Silicone resin composition for prepregs, carbon fiber prepreg and carbon fiber-silicone resin composite material

A technology of silicone resin composition and carbon fiber prepreg, which is applied in the field of silicone resin composition, can solve the problems of poor high temperature resistance and single function, and achieve the effects of improving mechanical properties, good flexibility and increasing strength

Inactive Publication Date: 2016-08-17
HARBIN INST OF TECH
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims to solve the problems of poor high temperature resistance and single function of existing silicone resin carbon fiber composite materials, and provides silicone resin compositions for prepregs, carbon fiber prepregs and carbon fiber silicone resin composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0020] Specific Embodiment 1: The silicone resin composition for prepreg in this embodiment includes 40-80 parts by weight of silicone resin, 20-60 parts of phenolic resin, 10-25 parts of toughening agent, 10-30 parts of functional filler, 1-5 parts of coupling agent and 0.5-5 parts of catalyst.

specific Embodiment approach 2

[0021] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the silicone resin is one or more of methyl silicone resin, phenyl silicone resin, and methyl phenyl silicone resin combined in any ratio. mixture. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0022] Embodiment 3: This embodiment is different from Embodiment 1 or Embodiment 2 in that: the phenolic resin is boron phenolic resin or molybdenum phenolic resin. Others are the same as in the first or second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Bending strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a silicone resin composition for prepregs, a carbon fiber prepreg and a carbon fiber-silicone resin composite material, relating to a silicone resin composition, a carbon fiber prepreg prepared from the silicone resin composition and a silicone resin composite material. The invention aims to solve the problems of poor high-temperature resistance and single function in the existing silicone resin-carbon fiber composite material. The composition comprises the silicone resin, a phenolic resin, a toughener, a functional filler, a coupling agent and a catalyst. The carbon fiber prepreg comprises a carbon fiber material and the composition for prepregs. The carbon fiber-silicone resin composite material is prepared by curing the carbon fiber prepreg. The curing method comprises winding molding, cast molding or compression molding. The carbon fiber prepreg is cured to obtain the carbon fiber composite material. The carbon fiber composite material has favorable mechanical properties and high-temperature resistance. The silicone resin composition is applicable to the field of silicone resin-carbon fiber composite materials.

Description

technical field [0001] The invention relates to a silicone resin composition, a carbon fiber prepreg and a silicone resin composite material using the silicone resin composition as raw materials. Background technique [0002] Because aerospace works at high altitude and high speed, the external materials of the machine are required to have better high temperature resistance, low temperature resistance, and ozone resistance. The development and needs of the aerospace industry have promoted the development of advanced composite materials, and the development and application of advanced composite materials have promoted the progress of aerospace. With the widespread use of advanced composite materials in the aerospace field, new requirements are put forward for the performance of composite materials. Composite materials are required to have high specific strength, high specific modulus, high temperature resistance, low temperature resistance, and ozone resistance. Aerospace p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/04C08L61/14C08K13/04C08K7/06C08K3/36C08K3/22C08K3/08C08J5/24
CPCC08L83/04C08J5/24C08J2383/04C08J2461/14C08L2205/025C08L2205/03C08L2205/035C08L61/14C08K13/04C08K7/06C08K3/36C08K2003/2227C08K2003/0806
Inventor 刘丽张炫烽钟正祥马震宇温泉徐慧芳黄玉东
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap