Biodegradable modified lignin particles and production method thereof

A technology of biodegradation and manufacturing method, applied in the field of biodegradable modified lignin particles and their manufacture, can solve the problems of increasing the cost of fully biodegradable materials, low elasticity of fully biodegradable materials, poor mechanical properties and processing stability, and the like, Achieving the effect of avoiding waste of food resources, enriching reserves and improving material carrying capacity

Inactive Publication Date: 2016-08-10
高陈堰
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in China and around the world, common fully biodegradable materials generally use polylactic acid (PLA) as a raw material, which needs to be made from starch raw materials extracted from plant resources (such as corn), and the production process requires consumption A large amount of edible food for human beings not only causes a waste of food resources, but also increases the cost of manufacturin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A biodegradable modified lignin particle, the raw material components used include:

[0033] 45 parts by weight of lignin, 47 parts by weight of polybutylene adipate / terephthalate, 3 parts by weight of stearic acid, 2 parts by weight of polyethylene wax and 0.5 parts by weight of oleic acid amide.

[0034] A method for preparing the biodegradable modified lignin particles, comprising the following steps:

[0035] (1) Take each raw material component according to the above parts by weight and mix them to obtain a mixture. The mixture was heated to 50° C. and stirred at a stirring speed of 300 r / min for 12 minutes, so that the raw material components in the mixture were further uniformly mixed to obtain a coarse material;

[0036] (2) Get the coarse material obtained in the step (1), use a twin-screw extrusion granulator to carry out granulation operation, the screw speed is 150r / min, and the granulation temperature is 120°C, to obtain the obtained granules with a partic...

Embodiment 2

[0038] A biodegradable modified lignin particle, the raw material components used include:

[0039] 38 parts by weight of lignin, 55 parts by weight of polybutylene adipate / terephthalate, 2 parts by weight of stearic acid, 3 parts by weight of polyethylene wax and 0.8 parts by weight of oleic acid amide.

[0040] A method for preparing the biodegradable modified lignin particles, comprising the following steps:

[0041] (1) Take each raw material component according to the above parts by weight and mix them to obtain a mixture. The mixture was heated to 40° C. and stirred at a stirring speed of 500 r / min for 8 minutes, so that the raw material components in the mixture were further uniformly mixed to obtain a coarse material;

[0042] (2) Get the coarse material obtained in the step (1), use a twin-screw extrusion granulator to carry out the granulation operation, the screw speed is 100r / min, and the granulation temperature is 150°C, to obtain the obtained granules with a par...

Embodiment 3

[0044] A biodegradable modified lignin particle, the raw material components used include:

[0045] 38 parts by weight of lignin, 40 parts by weight of polybutylene adipate / terephthalate, 3 parts by weight of stearic acid, 3 parts by weight of polyethylene wax and 1 part by weight of oleic acid amide.

[0046] A method for preparing the biodegradable modified lignin particles, comprising the following steps:

[0047] (1) Take each raw material component according to the above parts by weight and mix them to obtain a mixture. The mixture was heated up to 60° C. and stirred at a stirring speed of 300 r / min and a stirring time of 12 minutes, so that the raw material components in the mixture were further uniformly mixed to obtain a coarse material;

[0048](2) Get the coarse material gained in step (1), use a twin-screw extrusion granulator to carry out the granulation operation, the screw speed is 300r / min, and the granulation temperature is 120°C, to obtain the 1cm particle di...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to biodegradable modified lignin particles. The biodegradable modified lignin particles comprise the following raw components: 35 to 45 weight parts of lignin, 40 to 55 weight parts of poly(butylene adipate/terephthalate), 4 to 6 weight parts of auxiliary agents and 0.5 to 1 weight part of an organic anti-blocking agent; the auxiliary agents comprise stearic acid and polyethylene wax. A production method for the biodegradable modified lignin particles comprises the following steps: mixing the raw components according to the above parts by weight; heating and obtaining a coarse material after the raw components are mixed uniformly; taking the coarse material and granulating the coarse material to obtain the biodegradable modified lignin particles. The biodegradable modified lignin particles can be completely biodegraded after use, have high mechanical and processing performance, and have important significance to protect ecological environment and reduce white pollution. The biodegradable modified lignin particles are simple in production process and low in cost, and are suitable for batch production.

Description

technical field [0001] The invention belongs to the technical field of environmentally friendly degradable materials, and in particular relates to a biodegradable modified lignin particle and a manufacturing method thereof. Background technique [0002] Biodegradable material is a good environment-friendly material, and the popularization and use of this material is of great significance to reduce white pollution and protect the natural environment. At present, in China and around the world, common fully biodegradable materials generally use polylactic acid (PLA) as a raw material, which needs to be made from starch raw materials extracted from plant resources (such as corn), and the production process requires consumption A large amount of edible food for human beings not only causes waste of food resources, but also increases the cost of manufacturing and producing completely biodegradable materials, which is not suitable for promotion on a large scale. At the same time, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08L97/00C08L23/06C08K5/09C08K5/20C08K3/26
CPCC08L67/02C08L2201/06C08L2201/08C08L2205/03C08L97/005C08L23/06C08K5/09C08K5/20C08K2003/265
Inventor 高陈堰
Owner 高陈堰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap