Process of high-speed digital printing and interweaving of silks with gold and silver wires

A high-speed digital printing, gold and silver wire technology, applied in the field of textile processing, can solve the problems of metal coating peeling, unclear gold and silver wire, poor gold and silver effect, etc., and achieve the effect of clear printing and obvious gold and silver effect.

Active Publication Date: 2016-08-31
ZHEJIANG QIANJIANG TEXTILE PRINTING & DYING CO LTD
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the chemical properties of gold and silver threads are unstable and cannot be used like ordinary textile fibers
The aluminum film in the gold and silver wire is not resistant to alkali; the silver film is not resistant to acid, and the silver film will turn black when exposed to sulfide, and stretching or heavy friction will cause the metal plating to peel off
[0003] Digital printing after silk and gold and silver threads are interwoven will easily lead to unclear gold and silver threads, and the gold and silver effect will be poor after printing on it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A high-speed digital printing and silk gold and silver thread interweaving process is characterized in that the steps are as follows:

[0021] (1) Fabric open-width refining;

[0022] (2) Sizing: 3% QJ1501, 10% urea, 2% baking soda, 2% seaweed, 2% original starch, 1% anti-swimming, and 80% water.

[0023] (3) Sizing temperature control, the temperature is controlled at 60°C, so that after the silk sizing penetrates into the gold and silver wire sizing at 60°C, the contact surface between the size and the gold and silver wire will produce a peeling effect;

[0024] (4) After inkjet digital printing on the surface of gold and silver threads, control the steaming temperature at 80°C, humidity at 30%, steam pressure at 2kg, and speed at 15 meters per minute, so that the shelling degree of the surface of gold and silver threads will be aggravated by inkjet;

[0025] (5) Add cleaning agent and wash with water at 60°C, dehull the original sizing and steam to accelerate dehull...

Embodiment 2

[0031] A high-speed digital printing and silk gold and silver thread interweaving process is characterized in that the steps are as follows:

[0032] (1) Fabric open-width refining;

[0033] (2) Sizing: 2% QJ1501, 8% urea, 2% baking soda, 1.5% seaweed, 2% original starch, 2% anti-swimming, 77.5-82.5% water.

[0034] (3) Sizing temperature control, the temperature is controlled at 70°C, so that the silk sizing penetrates into the gold and silver wire sizing at 70°C, and the contact surface between the size and the gold and silver wire produces a peeling effect;

[0035] (4) After inkjet digital printing on the surface of gold and silver threads, control the steaming temperature at 80°C, humidity at 30%, steam pressure at 2kg, and speed at 15 meters per minute, so that the shelling degree of the surface of gold and silver threads will be aggravated by inkjet;

[0036] (5) Add cleaning agent and wash with water at 60°C, dehull the original sizing and steam to accelerate dehullin...

Embodiment 3

[0042] A high-speed digital printing and silk gold and silver thread interweaving process is characterized in that the steps are as follows:

[0043] (1) Fabric open-width refining;

[0044] (2) Sizing: QJ1501 1.5%, urea 7%, baking soda 3%, seaweed 2.5%, anti-swimming 1.5%, water 84.5%.

[0045] (3) Sizing temperature control, the temperature is controlled at 65°C, and after the silk sizing penetrates into the gold and silver wire sizing at 70°C, the contact surface between the size and the gold and silver wire will produce a peeling effect;

[0046] (4) After inkjet digital printing on the surface of the gold and silver wire, control the steaming temperature to 80°C, humidity to 30%, steam pressure to 2kg, and speed to 15 meters per minute, and the shelling degree of the surface of the gold and silver wire to be exacerbated by inkjet;

[0047] (5) Add cleaning agent and wash with water at 60°C, dehull the original sizing and steam to accelerate dehulling, completely peel off...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a process of high-speed digital printing and interweaving of silks with gold and silver wires. The process comprises the following steps of: (1) open-width scouring of a fabric; (2) sizing; (3) sizing temperature control, i.e., controlling a temperature within the range of 60-70 DEG C, in which after the temperature is within the range of 60-70 DEG C for sizing of gold and silver wires after thorough penetration of sizing of silks, a shelling effect may be produced on contact surfaces of a sizing agent with the gold and silver wires; (4) after ink-jet digital printing on the surface of the gold and silver wires, controlling an aging temperature to 80 DEG C, a humidity to 30%, a steam pressure to 2 kg and a speed per minute to 15 m / min, resulting in aggravated shelling degree due to ink jet on the surface of the gold and silver wires; (5) adding a detergent and carrying out open-width water washing at 60 DEG C to thoroughly peel a dye jetted on the gold and silver wires that is shelled by previous sizing and further shelled by aging, thus restoring the original effect of the gold and silver wires; (6) finishing and drying; and (7) tentering and softening to obtain the finished product. The process of high-speed digital printing and interweaving of silks with gold and silver wires can be used for solving the problems of unclear gold and silver wires and poor gold and silver effects after printing; the resulting silk-gold-silver wire fabric is clear in printing, lifelike, and very obvious in gold and silver effects.

Description

technical field [0001] The invention belongs to the field of textile processing, and in particular relates to a high-speed digital printing and real silk gold and silver thread interweaving process. Background technique [0002] Gold and silver thread is gold and silver thread + polyester or rayon twisted filaments! Mainly used in computer embroidery and craft accessories! It is widely used in handicrafts, fashion, embroidery, gift packaging and other industries and the processing of knitted wool, yarn, knitted fabric, warp knitted fabric, woven fabric, clothing accessories, decorative cloth, sofa release and other products. It is an ideal lining raw material. It is to use physical methods to cut the colored PET polyester film into extremely thin wires! Gold and silver thread is gold and silver thread + polyester or rayon twisted filaments! Mainly used in computer embroidery and craft accessories! It is widely used in handicrafts, fashion, embroidery, gift packaging and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/432D06M16/00D06M11/76D06M11/56D06P5/30B41M5/00D06B19/00D06M101/10
CPCB41M5/0047D06B19/0029D06M11/56D06M11/76D06M13/432D06M16/003D06M2101/10D06P5/30
Inventor 王树华
Owner ZHEJIANG QIANJIANG TEXTILE PRINTING & DYING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com