Electronic equipment shell, preparation method for electronic equipment shell coating, and electronic equipment
A technology for electronic equipment and shells, which is applied in the field of preparation of electronic equipment shells and their coatings, and can solve problems such as threats to human health and easy breeding of bacteria
Inactive Publication Date: 2016-07-20
BOE TECH GRP CO LTD +1
View PDF3 Cites 3 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] At present, electronic devices, especially mobile phones, are frequently used in daily life, and the ambient temperature is suitable, so bacteria are easy to breed and threaten human health; at the same time, electronic devices are often used in different environments. Friction occurs with other media, so the shell needs to have high wear resistance; thus, a wear-resistant and antibacterial electronic equipment shell is of great significance to the development and application of the current electronic equipment field
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
preparation example Construction
[0027] The embodiment of the present invention also provides a method for preparing a coating of an electronic device housing, comprising:
[0028] The precursor powder formed by the powder of manganese boronite and the powder of at least one metal is sprayed on the surface of the housing body of the electronic equipment to form the manganese boronite / metal composite coating.
Embodiment approach
[0030] Method 1, spraying the precursor powder formed by manganese boronite powder and aluminum powder onto the surface of the main body of the electronic device housing to form a manganese boronite / aluminum composite coating;
[0031] Method 2, spraying the precursor powder formed by manganese boronite powder and copper powder onto the surface of the main body of the electronic device housing to form a manganese boronite / copper composite coating;
[0032] Method 3: Spray the precursor powder formed by manganese boronite powder and magnesium aluminum alloy powder on the surface of the main body of the electronic equipment housing to form a manganese boronite / magnesium aluminum alloy composite coating.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to the technical field of electronic equipment, and discloses an electronic equipment shell, a preparation method for an electronic equipment shell coating, and the electronic equipment. The electronic equipment shell comprises a shell body, and a chambersite / metal composite coating formed on the surface of the shell body; the chambersite / metal composite coating is formed by spraying precursor powder on the shell body, wherein the precursor powder is formed by chambersite powder and the metal powder; the chambersite is kind of rare mineral and can be compounded with metal to form the chambersite / metal composite coating having high bonding strength; the chambersite has high wear resistance and antibacterial property, high neutron irradiation property, high gamma ray irradiation property and high electromagnetic property, so that the chambersite / metal composite coating is wear resistant and antibacterial; and according to the electronic equipment shell, the chambersite / metal composite coating is formed on the surface of the shell body, so that the electronic equipment shell is wear resistant and antibacterial.
Description
technical field [0001] The invention relates to the technical field of electronic equipment, in particular to a method for preparing an electronic equipment casing and a coating thereof, and an electronic equipment. Background technique [0002] At present, electronic devices, especially mobile phones, are frequently used in daily life, and the ambient temperature is suitable, so bacteria are easy to breed and threaten human health; at the same time, electronic devices are often used in different environments. Friction occurs with other media, so the shell needs to have high wear resistance; thus, a wear-resistant and antibacterial electronic equipment shell is of great significance to the development and application of the current electronic equipment field. Contents of the invention [0003] The invention provides a preparation method for an electronic equipment shell and its coating, and an electronic equipment, wherein the electronic equipment shell is both wear-resist...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): H05K5/02C23C4/12C23C4/10C23C4/06
CPCC23C4/06C23C4/10H05K5/02C23C4/134B02C17/1815
Inventor 梁栋王凯旋李伟袁洪亮马力尤杨武晓娟陈会顺彭晓青毕谣张子敬郑琪
Owner BOE TECH GRP CO LTD