Method for preparing graphene nanoplatelets with pulsed high pressure water jet mill
A graphene micro-sheet, water jet pulverization technology, applied in graphene, chemical instruments and methods, inorganic chemistry and other directions, can solve the problems of large environmental pollution, complex preparation process, high graphene production cost, and achieves easy preparation method, The effect of uniform dispersion of layers and low cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0027] Example 1
[0028] A method for preparing graphene microchips using a pulsed high-pressure water jet pulverizer:
[0029] (1) Heat 90 parts by weight of graphite powder at a heating temperature of 180°C for 20 minutes, and then combine the graphite powder and 0.5 parts by weight of ethanol, 0.4 parts by weight of potassium tripolyphosphate and 500 parts by weight. In the high-speed mixer where water is added, stir at 360 rpm during the adding process for 3 minutes to obtain an aqueous solution of graphite powder;
[0030] (2) The graphite powder aqueous solution obtained in step (1) is sent into a closed reaction kettle, and the graphite powder is pressurized and intercalated to embrittlement for 4 hours at a pressure of 10 MPa to weaken the van der Waals force between graphite powder layers to obtain pretreated graphite powder Aqueous solution
[0031] (3) The pretreated graphite powder aqueous solution obtained in step (2) is sent to the pulse high-pressure water jet pulver...
Example Embodiment
[0032] Example 2
[0033] A method for preparing graphene microchips using a pulsed high-pressure water jet pulverizer:
[0034] (1) Heat 98 parts by weight of graphite powder at a heating temperature of 220°C for 40 minutes, and then combine the graphite powder and 2.0 parts by weight of ethanol, 1.5 parts by weight of potassium tripolyphosphate and 1000 parts by weight. In the high-speed mixer where water is added, stir at 480 rpm during the adding process for 3 minutes to obtain an aqueous solution of graphite powder;
[0035] (2) The graphite powder aqueous solution obtained in step (1) is fed into a closed reaction kettle, and the graphite powder is pressurized and intercalated to embrittlement for 10 hours at a pressure of 25 MPa to weaken the van der Waals force between graphite powder layers to obtain pretreated graphite powder Aqueous solution
[0036] (3) The pretreated graphite powder aqueous solution obtained in step (2) is sent to the pulse high-pressure water jet pulve...
Example Embodiment
[0037] Example 3
[0038] A method for preparing graphene microchips using a pulsed high-pressure water jet pulverizer:
[0039] (1) Heat 93 parts by weight of graphite powder at a heating temperature of 200°C for 30 minutes, and then combine the graphite powder and 1.6 parts by weight of ethanol, 1.1 parts by weight of potassium tripolyphosphate and 8000 parts by weight. In the high-speed mixer where water is added, stir at 400 rpm during the adding process for 3 minutes to obtain an aqueous solution of graphite powder;
[0040] (2) The graphite powder aqueous solution obtained in step (1) is sent into a closed reaction kettle, and the graphite powder is pressurized and intercalated to embrittlement for 6 hours under a pressure of 16 MPa to weaken the van der Waals force between graphite powder layers to obtain pretreated graphite powder Aqueous solution
[0041] (3) The pretreated graphite powder aqueous solution obtained in step (2) is sent to the pulse high-pressure water jet pu...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap