capable of emitting a laser beam with nanoscale short pulse, an included angle alpha is formed between an optical axis of the laser beam and a surface to be washed at an intersection point, and alpha is greater than or equal to 30 degrees and less than or equal to 60 degrees; enabling a compressed air nozzle to point at the intersection point, forming an included angle beta between the compressed air nozzle and the surface to be washed, wherein beta is greater than or equal to 10 degrees and less than or equal to 20 degrees; enabling a suction nozzle of a dust sucking system to point at the intersection point, and forming an included angle gamma between the suction nozzle and the surface to be washed; a power setting step of setting average power and washing rate of the laser beam according to the thickness of an oxidization film with the surface to be washed; and a washing step of washing the surface to be washed via laser at the average power and the washing rate.

Description

technical field [0001] The invention relates to laser cleaning and laser welding technology, in particular to a method for laser cleaning of an aluminum alloy oxide film before welding. Background technique [0002] There are different forms of oxide films on the surface of aluminum alloys. At relatively low temperatures, the form of oxides is mostly Bayer body, and its composition is aluminum hydroxide, that is, Al(OH) 3 , can also be written as Al 2 o 3 ·3H 2 O. At a relatively high temperature, boehmite AlO(OH) (also written as Al 2 o 3 ·H 2 O) is an oxide film in the main form. [0003] The thickness of the natural oxide film formed by aluminum alloy in the atmosphere is only 2-30nm. There are two main methods of artificially preparing the oxide film: one is the chemical oxidation method, and the thickness of the oxide film prepared by it is 1-2.5 μm; the other is the anode Oxidation method, the thickness of the oxide film prepared by this method is 2.5-150 μm. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B08B7/00B23K26/0622B23K26/142B23K26/082B23K26/073B23K103/10
CPCB08B7/0042B23K26/0624B23K26/0738B23K26/082B23K26/142B23K2103/10
Inventor 冯杰才赵慧峰吴金鹏
Owner 上海临仕激光科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap