Cobwebbing waterborne colorful coating and preparation method thereof

A water-based multi-color paint, filamentary technology, applied in multi-color effect paint, coating and other directions, can solve the problems of consumers' visual fatigue, high cost, abrupt feeling of colorful paint film, etc., and achieves appropriate thixotropy, high flatness, Good water retention effect

Active Publication Date: 2018-04-24
佛山市顺德区巴德富实业有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the market is basically presented in the form of such round particles, which causes visual fatigue for consumers, and generally multi-color paints require a large amount of powder-supported base paint, resulting in high cost; unexpected

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] A preparation method of the water-based multi-color paint of the drawing, specifically comprising the following steps:

[0051] Step 1. Preparation of base paint:

[0052] 1) Inject deionized water into the disperser and heat to 80-90°C;

[0053] 2) Start the disperser, adjust the rotation speed to 400-800r / min, weigh and add polyvinyl alcohol, and disperse evenly. The dispersion time is 10-20 minutes, and the polyvinyl alcohol is completely dissolved;

[0054] 3) Weigh and slowly add kaolin and titanium dioxide in sequence, adjust the speed of the disperser to 1400-1600r / min, and disperse evenly for 15-25 minutes;

[0055] 4) Weigh and slowly add the resin emulsion, and adjust the speed of the disperser to 800-1200r / min, and disperse for 4-6 minutes;

[0056] 5) Weigh and slowly add a protective glue solution with a mass fraction of 9%, and disperse evenly for 10-20 minutes to obtain a white base primer;

[0057]6) Take out the white basic primer, add an appropriate...

Embodiment 1

[0069] A brushed water-based colorful paint, which is prepared by mixing a base paint, a protective glue solution with a mass fraction of 5% and a continuous phase;

[0070] In parts by weight, the base paint includes 35 parts of deionized water, 5 parts of polyvinyl alcohol, 0.5 parts of kaolin, 0.1 part of titanium dioxide, 20 parts of resin emulsion, 25 parts of protective glue solution with a mass fraction of 9%, and color paste 0.5 copies;

[0071] The continuous phase includes 40 parts of resin emulsion, 40 parts of deionized water, 2 parts of film-forming auxiliary agent, 0.1 part of multifunctional auxiliary agent, and 0.5 part of alkali swelling thickener;

[0072] Wherein, the base paint, the protective colloid solution with a mass fraction of 5% and the continuous phase are in a mass ratio of 1:1:1;

[0073] Polyvinyl alcohol is polyvinyl alcohol BP17-92 with a degree of polymerization of 1700 and a degree of alcoholysis of 98% at Sinopec Sichuan Vinylon Plant;

...

Embodiment 2

[0099] A brushed water-based colorful paint, which is prepared by mixing a base paint, a protective glue solution with a mass fraction of 5% and a continuous phase;

[0100] In parts by weight, the base paint includes 40 parts of deionized water, 8 parts of polyvinyl alcohol, 1 part of kaolin, 0.5 parts of titanium dioxide, 25 parts of resin emulsion, 30 parts of protective glue solution with a mass fraction of 9%, and color paste 1 copy;

[0101] The continuous phase includes 50 parts of resin emulsion, 50 parts of deionized water, 3.5 parts of film-forming auxiliary agent, 0.3 part of multifunctional auxiliary agent, and 0.8 part of alkali swelling thickener;

[0102] Wherein, the base paint, the protective colloid solution with a mass fraction of 5% and the continuous phase are in a mass ratio of 2:1:1;

[0103] Polyvinyl alcohol is polyvinyl alcohol BP17-92 with a degree of polymerization of 1700 and a degree of alcoholysis of 98% at Sinopec Sichuan Vinylon Plant;

[010...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses cobwebbing waterborne colorful coating and a preparation method thereof. The cobwebbing waterborne colorful coating is prepared from mixing of base coating, protective colloidal solution with a mass fraction of 5% and a continuous phase. The base coating is prepared from, by weight, 35-50 parts of deionized water, 5-10 parts of polyvinyl alcohol, 0.5-2 parts of kaolin, 0.1-1 part of titanium dioxide, 20-30 parts of resin emulsion, 25-40 parts of protective colloidal solution with the mass fraction of 9% and 0.5-2 parts of color paste. The continuous phase is prepared from, by weight, 40-60 parts of resin emulsion, 40-60 parts of deionized water, 2-5 parts of a coalescing agent, 0.1-0.5 part of functional additives and 0.5-1 part of alkali swelling thickening agent.A mass ratio of the base coating, the protective colloidal solution with the mass fraction of 5% and the continuous phase is (1-2):(1-2):1. The cobwebbing waterborne colorful coating is excellent in performances of thixotropy, thickening, leveling and the like.

Description

technical field [0001] The invention relates to a water-based colorful paint in a drawing shape and a preparation method thereof. Background technique [0002] Multi-color coatings are mainly used in imitation stone coatings, so they are also called liquid stones, also called imitation granite exterior wall coatings. They are composed of incompatible two-phase components, one of which is a continuous phase and the other is a dispersed phase. When painting, luxurious, beautiful and colorful patterns can be obtained by one-time spraying. The particles of conventional colorful paints are mainly round dots, forming the final paint film shape mainly in dots. [0003] At present, the market is basically presented in the form of such round particles, which causes visual fatigue to consumers, and generally multi-color coatings require a large amount of powder-supported base paint, resulting in high cost; Formed a sense of abruptness. [0004] Therefore, in the colorful paint mark...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/00C09D5/29C09D7/43C09D7/61C09D7/65C09D7/63
CPCC08K2003/2241C08L2205/03C09D5/29C09D201/00C08L101/00C08L29/04C08K13/02C08K3/346C08K3/22C08K5/10
Inventor 周永斌周才俊李婷
Owner 佛山市顺德区巴德富实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com