Resin color paste and production process thereof

A resin color paste and production process technology, applied in pigment paste, anti-corrosion coatings, etc., can solve the problems of poor coloring effect of coatings, waste of production raw materials, and decline in product quality, so as to achieve fine product quality, reduce production costs, and improve quality. Effect

Active Publication Date: 2016-10-12
WEIFANG HELI WATER BASED PAINT MAKING CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Resin color paste is one of the raw materials used in the production of paint. The resin color paste used in the production of water-based paint must have good water solubility. Otherwise, the color paste will float in the water after the paint is mixed with water, which will cause the coloring effect of the paint. Very poor; in addition, during the production of resin color paste, it is easy to produce shrinkage cavities, which will lead to a decline in product quality, and will also lead to uneven paint film when the paint is used in the later stage; moreover, the production of resin color paste During the process, heating and heat preservation are required so that the reaction between the various raw materials can proceed normally, but during the heating and heat preservation process, the solvent is easy to volatilize, resulting in waste of production raw materials and environmental pollution, which brings losses and inconvenient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin color paste and production process thereof
  • Resin color paste and production process thereof
  • Resin color paste and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of resin color paste, is made of following raw material:

[0032]

[0033] The production process includes the following steps:

[0034] Step 1: Add the prescribed amount of isooctyl alcohol and propylene glycol methyl ether into the epoxy kettle where the epoxy resin is melted, then add the prescribed amount of CYD epoxy resin, and feed the cooling water into the epoxy kettle and the condenser on the reaction kettle .

[0035] Step 2: Keep warm when the temperature rises to 80°C. After the epoxy resin in the epoxy kettle is completely melted, open the lid of the kettle and observe to confirm that it is completely melted.

[0036] Step 3: put the melted epoxy resin into the reaction kettle, when the temperature of the reaction kettle rises to 80°C, start stirring, add ethylenediamine and diethanolamine, and keep the temperature for 2 hours.

[0037] Step 4: After the heat preservation is completed, add the polyamine resin, raise the temperature to 100°C, and...

Embodiment 2

[0040] A kind of resin color paste, is made of following raw material:

[0041]

[0042] The production process includes the following steps:

[0043] Step 1: Add the prescribed amount of isooctyl alcohol and propylene glycol methyl ether into the epoxy kettle where the epoxy resin is melted, then add the prescribed amount of CYD epoxy resin, and feed the cooling water into the epoxy kettle and the condenser on the reaction kettle .

[0044] Step 2: Keep warm when the temperature rises to 85°C. After the epoxy resin in the epoxy kettle is completely melted, open the lid of the kettle and observe to confirm that it is completely melted.

[0045] Step 3: Put the melted epoxy resin into the reaction kettle, when the temperature of the reaction kettle rises to 85°C, start stirring, add ethylenediamine and diethanolamine, and keep the temperature for 2.5 hours.

[0046] Step 4: After the heat preservation is over, add the polyamine resin, raise the temperature to 102°C, keep t...

Embodiment 3

[0049] A kind of resin color paste, is made of following raw material:

[0050]

[0051]

[0052] The production process includes the following steps:

[0053] Step 1: Add the prescribed amount of isooctyl alcohol and propylene glycol methyl ether into the epoxy kettle where the epoxy resin is melted, then add the prescribed amount of CYD epoxy resin, and feed the cooling water into the epoxy kettle and the condenser on the reaction kettle .

[0054] Step 2: Keep warm when the temperature rises to 82°C. After the epoxy resin in the reactor is completely melted, open the lid of the kettle and observe to confirm that it is completely melted.

[0055]Step 3: Put the melted epoxy resin into the reaction kettle, when the temperature of the reaction kettle rises to 83°C, start stirring, add ethylenediamine and diethanolamine, and keep the temperature for 2.2 hours.

[0056] Step 4: After the heat preservation is over, add the polyamine resin, raise the temperature to 98°C, k...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
boiling pointaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses resin color paste and a production process thereof, and belongs to the technical field of anticorrosive paint. The resin color paste is prepared by performing chemical reaction and mixing on 260 to 330 parts of epoxy resin, 130 to 160 parts of ether alcohol solvents, 60 to 80 parts of isooctanol, 35 to 50 parts of diethanolameineb and 100 to 200 parts of polyamine resin and dispersing the obtained material in 10 to 20 parts of de-ionized water through being metered in parts by weight. The production process comprises epoxy resin melting, raw material addition and heat insulation reaction. In the resin color paste production process, the loss is little; the production cost is reduced; the hole shrinkage resistance effect is good; the product quality is improved; the hydrophilicity is high. Through the production process, the ring opening of epoxy resin is proper; the raw material waste is avoided; meanwhile, the water solubility of the epoxy resin is improved; the hole shrinkage of products is eliminated; the product quality is improved.

Description

technical field [0001] The invention relates to the technical field of anti-corrosion coatings, in particular to a resin color paste and a production process thereof. Background technique [0002] Resin color paste is one of the raw materials used in the production of paint. The resin color paste used in the production of water-based paint must have good water solubility. Otherwise, the color paste will float in the water after the paint is mixed with water, which will cause the coloring effect of the paint. Very poor; in addition, during the production of resin color paste, it is easy to produce shrinkage cavities, which will lead to a decline in product quality, and will also lead to uneven paint film when the paint is used in the later stage; moreover, the production of resin color paste During the process, heating and heat preservation are required so that the reaction between the various raw materials can proceed normally, but during the heating and heat preservation pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D17/00C09D5/08
CPCC09D5/08C09D17/002
Inventor 张希良谢俊
Owner WEIFANG HELI WATER BASED PAINT MAKING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com