External wall natural stone paint suitable for construction in low-temperature high-humidity environment

A low-temperature, high-humidity, real stone paint technology, applied in the field of exterior wall coatings, can solve the problems of easy whitening and flowering of the paint film, cracking of the paint film, poor water resistance, etc., and achieve water resistance, adhesion, and bond strength. Adhesion Strong, effect of improving stain resistance

Active Publication Date: 2016-10-12
湖南德泰建筑工程有限公司
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problems that the existing real stone paint is prone to cracking of the paint film, poor water resistance, whitening and flowering when it encounters water when it is applied in a low-temperature and high-humidity environment. wall real stone paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • External wall natural stone paint suitable for construction in low-temperature high-humidity environment
  • External wall natural stone paint suitable for construction in low-temperature high-humidity environment
  • External wall natural stone paint suitable for construction in low-temperature high-humidity environment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A real stone paint for exterior walls suitable for construction in low-temperature and high-humidity environments. It mainly consists of 75kg colored sand, 13kg silicon-modified styrene-acrylic emulsion 8666, 0.7kg film-forming aid, 2.5kg silica sol, 0.11kg thickener and 8.69kg Composition of conventional additives (including diluents). Among them, the colored sand is composed of 40kg of 40-80 mesh coarse sand and 35kg of 80-120 mesh fine sand; the particle size of silicon-modified styrene-acrylic emulsion 8666 is 0.1-0.6μm, and the appearance is milky white with a slight blue phase; Membrane aid is compounded by 0.3kg of Texanol ester alcohol, 0.2kg of ethylene glycol monobutyl ether and 0.2kg of benzyl alcohol; thickener is made of 0.05kg of polyurethane thickener and 0.06kg of alkali thickener (such as hydrophobically modified acrylic copolymer, carboxylic acid acrylic copolymer, etc., the same below). During the construction of real stone paint, control the moistur...

Embodiment 2

[0025] A real stone paint for exterior walls suitable for construction in low-temperature and high-humidity environments. It mainly consists of 80kg colored sand, 12kg silicon-modified styrene-acrylic emulsion 8666, 0.6kg film-forming aid, 2kg silica sol, 0.1kg thickener and 5.3kg Common additives (including diluents) composition. Among them, the colored sand is composed of 42.7kg of 40-80 mesh coarse sand and 37.3kg of 80-120 mesh fine sand; the particle size of silicon-modified styrene-acrylic emulsion 8666 is 0.1-0.6μm, and the appearance is milky white with a slight blue phase; The film aid is compounded by 0.257kg of Texanol ester alcohol, 0.1714kg of ethylene glycol monobutyl ether and 0.1714kg of benzyl alcohol; the thickener is compounded by 0.045kg of polyurethane thickener and 0.055kg. During the construction of real stone paint, control the moisture content of the base layer to less than 10%, and the pH value to less than 10, and use the hanging basket spraying meth...

Embodiment 3

[0027] A real stone paint for exterior walls suitable for construction in low-temperature and high-humidity environments. It mainly consists of 70kg colored sand, 15kg silicon-modified styrene-acrylic emulsion 8666, 0.8kg film-forming aids, 3kg silica sol, 0.15kg thickener and 11.05kg Common additives (including diluents) composition. Among them, the colored sand is composed of 37.33kg of 40-80 mesh coarse sand and 32.67kg of 80-120 mesh fine sand; the particle size of silicon-modified styrene-acrylic emulsion 8666 is 0.1-0.6μm, and the appearance is milky white with a slight blue phase; The film aid is compounded by 0.343kg of Texanol ester alcohol, 0.228kg of ethylene glycol monobutyl ether and 0.228kg of benzyl alcohol; the thickener is compounded by 0.0682kg of polyurethane thickener and 0.0818kg. During the construction of real stone paint, control the moisture content of the base layer to less than 10%, and the pH value to less than 10, and use the hanging basket sprayin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to an external wall natural stone paint suitable for construction in a low-temperature high-humidity environment. The invention is characterized in that the paint is mainly composed of the following components in percentage by mass: 70-80% of colored sand, 12-15% of silicon-modified styrene-acrylic emulsion 8666, 0.6-0.8% of film forming aid, 2.0-3.0% of silica sol, 0.1-0.15% of thickener and the balance of conventional aid, totaling 100%. The film forming aid is mainly compounded from Texanol ester alcohol, ethylene glycol monobutyl ether and benzyl alcohol. The thickener is compounded from a polyurethane thickener and an alkali thickener. The natural stone paint can achieve the constructability of the normal temperature environment in the low-temperature high-humidity environment.

Description

technical field [0001] The invention relates to an exterior wall paint, in particular to a real stone paint for an exterior wall, in particular to a real stone paint for an exterior wall suitable for construction in a low-temperature and high-humidity environment. Background technique [0002] The real stone paint for exterior walls is made of natural granite and other natural gravel and powder as main raw materials, synthetic resin emulsion as adhesive, and supplemented by various additives. Real stone paint for exterior walls has the rich texture and three-dimensionality of natural stone, as well as a solemn and harmonious aesthetic feeling; moreover, compared with exterior wall bricks and dry-hanging granite, it is more economical and applicable at lower prices. The decorative effect of real stone paint on the exterior wall is comparable to that of stone, and it is more suitable for shaping various artistic shapes than stone. Its durability and impermeability are longer, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/24
CPCC04B28/24C04B2111/00482C04B2111/27C04B14/06C04B24/40C04B24/02C04B24/023C04B24/282
Inventor 郭双华钟爱民钱琛王前坤
Owner 湖南德泰建筑工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com