Quick dissolving mold core capable of shortening removal time and using method thereof

A mold core and instant melting technology, which is applied in the direction of ion implantation plating, coating, metal material coating process, etc., can solve the possibility of increased corrosion and damage of the uranium layer in the NIF black cavity, high failure rate, aluminum mold core Long removal time and other problems, to achieve the effect of reducing post-processing and fracture protection layer plating process, improving production efficiency, and shortening removal time

Active Publication Date: 2016-09-21
LASER FUSION RES CENT CHINA ACAD OF ENG PHYSICS
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the long removal time of the existing aluminum mold core, which increases the possibility of the uranium layer of the NIF black cavity being corroded and damaged, resulting in a high failure rate due to demoulding during the preparation of the NIF black cavity. An instant mold core that shortens the removal time and its application method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quick dissolving mold core capable of shortening removal time and using method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0011] Specific implementation mode one: combine figure 1 , the present embodiment is an instant mold core that shortens the removal time, and it is composed of a cavity mold core 1 and a support rod 2; the support rod 2 is composed of a rod body 2-1, a reference surface 2-2 and an external thread; the The top of the support rod 2 is processed into an external thread, and the inner cavity of the cavity mold core 1 is processed into an internal thread, so that the cavity mold core 1 and the support rod 2 are screwed together; the rod body 2-1 of the support rod 2 A reference surface 2-2 is processed between the outer thread and the external thread, ensuring that the diameter of the reference surface 2-2 is equal to the outer diameter of the cavity mold core 1.

[0012] The support rod 2 described in this embodiment is cylindrical, and the top end of the support rod 2 has an external thread. Compared with the external thread, it can play a stable clamping role in the preparatio...

specific Embodiment approach 2

[0013] Specific implementation mode two: combination figure 1 The difference between this embodiment and the first embodiment is that a contact gap 3 is provided between the cavity core 1 and the reference surface 2-2, and the width of the contact gap 3 is 50 μm˜100 μm. Others are the same as the first embodiment.

specific Embodiment approach 3

[0014] Specific implementation mode three: combination figure 1 The difference between this embodiment and the specific embodiment 1 or 2 is: there is a gap 4 between the top of the cavity core 1 and the top of the external thread of the support rod, and the width of the gap 4 is 50 μm to 100 μm . Others are the same as those in Embodiment 1 or 2.

[0015] DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 2 and 3 The purpose of setting the contact gap 3 and the gap 4 is to facilitate the removal of the cavity mold core 1 from the support rod 2 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Surface roughnessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a mold core and a using method thereof, in particular to a quick dissolving mold core capable of shortening removal time and a using method thereof. By means of the quick dissolving mold core capable of shortening the removal time and the using method thereof, the problems that the removal time of an existing aluminum mold core is long, consequently, the possibility that a uranium layer of an NIF block cavity is corroded and destroyed is increased, and the failure rate caused by demolding in the preparation process of the NIF block cavity is high are solved. The quick dissolving mold core capable of shortening the removal time is composed of a cavity mold core body and a supporting rod. The supporting rod is composed of a rod body, a reference plane and an outer thread. The using method includes the steps that 1, coating is carried out, so that the cavity mold core body coated with the uranium-containing black cavity coating is obtained; and 2, demolding is carried out, and accordingly the uranium-containing black cavity is obtained. The quick dissolving mold core capable of shortening the removal time and the using method thereof have the advantages that the removal time is greatly shortened, post processing and fracture protection layer plating procedures are omitted, and production efficiency is improved. The quick dissolving mold core is mainly provided and utilized for preparing the uranium-containing black cavity.

Description

technical field [0001] The invention relates to a mold core and a method for using the same. Background technique [0002] The U-containing black cavity has a high energy gain, which can reduce the ignition energy requirement of the driver, increase the ignition energy margin, and reduce the ablation of the optical device. It is selected by the NIF ignition freezing target experiment. However, the chemical properties of U are extremely active, and after oxidation, the ionization heat capacity of the black cavity wall will be increased, resulting in a significant decrease in its conversion efficiency. Traditional aluminum or copper mandrels are no longer suitable. In order to reduce the possibility of oxidation or hydrogen embrittlement of the uranium layer, and reduce the probability of over-corrosion of the black cavity, the American NIF uranium-containing ignition black cavity development process uses an aluminum-copper composite mandrel (that is, the aluminum mold core i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C14/35C23C14/16C23F1/36C23F1/20
CPCC23C14/165C23C14/35C23F1/20C23F1/36
Inventor 邢丕峰赵利平柯博高莎莎杨蒙生李宁郑凤成易泰民李翠